Schlagworte
- Plasma polymerization (4)
- Dielectric properties (3)
- Thermal stability (3)
- Graphene oxide (2)
- Lead ions (2)
- Polystyrene (2)
- Surface and bulk characterization (2)
- Surface functionalization (2)
- Thin films (2)
- Acrylic acid (1)
Organisationseinheit der BAM
Decolorization of Acid Orange 142 (AO142) as important water pollutant was observed on the exposure of the dye solutions to an atmospheric non-thermal gas plasma. Aresponse Surface methodology (RSM) combined with a central composite design (CCD) was utilized to optimize the main factors (variables) affecting the degradation efficiency (response) of AO142, such as the applied voltage, the gap distance between the high voltage electrode and the surface of the solution. The regression analysis showed that a first-order polynomial model well fits the experimental data with a coefficient of determination R2=0.96. FT-IR, UV-vis,TOCand GC-MS measurements were used to investigate the decolorization of the dye on exposure to the plasma discharges. A possible Degradation pathway was postulated. Additionally, the conductivity and pH changes during the treatment were also evaluated. The plasma treatment combined with Fe2+ (plasma Fenton reaction) exhibited a higher degradation efficiency, higher energy yield connected with lower energy consumption in comparison to the plasma treatment without Fe2+ addition.
The work explores the synthesis and the properties of a novel composite membrane System based on modified polystyrene (PS) grafted onto a polyvinyl chloride (PVC) membrane.
PVC membranes were prepared by solution-casting followed by exposure to an atmospheric pressure dielectric barrier discharge (DBD) with O2 to obtain an activated Surface for grafting PS to it. Moreover, the thus prepared membranes were chemically modified furthermore by amination with polyethyleneimine or sulfonation with 4 M sulfuric acid.
The membrane surface characteristics such as wettability, structure and morphology were investigated using water contact angle measurements, attenuated total reflection Fourier transform infrared spectroscopy and scanning electron microscopy experiments. The thermogravimetric stability and electrolytic responses of the membranes were studied utilizing TGA, ion exchange capacity (IEC), and solvent uptake. A significant result of plasma and chemical modification was to produce a membrane material with low permeability. Thus, the methanol permeability of the sulfonated membranes measured for 12 h was measured to 2.34$108 cm2 s1 compared to 177.00$108 cm2 s1 of Nafion 117®which is considered as a benchmark. This result indicates that the prepared sulfonated samples are an innovative and effective material for decreasing the methanol crossover in fuel cells to a great extent. This makes the PVC-g-St membranes are promising and attractive as new materials for polyelectrolyte membrane for fuel cells.
The synthesis and optimization of superior and eco-friendly sorbents for Pb(II) pose a great challenge in the field of water treatment. The sorbent was developed by introducing graphene oxide (GO) into the matrix of polyvinyl formaldehyde (PVF) foam. The immobilization of GO in PVF results in significant increase in the maximum adsorption capacity (Qt) of GO powder for Pb(II), from ≈800 to ≈1730 mg g−1 in the case of GO/PVF foam. As compared with GO powder in Pb(II) aqueous solutions, PVF matrix keeps GO sheets stable without any agglomeration. The large surface area of GO sheet allows the abundant oxygenated functional groups on its surface to participate effectively in the Pb(II) adsorption process, leading to the huge increase of the Qt. Adsorption isotherms and kinetic studies indicated that the sorption process of Pb(II) on GO/PVF was done on heterogenous surface by ion-exchange reaction. The GO/PVF foam showed an excellent reusability for more than 10 cycles with almost the same efficiency and without any significant change in its physical properties.
Nowadays, sensors based on polymers/nanostructured metal oxide composites have been investigated exten-sively because of their sensitivity to NO2 gas at ambient temperature. In this work, nanocomposite membranes of xanthan gum (XG) with different contents of MnO2 nanoparticles were prepared as a potential NO2 gas sensor operating at room temperature by a simple one-step oxidation-reduction reaction. The structural, morphological, thermal, and electrical properties of the composite membrane were investigated. The FT-IR results confirm the successful preparation of MnO2 through the oxidation of XG by KMnO4 and reveal further the structural changes of the XG/MnO2 nanocomposite upon its exposure to NO2 gas. The capping of the synthesized MnO2 nano-particles by XG, the surface composition of the XG/MnO2 nanocomposite membranes, and the effect of NO2 gas on the surface composition was investigated using the XPS technique. The DC conductivity and dielectric loss of nanocomposites were higher than for neat XG. The conductivities of the nanocomposites XG/MO-4, XG/MO-4/ low NO2, and XG/MO-4/high NO2 composites are half, one, and three orders of magnitude higher than that for pure XG revealing a transition from insulating to conductive properties. The results demonstrated that XG/MnO2 nanocomposite membranes are promising for potential applications in NO2 gas sensing.
Thin poly(acrylic acid) PAA films were deposited by pulsed plasma polymerization on different organic and inorganic substrates. The structureproperty relationships of the deposited acrylic acid polymers were studied in dependence on the monomer pressure by various techniques and probes. The surface and bulk properties of the plasma deposited films were investigated by X-ray photoelectron spectroscopy, attenuated total reflection infrared, and broad band dielectric spectroscopy. The experimental infrared frequencies of PAA films are compared with those predicted from quantum mechanical calculation. The concentration of the COOH groups in the film (stored in ambient air) decreased by about 15 % compared to the as-prepared sample. The plasma deposited PAA probably form a highly branched product. However, the dielectric measurements show that in addition to the hydrogen bonds, self condensation process was able to hinder the localized fluctuation as well. These processes lead to form a cross-linked network polymer film. Nevertheless, a low energy is sufficient to break these processes during heating at atmospheric pressure. Therefore, homogenized samples with free branches (functional group) were obtained after a first heating with structures close to conventional polymerized acrylic acid. Thus, a thermally stable product was obtained.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition and their structures were studied in dependence on the duty cycle (DC) for a fixed composition of 1:1. As a result, low values of DC doses preserve the structure of monomers in the plasma deposited polymers while high DC leads to a higher degree of fragmentation and a loss in regular structure. Regarding plasma copolymerisation as a feasible method to finish surfaces with a definite number of functional groups it is necessary to characterize both, the chemical nature and the physical properties of the deposited layer. Therefore, a combination of different methods was employed for the characterization of thin plasma copolymer films (FTIR, dielectric spectroscopy, differential scanning calorimetry, X-ray photoelectron spectroscopy (XPS)). Special attention was paid on the unambiguous identification of COOH groups at the surface after derivatization with trifluoroethanol by XPS and in the volume by FTIR. The glass transition temperature of the copolymer system is lower than that for the both plasma deposited homopolymers and increases with the DC in difference to plasma deposited poly(acrylic acid). The dielectric measurements showed that the plasma deposited films were not thermally stable and underwent an undesired post-plasma chemical reaction. The results obtained by dielectric spectroscopy are discussed in detail in comparison with the data from FTIR and XPS measurements.
Degradation behavior of thin polystyrene films on exposure to Ar plasma and its emitted radiation
(2013)
Spin-coated films of amorphous polystyrene (PS) were exposed to argon plasma for a few seconds to several minutes. The PS film was either in direct contact with the plasma or was shielded from the direct plasma contact by filters with different cutoff wavelengths in the vacuum UV region or by a Faraday cage (FC) made from metal mesh to prevent the impinging of charged species. Only energy-rich neutrals and plasma radiation may be operative in presence of the FC. lithium fluoride (LiF) filter protects the sample from direct contact with the plasma. Wavelengths of plasma radiation shorter than c. 105 nm (≈ 11.8 eV) were cut off. Glass filters made of fused SiO2 have a cutoff at λ ≈175?nm completely the vacuum UV radiation of plasma (ca. 175 nm ≈ 7.0 eV). These energies are sufficient to produce C–C, C–H bond scissions in case of direct Ar plasma exposure and Ar plasma exposure with use of the LiF filter. Only quartz glass shielding did not produce significant effects on the polymer surface in comparison to the reference PS, either in surface energy or O/C ratio or in IR spectra. Oxygen plasma has worked most aggressive and had etched the PS film, thus establishing a steady state between introduction of new oxygen functionalities and polymer etching. Ar plasma exposure produces also oxidation and etching of the polymer films as the oxygen plasma. Using of a FC during Ar plasma exposure or the LiF filter a slightly weaker oxidation was observed.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.