Creep behavior of a γ΄-strengthened Co-base alloy with zero γ/γ΄-lattice misfit at 800 °C, 196 MPa
(2017)
Deformation and structural behavior of an experimental γ΄-strengthened Co-base alloy during creep at 800 °C and 196 MPa have been investigated. The characteristic features of this alloy are zero γ/γ΄-lattice misfit and a fine γ/γ΄-microstructure. In the initial condition, the γ΄-precipitates in this alloy are small (size of about 100 nm), have polyhedral morphology, and are separated by the very narrow c-channels (width of about 10 nm). The tests performed up to about 1% creep strain (about 500 h creep time) gave creep curves with a slow constant strain rate and without an apparent transient creep, typical for superalloys with nonzero misfit. In this initial stage of creep, entering of the narrow γ-channels by dislocations is blocked by a strong Orowan force. The micromechanism of creep was identified as an octahedral glide of h011i superdislocations simultaneously in two phases, γ and γ΄. The γ/γ΄-microstructure with zero misfit shows no rafting but rapidly coarsens isotropically. It is concluded that zero misfit is beneficial at the initial stages of the creep but is unfavourable for longterm creep because of the continuous microstructural coarsening.
Data about the creep of metals and their alloys at temperatures close to the melting point are very limited. The reason is that most engineering alloys are used at temperatures below 0.6-0.8 of their melting point, so, investigation of creep at higher temperatures has usually no practical relevance. For some special applications however it is important, in our case hot isostatic pressing (HIP) of single-crystal turbine blades cast from nickel-base superalloys. In order to remove porosity the blades are HIPed at temperatures above GammaP-solvus where superalloy has no strengthening GammaP-phase and therefore is very soft. E.g., the company Howmet Castings hips the superalloy CMSX-4 at 1288°C, which corresponds to a homologous temperature of about 0.97=1561 K/1612 K (solidus temperature). Knowledge about the creep of CMSX-4 at this temperature and understanding of the creep mechanisms are necessary to model the kinetics of pore closure during HIP.
CMSX-4 single-crystals of [001] orientation and few single-crystals of different orientations, [011], [123] and [111], were tested under creep conditions at 1288°C in the stress range between 4 and 16 MPa. At this temperature which is above the GammaP-solvus (for CMSX-4 1280°C) the superalloy has single phase structure representing the Gamma-solid solution of nickel strengthened by solute atoms. On creep curves of CMSX-4 single-crystals of different orientations measured at 1288°C/10 MPa it is seen that despite such a high homological temperature, 0.97, CMSX-4 shows very high anisotropy of creep rate. The average creep rate of [001] single-crystal in the range 0-30% strain is about 11.5 time faster than that for [111], a ratio, which is even higher than at the practically relevant temperatures 750-1100°, see e.g.. Approximation the strain rate – stress dependence by the Norton power law gave a stress exponent n of about 6 which is an indication of dislocation creep. The specimen shape after testing, analysis of traces of plastic deformation by electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) investigations indicate on dislocation slip on the octahedral system <011>{11-1}.This result however does not support the current doctrine that at high temperatures creep of metals and alloys are climb controlled. It is concluded from the obtained results that even at such a high homologous temperature, 0.97, dislocation movement by slip is more preferable than by climb if only relatively week obstacles are present like solute atoms and low angle boundaries (LABs).
It is remarkable that under used testing conditions the necking and recrystallization behavior of differently oriented single-crystals is very different. E.g., the [001] single-crystal showed very large local strain during necking, Phi=99.8%, and no recrystallization (see Fig. 3a), while the [111] single-crystal small necking, Phi=62%, accompanied by recrystallization. Such a specific deformation and recrystallization has to be undestood.
The obtained creep data of CMSX-4 was introduced in a finite element model in order to simulate pore closure during commercial HIP at a temperature of 1288°C.