Electron microscopy investigation of the structure of a compact extruded from nanopowder of nickel
(2007)
Moiré fringes for misfit measurements at incoherent y/y'-interfaces of nickel-base superalloys
(1998)
A diffusion couple between directionally solidified nickel and the single crystal Ni-base superalloy CMSX-10 was produced by hot pressing in vacuum. The diffusion couples were heat treated at temperatures between 1050 and 1250 °C. The exposed samples were characterized by SEM/EBSD/EPMA. The interdiffusion results in dissolution of the c¢-Ni3 Al in the superalloy and in growth of nickel grains towards CMSX-10. Rapid diffusion of aluminum from the superalloy into pure nickel leads to a significant formation of pores in the superalloy. The interdiffusion processes were modelled using the finite-element simulation software DICTRA with the databases TCNi5 and MobNi2, tailored specially for Ni-base superalloys. The effect of alloying elements on the interdiffusion profiles is discussed in terms of alloy thermodynamics. The calculated element concentration profiles are in good agreement with the EPMA measurements.
The interdiffusion modeling correctly predicts the shapes of the concentration profiles, e.g. kinks on the Al and Ti profiles in the vicinity of the original interface in the joint. The calculation predicts with reasonable accuracy the extent and the location of the Kirkendall porosity.
Data about the creep of metals and their alloys at temperatures close to the melting point are very limited. The reason is that most engineering alloys are used at temperatures below 0.6-0.8 of their melting point, so, investigation of creep at higher temperatures has usually no practical relevance. For some special applications however it is important, in our case hot isostatic pressing (HIP) of single-crystal turbine blades cast from nickel-base superalloys. In order to remove porosity the blades are HIPed at temperatures above GammaP-solvus where superalloy has no strengthening GammaP-phase and therefore is very soft. E.g., the company Howmet Castings hips the superalloy CMSX-4 at 1288°C, which corresponds to a homologous temperature of about 0.97=1561 K/1612 K (solidus temperature). Knowledge about the creep of CMSX-4 at this temperature and understanding of the creep mechanisms are necessary to model the kinetics of pore closure during HIP.
CMSX-4 single-crystals of [001] orientation and few single-crystals of different orientations, [011], [123] and [111], were tested under creep conditions at 1288°C in the stress range between 4 and 16 MPa. At this temperature which is above the GammaP-solvus (for CMSX-4 1280°C) the superalloy has single phase structure representing the Gamma-solid solution of nickel strengthened by solute atoms. On creep curves of CMSX-4 single-crystals of different orientations measured at 1288°C/10 MPa it is seen that despite such a high homological temperature, 0.97, CMSX-4 shows very high anisotropy of creep rate. The average creep rate of [001] single-crystal in the range 0-30% strain is about 11.5 time faster than that for [111], a ratio, which is even higher than at the practically relevant temperatures 750-1100°, see e.g.. Approximation the strain rate – stress dependence by the Norton power law gave a stress exponent n of about 6 which is an indication of dislocation creep. The specimen shape after testing, analysis of traces of plastic deformation by electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) investigations indicate on dislocation slip on the octahedral system <011>{11-1}.This result however does not support the current doctrine that at high temperatures creep of metals and alloys are climb controlled. It is concluded from the obtained results that even at such a high homologous temperature, 0.97, dislocation movement by slip is more preferable than by climb if only relatively week obstacles are present like solute atoms and low angle boundaries (LABs).
It is remarkable that under used testing conditions the necking and recrystallization behavior of differently oriented single-crystals is very different. E.g., the [001] single-crystal showed very large local strain during necking, Phi=99.8%, and no recrystallization (see Fig. 3a), while the [111] single-crystal small necking, Phi=62%, accompanied by recrystallization. Such a specific deformation and recrystallization has to be undestood.
The obtained creep data of CMSX-4 was introduced in a finite element model in order to simulate pore closure during commercial HIP at a temperature of 1288°C.
An improved diffusion model is proposed for pore annihilation during HIP of single-crystal nickel-base superalloys. The model assumes the pore dissolution by emission of vacancies and their sink to the low angle boundaries. Calculation, considering distribution of the pore sizes, predicts the kinetics of pore annihilation similar to the experimental one.
The shape of X-ray reflections from the cuboidal γ/γ'-microstructure was investigated. The measurements were performed on the 4th generation single-crystal nickel-base superalloy TMS138. It is shown that reflections from non-cubic crystallographic planes split not only in d-scale due to the different spacing of the γ- and γ'-lattices but also in the pole figure due to the tilting of γ-lattice planes. This tilting results from the elastic distortion of the γ-lattice caused by the γ/γ'-misfit. The results obtained are discussed under the methodical aspect of misfit measurement.
Kirkendall porosity that forms during interdiffusion in a diffusion couple of nickel-base superalloy CMSX-10 with pure nickel is investigated. The diffusion experiments are conducted at a temperature of 1250 °C, where the strengthening ƴ'-phase ist partially dissolved. The porosity is studied by X-ray sub-μ tomography with a spatial resolution of about 0.35³ μm³ at the European Synchrotron Radiation Facility (ESRF) in Grenoble, France. It is found that depending on the distance from the interface the Kirkendall pores take different shapes: octahedral, rounded pyramidal, drop shaped, dendritic, pear shaped, and joint shapes. Such a variety of pore morphologies indicates a complex multistage process of porosity nucleation and growth under vacancy supersaturation of different degrees. The experimental findings are interpreted on the basis of the results of diffusion modeling. It is shown that the kinetics of porosity growth is essentially influenced by the dissolution of the ƴ'-phase.
Initially, as-cast and homogenized single crystals of nickel-base superalloy CMSX-4 are subjected to hot isostatic pressing at 1288 °C. Two series of experiments are conducted: under the same pressure of 103 MPa but with different durations, between 0.5 and 6 h, and under different pressures, between 15 and 150 MPa, but for the same time of 0.5 h. The porosity annihilation is investigated metallographically and by high-resolution synchrotron X-ray tomography. The obtained experimental results are compared with the predictions of the vacancy model proposed recently in the group. Herein, the model is further refined by coupling with X-ray tomography. The model describes the evolution of the pore arrays enclosed in the 3D synchrotron tomograms during hot isostatic pressing and properly predicts the time and stress dependences of the pore annihilation kinetics. The validated model and the obtained experimental results are used for selecting the optimal technological parameters such as applied pressure and processing time
Interdiffusion in the Face-Centered Cubic Phase of the Co-Al-W-Ta System Between 1090 and 1240 °C
(2018)
Interdiffusion of Al, W, Ta and Co in a Co-base alloy at temperatures between 1090 and 1240 °C has been investigated. The interdiffusion coefficients were found to be close to those reported for these elements in Ni-base alloys. Combining the diffusion simulation software DICTRA with the Ni-base diffusion databases TCNi5 and MobNi3, the interdiffusion profiles of Co, Al W, and Ta were modeled for Co9Al8W2Ta/Co diffusion couples annealed at different temperatures and for different times. The results show that interdiffusion in the Co-Al-W-Ta alloys can be modeled reasonably well using the available commercial databases for thermodynamics and kinetics of Ni-base systems.