A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistances can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented.
In the presentation different zinc coatings are presented and investigated. Their naturally formed protective layers are electrochemically characterized and corrosion relevant values are determined by using a gel pad based on polysaccharide. The corrosion relevant values allow the differentiation of various zinc coating systems and can describe the current protective effect provided by the coating. It is shown that gel-type electrolytes influence protective layers and coatings considerably less than corresponding bulk electrolytes. From the results it is evident that gel-type electrolytes represent a viable and promising field in corrosion research.
Surface treatments usually are used to modify the appearance and properties of stainless steel surfaces. Simultaneously, the corrosion resistance of the stainless steel surface being related intrinsically to the spontaneous formation of a passive layer also will be affected. In this respect, the influence of different surface treatments on the corrosion resistance of Type 304 (UNS S30400) stainless steel to pitting corrosion has been evaluated by means of potentiostatic electrochemical noise measurements and surface characterization. Typical industrial treatments including mechanical grinding, glass blasting, and pickling were taken into account. Additionally, special consideration was put on the effect of aging conditions of the passive layer after surface treatments, in particular on the relative humidity. Benefits and limitations of the different applied surface treatments concerning protectiveness of the stainless steel surface were determined and discussed.