Porous Si3N4/SiC ceramics were rapidly prepared with Y2O3 as sintering additive and ZrO2 as nitrided catalyst, using Si and SiC as starting powders. Porous Si3N4/SiC ceramics with 5 wt% ZrO2 addition showed a complete nitridation and good mechanical properties (with a high porosity of 34.96%, flexural strength of 150±4.2 MPa, linear shrinkage of 0.02%). It was revealed that the reciprocal formation of ZrO2 and ZrN effectively enhanced nitridation by inhibiting the melting of silicon in micro-regions.
Porous Si3N4/SiC ceramics were prepared with Si and SiC as raw materials, Y2O3 as sintering additive and ZrO2 as nitrided catalyst through a rapid nitration process. The nitriding rate as a function of temperature and duration was investigated. The porous Si3N4/SiC ceramics with 8 wt% monoclinic ZrO2 addition that was nitrided at 1400 °C for 2 h exhibited the highest nitridation degree of 95%. The experimental results also demonstrated that the reciprocal formation of ZrO2 and ZrN can effectively enhance the level of nitridation by suppressing the melting of silicon in micro-regions. The effects of nitriding time on the mechanical properties of the specimens with ZrO2 as a catalyst was also studied. After nitrided at 1400 °C for various durations from 2 to 8 h, the porous Si3N4/SiC ceramics with the properties of a porosity over 39.8%, a flexural strength over 88.9 MPa and a linear shrinkage lower than 0.6% were achieved. The systematic investigation reveals the catalytic mechanism of ZrO2 in the synthesis of Si3N4/SiC ceramics.