The direct ink writing of an ink composed of a preceramic polymer and fillers was used to produce hardystonite (Ca2Zn-Si2O7) bioceramic scaffolds. Suitable formulations were developed for the extrusion of fine filaments (350 µm diameter) through a nozzle. The preceramic polymer was employed with the double purpose of contributing to the rheology of the ink by increasing its viscosity and of forming the hardystonite phase upon heat treatment by reacting with the fillers. A control of the rheology is essential when spanning features have to be produced, and therefore the main rheological characteristics of the inks were measured (flow curves, dynamic oscillation tests, viscosity recovery tests) and compared to models reported in the literature. Highly porous scaffolds (up to 80% total porosity) were produced and heat treated in air or in nitrogen atmosphere. The influence of the heat-treatment atmosphere on the morphology, crystalline phase assemblage, and compressive strength of the scaffolds was investigated.
In this work, we demonstrated that the hardystonite (Ca2ZnSi2O7) bioceramics can be produced withhigh phase purity, starting from different preceramic polymers and suitable fillers (precursors for CaOand ZnO) after heating at 1200◦C in air. Open-celled hardystonite foams were easily prepared from a filler-containing silicone resin using hydrazine as foaming agent. The fabrication of cellular structures using a preceramic polymer and fillers was possible because the polymeric melt allowed for the entrapment of the gases generated by the decomposition of hydrazine, and the simultaneous cross-linking of the preceramic polymer enabled the retention of the foam structure. Samples with a well-developed hierarchical porous structure, with an open porosity ranging from ∼65 to ∼81 vol% and an average cell window size ranging from 150 to 500 µm were produced. The hardystonite components possessed a compressive strength ranging from ∼1.4 to ∼2.1 MPa.