The coherent superposition of two anti-phased thermal wave fields creates a zone of destructive interference which is extremely sensitive to the presence of defects without any reference measurements.
Combining a high power laser with a spatial light modulator allows modulating phase and amplitude of an illuminated surface that induces spatially and temporally controlled thermal wave fields. The position and depth of defects are reconstructed from analysis of the Amplitude and Phase of the resulting photothermal signal. The proposed concept is experimentally validated and supported by numerical modeling.
The detection and characterization of surface cracks in steel specimens prior to damage is a technologically and economically highly significant task and is of utmost importance when it comes to safety-relevant structures. In steel production where steel billets at high temperatures have to be inspected while moving a number of well-established NDT methods cannot be applied. Laser thermography however is a promising candidate to serve as a fast, non-contact and remote tool in this case. We present a study that shows that the crack detection capabilities of laser thermography can be extended also to specimens at high temperature. A combination of inductive and laser heating allows to systematically study the contrast formation as well as the optimization of the important measurement parameters. The experiments are accompanied by FEM simulations that provide a better insight of the physical correlations and support the experimental developments. The aim of these studies is to develop a system with high inspection speed and detection performance to be in-line operated under the hostile environment of steel production lines.
The method described here allows to determine the size of the thermal contact between two metal sheets joined by spot welding. This size is a measure for the size of the weld nugget, i.e. the zone melted during the welding process, and thus the quality of the welded joint. The method applies active thermography in transmission or reflection setup. Especially the reflection setup offers an attractive possibility for non-destructive testing when components can be accessed from one side only. The spot weld region is optically heated by laser or flash light radiation. The weld nugget provides the mechanical joint, but also constitutes a thermal bridge between the two welded sheets. The latter will be exploited in this method. The better thermal contact at the weld Nugget contrasts with the surrounding material, where the heat transfer between the two sheets is comparatively low. A major advantage of the described method is the applicability on sheets without any surface treatment. This is achieved by a proper normalization of the data, allowing for a correction of the varying surface emissivity.