Retraction of "Effect of Ca2+ doping on the upconversion luminescence properties of NaYF4:Yb3+/Tm3+ nanoparticles and study of its temperature measurement performance" by Mingzhou Meng et al., CrystEngComm, 2022, 24, 4887–4898, https://doi.org/10.1039/D2CE00562J.
The Royal Society of Chemistry, with the agreement of the authors, hereby wholly retracts this CrystEngComm article due to concerns with the reliability of the data.
A solvothermal method was used to prepare a series of Yb3+/Tm3+/Ca2+ co-doped NaYF4 nanoparticles with different Ca2+ contents. Strong upconversion blue fluorescence could be observed under 980 nm laser excitation of the samples. The effect of different Ca2+ contents on the luminescence intensity was investigated, and it was found that the UV-vis upconversion luminescence increased and then decreased with an increasing Ca2+ concentration during the increase of the Ca2+ content from 0 mol% to 25 mol%, reaching the strongest fluorescence at 15 mol%, which was up to about 28 times stronger than that without Ca2+ doping. Furthermore, the mechanism was investigated, and it was found that the doping of Ca2+ disrupted the symmetry of the crystal field, resulting in a significant enhancement of the overall fluorescence. Applied to fluorescence intensity ratio thermometry, the absolute and relative sensitivities are as high as 0.0418 K−1 and 2.31% K−1, respectively, with a minimum temperature resolution of 0.0129 K.
A series of NaYF4:Yb3+/Tm3+@NaYF4:Yb3+/Er3+ nanoparticles doped with Tm3+ and Er3+ were successfully prepared by the solvothermal method. Under 980 nm laser excitation, intense upconversion emission peaks of Tm3+ and Er3+ were observed for all samples. By doping Tm3+ and Er3+ with core–shell partitioning, not only a significant increase in fluorescence intensity could be achieved, but also simultaneous temperature measurements on multiple thermocouple energy levels could be realised. In addition, the temperature sensing performance of different thermocouple energy levels was also investigated, and it was found that the 3 F3 → 3 H6 and 1 G4 → 3 F4 thermocouple energy level pairs of Tm3+ were the best, with maximum absolute sensitivity and maximum relative sensitivity of up to 0.0250 K−1 and 2.155% K−1 respectively, higher than the sensitivity of other thermocouple energy levels. It has a temperature resolution of less than 0.0139 K, which is lower than that of most materials available today. By using this material as a probe to build a fiber optic temperature sensor platform, it was found to have reliable temperature measurement performance.
Phosphoric acid as the electrolyte in high-temperature polymer electrolyte membrane fuel cell plays an essential role in ist performance and lifetime. Maldistribution of phosphoric acid in the catalyst layer (CL) may result in performance degradation. In the present study, pore-scale simulations were carried out to investigate phosphoric acid’s multiphase flow in a cathode CL. A reconstructed CL model was built using focused ion beam-SEM images, where distributions of pore, carbon support, binder, and catalyst particles can be identified. The multi-relaxation time lattice Boltzmann method was employed to simulate phosphoric Acid invading and leaching from the membrane into the CL during the membrane electrode assembly fabrication process. The predicted redistribution of phosphoric acid indicates that phosphoric acid of low viscosity or low wettability is prone to leaching into the CL.
The effective transport properties and the active electrochemical active surface area (ECSA) were computed using a pore-scale model. They were subsequently used in a macroscopic model to evaluate the cell performance. A parametric study shows that cell performance first increases with increasing phosphoric acid content due to the increase of ECSA. However, further increasing phosphoric acid content results in performance degradation due to mass transfer limitation caused by acid flooding.
In this study, the optimized fabrication and evolution of the microstructure and magnetic Transition behavior of the melt-extraction LaFe11.2Si1.8 microwires have been studied. After the optimization of extraction technique (heating power 22 KW, feeding rate 30-50 mm/s, rotation velocity 1700 r/min), the content of La Fe,Si)13 phase in the as-extracted microwires was 54 wt% due to the high solidification velocity, which was increased to 85 wt% via annealing at 1373 K for 20 min. The amount of La(Fe,Si)13 phase was increased and the composition of La(Fe,Si)13 phase became more homogenized through peritectic reaction and short-distance diffusion in the microwires during annealing process. The coexistence of the nanocrystalline and amorphous structures contributed to the broad magnetic Transition temperature range of the as-extracted and annealed microwires. The annealed microwires exhibited a second-order magnetic transformation behavior and showed a maximum magnetic entropy Change jDSMjmax of 6.2 J/kgK and working temperature interval of 36.0 K under a magnetic field of 20 kOe.
Light-induced NO release based on exogenous NO donors has attracted substantial attention in clinical applications; the induction light source usually converts near-infrared light to blue or ultraviolet light.
However, the low efficiency of near-infrared light-assisted chemical light energy conversion remains a challenge, especially for NaYF4:Yb3+/Tm3+ photoconverting near-infrared light to ultraviolet (UV) and blue light. In this paper, a luminescence-enhanced strategy is reported by doping Ca2+ into NaYF4:Yb3+/Tm3+ and coating it with NaGdF4 through a two-step solvothermal method. Then, UCNPs modified with methyl-b-cyclodextrin (M-b-CD) are loaded on a ruthenium nitrosyl complex [(3)Ru(NO)(Cl)] as nitric oxide release-molecules (NORMs). X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDS) data demonstrated that Ca2+ was successfully doped into NaYF4:Yb3+/Tm3+ nanoparticles as the core, and a pure hexagonal phase, NaYF4, was obtained from the doping of Ca2+. TEM revealed that the crystallinity was significantly improved after Ca2+ doping, and the core–shell structure was successfully synthesized, with NaGdF4 directionally grown on the NaYF4:Ca/Yb/Tm core. Fluorescence tests showed that, especially in the ultraviolet and blue light excitation wavelength regions, the UC emission intensity of the Ca-doped NaYF4:Yb3+/Tm3+@NaGdF4 core–shell UCNPs increased by 302.95 times vs. NaYF4:Yb3+/Tm3+ UCNPs. Finally, the release of NO was tested by the Griess method. Under 980 nm irradiation, the cell viability distinctly decreased with increasing UCNPs@M-b-CD-NORMs concentration. This study Shows that NORM release of NO is triggered by enhanced up-converted UV and blue light, which can be used for the development of UV photo-sensitive drugs.
NaYF4 as the core and NaGdF4 as the outer layer were used to obtain
NaYF4:Yb3+/Tm3+@NaYF4:Ce3+/Eu3+ nanoparticles. Physical and morphological investigations indicated that the obtained nanoparticles were prepared in a hexagonal shape, with the NaGdF4 shell layer uniformly encapsulated on the NaYF4 core.
Strong Tm3+ upconversion emission peaks were observed for a 980-nm-laser-excited sample, while strong Eu3+ downconversion emission peaks were observed for a 254-nm-laser-excited sample. By zonal doping of Tm3+ and Eu3+, their fluorescence intensity can be significantly increased; more importantly, simultaneous temperature measurements with dual-mode upconversion/downconversion can be achieved. The temperature measurement properties of the dual mode were also investigated, and it was discovered that the upconversion 3F3 → 3H6 and 1G4 → 3F4 thermocouple energy levels gave the best temperature measurements with maximum absolute and relative sensitivities of 0.0877 K−1 and 1.95% K−1, respectively, which are better than the current temperature measurement sensitivities of most rare-earth-based materials. This material was prepared as fiber-optic temperature-sensing probes to detect the temperature in the environment in real time and was found to perform excellently for temperature measurement.