Practical methods for the safety assessment of postulated crack-like material defects of cubic containers made of ductile cast iron are presented. A formula for the stress intensity factor of a crack in a fillet with a radius from 20 to 200 mm under static load conditions is given. From that, an assessment diagram is derived for the critical depth of a crack in a fillet. The formula may be used to estimate the stress intensity factor of a dynamically loaded crack for special cases. As an application the results of the estimation procedure are compared with the results of a dynamic finite element calculation.
BAM is the responsible authority in Germany for the assessment of the mechanical and thermal design safety of packages for the transport of radioactive materials. The assessment has to cover the proof of brittle fracture safety for package components made of potentially brittle materials. This paper gives a survey of the regulatory and technical requirements for such an assessment according to BAM's new 'Guidelines for the application of ductile cast iron for transport and storage casks for radioactive materials'. Based on these guidelines, higher stresses than before will be permissible, but it is necessary to put more effort into the safety assessment procedure. The fundamentals of such a proof using the methods of fracture mechanics are presented. The recommended procedure takes into account the guidelines of the IAEA's advisory material which are based on the prevention of crack initiation. Examples of BAM's research and safety assessment practices are given. Recommendations for further developments towards package designs with higher acceptable stress levels will conclude the paper.
Within the last years BAM has carried out numerous drop tests with prototype casks made of ductile cast iron onto targets according to the requirements for final disposal of non-heat generating waste in the German KONRAD repository. The results have shown that the target specifications in the acceptance criteria have to be defined more accurately to get reproducible test results with high precision. Hence, a suitable test stand foundation was developed with much effort. The integrity of the upper concrete layer of this target must be preserved during a test.
Recently the geometrical properties of a tested cubic cast iron container led to a concentration of the impact forces beneath the container walls. The target was damaged strongly with the consequence of inadmissible reduction of cask stresses. For that reason the target construction was modified. However, the basic design was not changed. A prefabricated concrete slab was still joined by a mortar layer to the IAEA target of the BAM drop test facility. In the course of the optimization of the test stand foundation the concrete slab dimensions and the reinforcement were enlarged. During the drop test repetition the target kept intact. Additionally, the mechanical behavior of the cast iron container and the target was analyzed by finite element calculations.
This improved target construction is suggested as a reference target for drop tests with casks whose mass and base area are covered by the container types VI or VII respectively according to the KONRAD repository acceptance criteria.
The measurements during the drop tests with cast iron casks have provided the strains on the cask surface at selected positions. This allows the verification of finite element simulations of drop tests which show the stress distribution also inside the component. In September 2008 a drop test was carried out with a cylindrical cast iron cask containing an artificial material defect which was designed under consideration of critical stress states in the cask body. This drop test could demonstrate the safety against failure by fracture of a cask made of a special cast iron with reduced fracture toughness.