In drop test scenarios related to assessing and licensing the storage procedure of spent fuel and high active waste, the casks under examination are generally not equipped with impact limiters. Hence, the extent of mechanical stresses in case of an assumed handling accident is largely affected by the ground properties of the reception hall floor in the specific storage facility.
Unlike conventional brittle foundation materials, damping concrete performs quite well in such applications as it features high stiffness as well as high energy absorption due to the filler pore volume. However, its damping ability is not sufficiently exploited in current finite element (FE) calculations due to a lack of advanced material models for simulating its impact response. An implementation of qualified concepts that account for plastic, strain rate dependent behavior requires additional information that has to be provided by systematic test series.
BAM recently started a research project to generate such data, subsequently to develop and to improve numerical methods for the analysis of impact limiters and damping foundation material and thus to optimize safety assessment tools for the design of transport and storage casks. A major part of this research concerns dynamic compression tests of variably shaped specimens conducted at a servo hydraulic 1MN impact testing machine as well as at a BAM facility for guided drop tests. This presentation focuses 100mm damping concrete cubes deformed vertically at constant rates under different constraint conditions. For example, a special fitting jig was constructed to subject the specimens to multi-axial loading. Thereby a deformation of 60% could be applied.
Simulation was conducted by FE code ABAQUS based on material models Concrete damaged plasticity and Crushable foam which both allow defining rate sensitive nonlinear stress-strain relations in compression beyond the classic metal plasticity approach.
Die mechanische Beanspruchung von Transport- und Lagerbehältern für radioaktive Stoffe gemäß den durch die IAEA vorgegebenen Prüfszenarien oder bei Unfällen, die während der Handhabung in einer kerntechnischen Anlage auftreten können, wird maßgeblich durch das Design der Stoßdämpfer und die Eigenschaften des jeweiligen Untergrundes beeinflusst. Da der Nachweis der Behälterintegrität und -dichtheit häufig an numerische Simulationen gekoppelt ist, sind für die sicherheitstechnische Auslegung der Konstruktion zuverlässige Informationen über das Energieabsorptionsvermögen der Werkstoffe und eine geeignete Umsetzung dieser Daten in FEM - Programme erforderlich. Die im Rahmen von Falluntersuchungen bei der BAM festgestellten, teilweise erheblichen Abweichungen zwischen experimentellen und berechneten Größen sind entsprechend darauf zurückzuführen, dass die zur Verfügung stehenden numerischen Verfahren das komplexe Verhalten der stoßdämpfenden Strukturen
nicht ausreichend präzise wiedergeben. Hiervon besonders betroffen sind Bauteile aus Holz und Polyurethan-Schaum (PU-Schaum), die zur Konstruktion von Behälterstoßdämpfern für die Transportkonfiguration eingesetzt werden, sowie Dämpferbeton, der in ausgewählten Bereichen im Fundament von Standort-Zwischenlagern eingebaut wird. Um die zugehörigen Materialmodelle weiter zu entwickeln und die dafür erforderliche Datenbasis zu schaffen, hat die BAM vor knapp zwei Jahren das vom BMBF geförderte Forschungsvorhaben ENREA (Entwicklung rechnerischer Analysemethoden für stoßdämpfende Strukturen beim Anprall oder Absturz von Abfallgebinden) gestartet. Wesentlicher Bestandteil ist ein systematisches Versuchsprogramm, bei dem die drei genannten Werkstoffe statisch und dynamisch hohen Druckbelastungen ausgesetzt werden. Relevante Versuchsparameter sind, neben der Dehnrate, die Temperatur und Lagerungsbedingungen sowie die Orientierung des Werkstoffes hinsichtlich der Belastungsrichtung. Dieser Beitrag präsentiert die wichtigsten Ergebnisse aus der ersten Versuchsphase, die durch weggesteuerte Versuche mit konstanten Prüfgeschwindigkeiten von 0,02 mm/s und 3000 mm/s gekennzeichnet ist. Darüber hinaus wird die Verwertung dieser Daten zur Anpassung von Materialmodellen auf der Grundlage von Nachrechnungen gezeigt, wobei die Möglichkeiten und Grenzen der verwendeten Konzepte Umrissen werden. Aufgrund des Umfangs, den die Versuche mit Holzwerkstoffen einnehmen, und des erforderlichen Aufwandes für die numerische Modellierung werden die entsprechenden Maßnahmen und Ergebnisse in einem eigenständigen Beitrag auf der KONTEC vorgestellt.
Während des Transportes sind Behälter für hoch radioaktive Abfälle durch stoßdämpfende Bauteile vor Einwirkungen, die aus Unfallszenarien gemäß den IAEA Regularien resultieren können, weitestgehend geschützt. Nach dem Entfernen dieser Komponenten im Rahmen der Einlagerung ins Zwischenlager müssen Vorkehrungen getroffen sein, um Beanspruchungen der Behälter aus möglichen Handhabungsunfällen im Empfangsbereich zu reduzieren. Die Maßnahmen müssen vor allem darauf abzielen, die stoßdämpfenden Eigenschaften der potentiellen Aufprallflächen zu optimieren. Da Standardmaterialien für Fundamente nur ein geringes Energieabsorptionsvermögen aufweisen, wurde durch die Firma HOCHTIEF eine neuartige Betonmixtur entwickelt, bei der ein spezieller Leichtzuschlag zum Einsatz kommen. Zur Charakterisierung dieses sogenannten Dämpferbetons liegen Standardkennwerte vor sowie Messwerte aus Eindringversuchen, die zur Qualitätssicherung für jede Produktcharge durchgeführt werden. Das stoßdämpfende Potential des neuen Werkstoffs kann jedoch nur dann vollkommen ausgeschöpft werden, wenn die Energieabsorption in numerischen Simulationen der Behälterabstürze über die gesamte Belastungsdauer zuverlässig wiedergegeben wird. Für die Implementierung und Anpassung eines entsprechenden Materialmodelis in einem Finite Elemente (FE) Programm
sind Daten aus systematischen Druckversuchen mit Variation der relevanten Einflussgrößen erforderlich. An der BAM werden daher im Rahmen eines werkstoffübergreifenden Forschungsvorhabens zur Untersuchung von stoßdämpfenden Strukturen auch die Eigenschaften von Dämpferbeton experimentell untersucht und zugehörige numerische Methoden entwickelt. Der aktuelle Beitrag behandelt die Ergebnisse der ersten Projektphase, in der kubische Probekörper mit der Kantenlänge 100mm bei unterschiedlichen Lagerungsbedingungen statisch und dynamisch gestaucht wurden. In nachfolgenden Versuchen wird der Einfluß der Probengröße ermittelt sowie die Eignung der verwendeten Materialmodelle anhand realistischer Belastungssituationen validiert.
Versuchsprogramm.
Mechanical drop test scenarios for Type B (U) packages according to the IAEA regulations have to be carried out onto the so-called “unyielding target” (usually with cask impact limiters) and onto the puncture bar respectively. They are predefined and do not require any further investigation of scenarios that really could happen on transportation routes. Cask accident scenarios in the framework of approval procedures for interim storage sites are derived from a detailed analysis of the handling procedures necessary from arrival of cask at the site to its storing position.
In that case, casks are usually handled without impact limiters. Dependent on possible drop heights, drop positions and floor properties, conservative cask accident scenarios are derived for further safety proofs.
According to the mechanical assessment concept of the considered approval procedure numerical calculations have to be provided by the applicant to demonstrate mechanical cask safety. Stresses and strains in the cask body as well as in the lid System have to be identified and assessed. Using the example of a 3-mvertical-drop of a transport and storage cask for spent fuel elements onto the floor construction made of damping concrete covered by screed, BAM developed a finite element model. The finite element code ABAQUS/Explicit™ was used. Results of experimental investigations are not available. Therefore parameter studies are necessary to identify the sensitivity of the finite element model to significant Parameters and to verify the finite element models according to the requirements of the Guidelines for the Numerical Safety Analyses for the Approval of Transport and Storage Casks for Radioactive Materials (BAM GGR-008).
The paper describes the modeling of the material behavior and attachment of bottom side cask components. Questions concerning the modeling of a crack length limiting reinforcement in the screed layer are discussed. The influence of the mesh density of the screed layer and its strength is considered as well. Finally, the developed finite element model can be used for a numerical safety assessment. It can help to understand the complex mechanisms of the interaction between the cask components and floor construction.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and for spent fuel transportation casks. In addition, they are also used for spent fuel storage and transportation casks (dual purpose casks (DPC)) as auxiliary seals to allow leakage rate measurements of metal barrier seals for demonstration of their proper assembling conditions. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal, and environmental conditions as well as irradiation during the entire operation period. Concerning DPC, degradation effects should be limited in a way that, for example, effects from potentially released decomposition elements may not harm e.g. metal barrier seals. Leakage rate measurements should be possible also after long interim storage periods prior to subsequent transportation.
Because of the complex requirements resulting from the various applications of containers for radioactive waste and spent nuclear fuel, BAM has initiated several test programmes for investigating the behaviour of elastomer seals. In this contribution the current status is described and first results are discussed.
Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level radioactive waste as well as in construction of the already licensed Konrad repository for low and intermediate level radioactive waste, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues.
The long-term performance of elastomer seals for lid systems of transport and storage casks, whether used as auxiliary seals in spent fuel casks or as primary seals for low and intermediate level waste packages, is an important issue in this context. The polymeric structure of these seals causes a complex mechanical behavior with time-dependent sealing force reduction.
The results of a comprehensive purpose-designed test program consisting of basic compression and tension tests as well as relaxation tests on unaged specimens of representative types of elastomers (fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM)) at different temperatures and strain rates are presented. They were used to identify the constitutive behavior and to obtain parameters for finite element material models provided by the computer code ABAQUS®. After estimating the influence of uncertainties such as Poisson’s ratio and friction coefficient by sensitivity analyses, the chosen parameters had to prove their suitability for the finite element simulation of the specimen tests themselves.
Based on this preliminary work the simulation of a specific laboratory test configuration containing a typical elastomer seal with circular cross section is presented. The chosen finite element material model and the implemented parameters had to show that they are able to represent not only the specimen behavior under predominantly uniaxial load but also the more complex stress states in real components. Deviations between the measured and calculated results are pointed out and discussed.
For the consideration of long-term effects in the simulation of elastomer behavior, test results of aged specimens are needed. First information about a new test program, started recently and planned to provide these data, are given.
The German nuclear waste management strategy consists of dry interim storage of spent fuel inside dual purpose casks and its subsequent direct final disposal in a deep geological repository. Interim storage is limited to 40 years so far, but will have to be extended until repository site selection and operation is concluded, potentially up to 100 years. In this context, research on the long term performance of safety relevant cask components and fuel rod integrity during such extended periods of time is of outmost importance. The barrier function of the fuel cladding depends on its integrity under operational and accidental conditions along with storage and subsequent transportation and is mainly affected over time by altering of the cladding microstructure and by thermo-mechanical conditions during reactor operation and subsequent wet and dry storage.
This paper focuses on failure mechanisms regarding cladding embrittlement caused by physical phenomena concerning hydrogen dissolution and precipitation of hydrides in the zirconium matrix. Within this context, potential cladding integrity issues under extended interim storage conditions followed by transportation are emphasized.
Delayed hydride cracking (DHC) is a well-known time-dependent temperature-activated phenomenon failure mechanism of the fuel cladding during reactor operation. The phenomenon consists of hydrogen diffusion and hydride precipitation at the tip of an initial crack and the propagation of the crack to an approximate distance equal to the length of the hydride. This failure mechanism is temperature-activated phenomenon and enhances along with thermal cycling of the fuel cladding, e. g. during reactor shutdowns. DHC shows limited relevance under quasi static storage conditions with continuously lowering temperatures. However, the literature points that DHC may occur when the temperature during storage decreases to a certain level after some decades and in combination with stress concentrations in the cladding material.
When spent fuel is transferred to dry storage by vacuum drying, the cladding temperature raises up to peak temperatures of ~370°C. Under these conditions, hydrides dissolute into the zirconium matrix up to the solubility limit defined by the peak temperature and this amount of hydrogen can precipitate in a radial re-oriented fashion due to the temperature decrease during storage. Cladding materials with radially precipitated hydrides show significant embrittlement. Radially oriented hydrides are perpendicularly oriented to hoop stresses representing the most critical configuration. Brittle failure of the cladding then occurs by crack propagation through radially oriented hydrides and finally through the zirconium matrix. The susceptibility to radial hydride precipitation depends on cladding material type and microstructure, hydrogen content, pre-drying hydride distribution, irradiation conditions, and temperature and stress histories during drying and storage operations.
This paper addresses major considerations concerning spent fuel cladding embrittlement due to hydride precipitation with regard to the boundary conditions of dry spent fuel storage in Germany. Analytical, numerical, and experimental approaches are to be discussed by BAM in order to identify the specific needs for future R&D work in that area with the purpose to provide the necessary data base for proper safety demonstration and evaluation along with future extended storage licensing procedures.
Experimental and numerical studies of shock absorbing materials for containers for radioactive waste
(2012)
Existing spent nuclear fuel (SF) and high active waste (HAW) management policies and practices worldwide are the result of past presumptions that sufficient reprocessing and/or disposal capacity would be available in the near term. Consequently, in the past many countries have developed specific solutions for different periods of time due to their individual national nuclear policies.
In Germany the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for SF and HAW management and transport and storage licenses have been issued accordingly. The current operation licenses for existing storage facilities have been granted for a storage period of up to 40 years. This concept has demonstrated its suitability for over 20 years so far. Relevant safety requirements have been assessed for the short-term as well as for the long-term for site-specific operational and accidental storage conditions. But in the meantime significant delays in the national repository siting procedure occurred which will make extended storage periods necessary in the future.
With the clear expectation of the need for extending spent fuel storage in Germany beyond the initial license period of maximum 40 years additional material data and knowledge about the long term performance and integrity of casks and internals like fuel rods will be required to meet major safety goals and regulatory requirements.
Based on a broad knowledge base about fuel cladding behavior, degradation mechanisms and related potential failure mechanisms, e. g. induced by reoriented Hydride precipitation, as illustrated in this paper, a specific gap analyses for the German situation regarding fuel conditions and cladding materials should identify the specific knowledge gaps to be addressed and closed in the near future. This is of specific interest as all spent fuel assemblies are going to be transferred to dry cask storage with the next decade and as a consequence of the German nuclear phase-out decision.
Within several decades, BAM as a Federal materials research institute gathered a broad range of expertise in the safety evaluation of materials, components and casks under operational and accidental thermal and mechanical conditions. This paper elucidates selected Basic considerations regarding technical and scientific knowledge about the long term aging performance and potential failure mechanisms of fuel cladding materials.
Under consideration of the national R&D funding policy which has been adapted to the extended interim storage or pre-disposal needs and the competences of BAM, its future R&D strategy is explained and some R&D objectives have already been identified. BAM will continue and expand ist engagement in the area of investigating fuel cladding material behavior in the long term and developing validated simulation and analyses tools in collaboration with national and international partners. R&D outcomes shall improve the knowledge-base to close identified knowledge gaps in the area of demonstrating fuel cladding integrity and to provide crucial information with regard to future safety assessments for the extended interim spent fuel storage.