Filtern
Dokumenttyp
Sprache
- Englisch (2) (entfernen)
Schlagworte
- Concrete (2) (entfernen)
Organisationseinheit der BAM
Investigating the spalling behaviour of a concrete mixture using large scale members is complex and expensive. Thus, the susceptibility of concrete to spalling is investigated by means of fire tests on small scale specimens. However, the reduction of the fire exposed surface increases the influence of boundary effects. Macrocracking and the water loss via the lateral surfaces reduce the impact of the thermomechanical and thermohydraulic damage mechanisms and therefore, lower the risk of spalling. Thus, the influence of different restraints on the spalling behaviour of intermediate scaled specimens (Ø=0.47 m; h=0.29 m) was investigated for two ordinary concrete mixtures. Both mixtures had the same composition except the type of aggregate. One mixture contained only quartzitic aggregates, whereas the other mixture was made with basalt grit as coarse aggregates. Applied steel rings restrained the thermal expansion of the specimen and prevented the loss of water, whereas applied steel sheet primarily reduced the loss of water during the fire test. Additionally, the fire exposed surface of one specimen of each mixture was pre-dried under controlled climate conditions and fire tested with applied steel rings. The results show a higher spalling volume for the ring restrained specimens compared to the other covering types. Further, the pre-dried boundary zone leads to delayed and decreased occurrence of spalling compared to the non-dried specimens for the concrete with quartzitic aggregates and to a prevention of spalling for the mixture with basalt aggregates. Additionally, the results show that the influence of the thermomechanical behaviour of the coarse aggregates increases with increasing restraint. The restrained conditions of the specimens with applied steel ring are comparable to the conditions in the centre of a large scale member. This test series is a further step for possible concept of steel ring restraint concrete specimens as “screening-tests” in upcoming projects.
This paper presents a probabilistic methodology based on the thermo-mechanical finite elements analysis to investigate the impact of the variability of the thermal properties of the concrete in the fire safety of structures. This is meant to evaluate if characteristic values or safety factors for the conductivity and specific heat are required during the semi-probabilistic structural fire safety assessment. To illustrate the use of the proposed methodology, this work includes a case-study with a tunnel lining which considers the uncertainties related to the thermal and mechanical properties of the concrete, the soil load, and the temperatures described by the standard temperature-time curve. Two failure criteria are considered: one was the maximum temperature of 300 °C at the reinforcement and the other based on the temperature-dependent strength as provided in the Eurocode EN 1992-1-2. Several finite element analyses are performed. The design of experiments is executed by a Correlation Latin Hypercube Sampling. The calculated probability of failure has different values depending on the adopted failure criteria. A sensitivity analysis using the Spearman's rank correlation coefficient was carried out and demonstrates that the uncertainty related to the specific heat has the greatest impact on the results.