Filtern
Dokumenttyp
- Zeitschriftenartikel (6)
- Vortrag (6)
- Beitrag zu einem Tagungsband (5)
Schlagworte
- Compression set (8)
- Ageing (7)
- Compression stress relaxation (4)
- Modelling (3)
- O-ring (3)
- Simulation (3)
- (U)HMWPE (2)
- Aging (2)
- Arrhenius (2)
- Compression Set (2)
- Irradiation (2)
- Leakage rate (2)
- SHPB (2)
- Sequential analysis (2)
- Stress relaxation (2)
- WAXD (2)
- Alterung (1)
- CSR (1)
- Chemical processes (1)
- Coefficient of Friction (1)
- Component tests (1)
- Continuous compression stress relaxation (1)
- Cross-linking (1)
- Degradative processes (1)
- EPDM (1)
- Elastomer (1)
- Elastomer Dichtung (1)
- Elastomers (1)
- Experiment (1)
- FTIR (1)
- HNBR (1)
- Heterogeneous ageing (1)
- IRHD (1)
- IRHD micro hardness (1)
- IRHD microhardness (1)
- Intermittent compression stress relaxation (1)
- Kinetic study (1)
- Leakage (1)
- Leakage Rate (1)
- Modeling (1)
- Numerical Simulation (1)
- O-Ring (1)
- Physical relaxation (1)
- Processes (1)
- Radioactive Waste (1)
- Recovery (1)
- Scission (1)
- Seal (1)
- Seal Behavior (1)
- TTS (1)
- Tightness (1)
- stress relaxation (1)
Organisationseinheit der BAM
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (6)
Elastomers are susceptible to chemical ageing, i.e., scission and cross-linking, at high temperatures. This thermally driven ageing process affects their mechanical properties and leads to limited operating time. Continuous and intermittent stress Relaxation measurements were conducted on ethylene propylene diene rubber (EPDM) and hydrogenated nitrile butadiene rubber (HNBR) samples for different ageing times and an ageing temperature of 125 °C. The contributions of chain scission and cross-linking were analysed for both materials at different ageing states, elucidating the respective ageing mechanisms. Furthermore, compression set experiments were performed under various test conditions. Adopting the two-network model, compression set values were calculated and compared to the measured data. The additional effect of physical processes to scission and cross-linking during a long-term thermal exposure is quantified through the compression set analysis. The characteristic times relative to the degradation processes are also determined.
At the Bundesanstalt für Materialforschung und -prüfung (BAM) in Division 3.4 Safety of Storage Containers, one of our tasks is to evaluate the safety of containers designed for disposal of low and intermediate radioactive waste. As such containers might be transported before and stored until disposal, safe enclosure of the radioactive inventory is important for this time span.
Elastomer O-rings are widely used as barrier seals in these containers. Thus, as for many other applications, an understanding of the practical effects of ageing degradation on elastomer seals during long-term exposure is mandatory for predicting the lifetime of such components. According to a long-term test programme on three kinds of rubbers (EPDM and FKM (relevant for application), HNBR (for comparison)), over several years we have studied the degradation and the change of mechanical properties (e.g. hardness, strain at break) at four different ageing temperatures (75 °C, 100 °C, 125 °C and 150 °C) as well as the change of sealing properties. Continuous and intermittent compression stress relaxation (CSR) measurements were performed in order to investigate the respective contribution of crosslinking and chain scission to the observed degradation effects. Thus, the degradation kinetics and mechanisms could be resolved more clearly. For assessing the seal performance, compression set (CS) and leakage rate measurements were conducted. The experimental results showed that the O-rings remained leak-tight under purely static conditions even when CSR, CS and mechanical properties already indicated far advanced degradation. For this reason, a modified leakage test involving a small and rapid partial decompression of the seal was developed that enabled determining an end-of-lifetime criterion for O-rings with a safety margin for thermal shrinkage and vibrations.
During an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and two ageing temperatures of 125∘C and 150∘C. To exclude possible diffusion-limited oxidation (DLO) effects that can distort the data, IRHD microhardness measurements were taken over the cross section of compressed O-rings. Continuous stress relaxation measurements were taken on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategy of the material model is based on our experimental investigations on homogeneously aged elastomer O-rings. The simulated results are in good agreement with the experiments.
At the Bundesanstalt für Materialforschung und -prüfung (BAM) in Division 3.4 Safety of Storage Containers, one of our tasks is to evaluate the safety of containers designed for disposal of low and intermediate radioactive waste. As such containers might be transported before and stored until disposal, safe enclosure of the radioactive inventory is important for this time span. Elastomer O-rings are widely used as barrier seals in these containers. Thus, as for many other applications, an understanding of the practical effects of ageing degradation on elastomer seals during long-term exposure is mandatory for predicting the lifetime of such components. According to a long-term test programme on three kinds of rubbers (EPDM and FKM (relevant for application), HNBR (for comparison)), over several years we have studied the degradation and the change of mechanical properties (e.g. hardness, strain at break) at four different ageing temperatures (75 °C, 100 °C, 125 °C and 150 °C) as well as the change of sealing properties. Continuous and intermittent compression stress relaxation (CSR) measurements were performed in order to investigate the respective contribution of crosslinking and chain scission to the observed degradation effects. Thus, the degradation kinetics and mechanisms could be resolved more clearly. For assessing the seal performance, compression set (CS) and leakage rate measurements were conducted. The experimental results showed that the O-rings remained leak-tight under purely static conditions even when CSR, CS and mechanical properties already indicated far advanced degradation. For this reason, a modified leakage test involving a small and rapid partial decompression of the seal was developed that enabled determining an end-of-lifetime criterion for O-rings with a safety margin for thermal shrinkage and vibrations.
Elastomer seals are used in many industrial applications due to their excellent mechanical properties at a wide range of temperatures. Their high versatility and recovery potential under several load conditions make them well suitable for the application in containers designed for transport, storage and/or disposal of radioactive materials. In containers for low and intermediate level radioactive waste, elastomer seals are used as barrier seals, and as auxiliary seals in storage and transportation casks (dual purpose casks) for heat generating radioactive waste, such as spent fuel and high-level waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered and prohibit an unnecessary cask handling. An extensive knowledge of the change of the elastomer’s properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the permanent safe enclosure of the radioactive material is mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have been already made and are still planned to scientifically support this task.
Compression stress relaxation and compression set were identified as key indicators of elastomer long-term performance and quantitatively investigated in comprehensive test programs. Among other representative types of elastomers, specimens made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the most important of their complex mechanical properties.
In the presented study, exemplary results were used to simulate the compression stress relaxation and the compression set of elastomer O-rings during aging. Regarding the influence of temperature, the time-temperature superposition principle is applied in the relaxation analysis of elastomer O-rings. The proposed model is implemented in the commercial finite element software ABAQUS/Standard® [1] with a sequential temperature displacement coupling. Numerical results match the experimental compression stress relaxation measurements well. The prediction of compression set values after long-term aging shows a relatively good agreement with the experimental results. Nevertheless, all input parameters derived from the specimen tests, additional assumptions concerning boundary conditions and modeling strategy are discussed with regard to the identified slight discrepancies.
The possibility to extend the finite element model to represent the O-ring seal’s ability to recover after a (fast) partial release is taken into account.
To improve the predictive capability of long-term stress relaxation of elastomers during thermo-oxidative ageing, a method to separate reversible and irreversible processes was adopted.
The separation is performed through the analysis of compression set after tempering. On the Basis of this separation, a numerical model for long-term stress relaxation during homogeneous ageing is proposed. The model consists of an additive contribution of physical and chemical relaxation.
Computer simulations of compression stress relaxation were performed for long ageing times and the results were validated with the Arrhenius treatment, the kinetic study and the time-temperature superposition technique based on experimental data. For chemical relaxation, two decay functions are introduced each with an activation energy and a degradative process. The first process with the lower activation energy dominates at lower ageing times, while the second one with the higher activation energy at longer ageing times. A degradation-rate based model for the evolution of each process and ist contribution to the total system during homogeneous ageing is proposed. The main advantage of the model is the possibility to quickly validate the interpolation at lower temperatures within the range of slower chemical processes without forcing a straight-line extrapolation.
Eine Aufgabe des Fachbereichs 3.4 Sicherheit von Lagerbehältern der Bundesanstalt für Materialforschung und -prüfung (BAM) ist es, die Sicherheit von Behältern zur Lagerung von radioaktivem Abfall mit vernachlässigbarer Wärmeentwicklung zu bewerten. Da solche Behälter vor der Entsorgung transportiert und gelagert werden, ist während dieser Zeit ein sicherer Einschluss des radioaktiven Inhalts von größter Bedeutung. Zur Abdichtung dieser Behälter sind Elastomer-O-Ringe weit verbreitet. Um für solche, wie auch für viele andere Anwendungen, eine Voraussage über die Lebensdauer dieser Komponenten treffen zu können, ist es unerlässlich zu verstehen, welchen Einfluss der durch Alterung hervorgerufene Abbau auf Dauer auf die Elastomerdichtungen hat. In einem Langzeittest wurden drei Kautschukarten (EPDM und FKM, die für die Anwendung relevant sind, und HNBR als Vergleich) über mehrere Jahre untersucht. Dabei wurden die Veränderungen der mechanischen Eigenschaften (z. B. Härte und Bruchdehnung) bei vier verschiedenen Alterungstemperaturen (75 °C, 100 °C, 125 °C und 150 °C) sowie das Dichtungsverhalten betrachtet. Um den Einfluss von Vernetzung und Kettenspaltung auf die beobachteten Alterungseffekte zu bestimmen, wurden Messungen zur kontinuierlichen und intermittierenden Druckspannungsrelaxation durchgeführt. Dadurch konnten Erkenntnisse über Kinetik und Mechanismus der Abbaureaktionen
gewonnen werden. Zur Einschätzung des Dichtungsverhaltens wurden Durckverformungsrest und Leckagerate gemessen. Die Ergebnisse zeigen, dass die O-Ringe unter statischen Bedingungen auch dann dicht halten, wenn die Werte für Druckverformungsrest, Druckspannungsrelaxation und mechanische Eigenschaften schon auf einen fortgeschrittenen Alterungsabbau hindeuten. Aus diesem Grund wurde ein modifizierter Dichtigkeitsversuch mit einer geringen und schnellen teilweisen Entlastung der Dichtung entwickelt, mit dessen Hilfe sich ein Lebensdauerkriterium bestimmen lässt, das eine Sicherheitsspanne für thermische Schrumpfung und Vibrationen beinhaltet.
Elastomer seals are used in many industrial applications due to their excellent mechanical properties at a wide range of temperatures. Their high versatility and recovery potential under several load conditions make them well suitable for the application in containers designed for transport, storage and/or disposal of radioactive materials. In containers for low and intermediate level radioactive waste, elastomer seals are used as barrier seals, and as auxiliary seals in storage and transportation casks (dual purpose casks) for heat generating radioactive waste, such as spent fuel and high-level waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered and prohibit an unnecessary cask handling. An extensive knowledge of the change of the elastomer’s properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the permanent safe enclosure of the radioactive material is mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have been already made and are still planned to scientifically support this task.
Compression stress relaxation and compression set were identified as key indicators of elastomer long-term performance and quantitatively investigated in comprehensive test programs. Among other representative types of elastomers, specimens made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the most important of their complex mechanical properties.
In the presented study, exemplary results were used to simulate the compression stress relaxation and the compression set of elastomer O-rings during aging. Regarding the influence of temperature, the time temperature superposition principle is applied in the relaxation analysis of elastomer O-rings. The proposed model is implemented in the commercial finite element software ABAQUS/Standard® [1] with a sequential temperature displacement coupling. Numerical results match the experimental compression stress relaxation measurements well. The prediction of compression set values after long-term aging shows a relatively good agreement with the experimental results. Nevertheless, all input parameters derived from the specimen tests, additional assumptions concerning boundary conditions and modeling strategy are discussed with regard to the identified slight discrepancies.
The possibility to extend the finite element model to represent the O-ring seal’s ability to recover after a (fast) partial release is taken into account
The main task of the division "Safety of Storage Containers" at BAM is the safety assessment of storage containers for radioactive waste. A sufficient sealing of bolted lid systems for the safe containment of the waste for transport, storage and disposal is very important. Extensive knowledge of the change of the elastomer’s properties during ageing and the availability of reliable end-of-lifetime criteria is mandatory to guarantee long term safe enclosure.
In a long-term test programme over 5 years we have studied the degradation and the change of sealing properties of several elastomers, including EPDM, at four different ageing temperatures (75 °C, 100 °C, 125 °C and 150 °C). Compression stress relaxation (CSR) and compression set (CS) experiments were carried out. It has been found that when the data does not cover a sufficient time frame necessary for the evolution of the degradation of a chosen property, a curvature in the Arrhenius relationship is observed. For CSR, the curvature was observed for samples aged up to 186 days. As for CS experiments, the curvature was detected for sample aged up to 2 years. To cover the possible lack of experimental long-term data at low temperatures, a numerical model for CSR was developed and longer ageing times for the simulation were adopted. A degradation-rate based model for the evolution of degradative processes is proposed. The main advantage of the model is the possibility to quickly validate the interpolation at lower temperatures within the range of slower chemical processes without forcing an Arrhenius straight-line extrapolation. The model was also applied to CS experiments and validated by the 5 years experimental results where the curvature was gone, and the degradation property has followed an Arrhenius relationship. In the figure the contribution of the two degradative processes are shown over CS and CSR respectively.
During an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and an ageing temperature of 125 °C. To exclude possible diffusion limited oxidation (DLO) effects that can distort the data, IRHD micro hardness measurements were performed over the cross-section of compressed O-rings. Continuous stress relaxation measurements were conducted on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategy of the material model is based on our experimental investigations on homogeneously aged elastomer O-rings. The simulated results are in good agreement with the experiments.