Corrosion resistance of duplex stainless steel (SS) (UNS S32101) and super austenitic SS (UNS NO8031) (Alloy 31) was investigated in crevice conditions in a saline brine. Rubber was used to form a metal/non-metal-crevice confguration. UNS NO8031 did not exhibit any signs of pitting corrosion even by applying potentials much more positive than the corrosion potential.
Condensates from the gas stream in simulated CO2 transport pipelines have been identified during the experiments in the laboratory. Because of their acidic origin the corrosion resistance of pipeline steels used for CCS (carbon capture and storage) technology might be limited. Over the last years it has become clear that the amount of water and acid building constituents in the CO2 stream has to be controlled very well. In this work, condensates formed in experiments using gaseous CO2 containing high amounts of water, NO2 and SO2 were analyzed, replicated, and used for extensive electrochemical experiments. These highly acidic condensates were enriched with CO2 and then applied to characteristic steels planned to use in the CCS transport chain. Even high alloy steels are susceptible to localized corrosion under these conditions. The results implicate that condensation of aggressive acid droplets has to be avoided or the locations where condensation takes place have to be controlled extensively.
The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness.
The corrosion behaviour of martensitic stainless injection-pipeline steel X46Cr13 exposed to CO2 saturated artificial saline brine with high chloride concentration similar to onshore CCS-site at Ketzin, Germany has been investigated by means of electrochemical technique and microscopic observations at short exposure times (up to 24?h) and by mass loss and metallographic observations at exposure times up to 17520?h. Pitting corrosion kinetics has been characterised and the predictions about the corrosion mechanism are made.