AZ31 Mg alloy sheet was welded using a gas-tungsten arc (GTA) process over inserts containing 2.3-9.3 wt.% Al. The welded specimens were susceptible to SCC in distilled water, with susceptibility increasing with decreasing weld metal Al (or β particle) concentration. Primary stress corrosion cracks initiated at the weld metal-HAZ interface by stress-assisted localised dissolution and propagated through the weld and base metals by transgranular and intergranular H-assisted fracture (TG-HAF and IG-HAF) respectively. The IG fracture mode may be intrinsic to the texture imparted upon the base metal by rolling. The increase in SCC susceptibility with decreasing weld metal Al concentration is contrary to the purported roles of β particles in promoting localised corrosion and as crack nucleation sites, but corresponds with increases in weld - base metal galvanic current density and weld metal localised corrosion susceptibility.
Carbon arc-air gouging is a common technology when repairing defects in welded structures. Often this technique is applied in repeated cycles even on the same location of the joint. Due to the multiple heat input by gouging and subsequent re-welding, the residual stresses are strongly influenced. This can become crucial when microstructure and mechanical properties are adversely affected by multiple weld reparations. Knowledge about the relation of gouging and residual stresses is scarce but important when high strength steels, which are sensitive to residual stresses, are processed. The present study shows the effect of repair welding on a high strength steel structural element. The weld and the heat affected zone were subjected to multiple thermal cycles by gouging and subsequent repair welding. The residual stresses were determined by X-ray diffraction at different positions along the joint. The results showed that the residual stress level has increased by the repair cycles. This is most pronounced for the heat affected zone. Adapted welding procedures may prevent detrimental residual stress distributions.