Filtern
Dokumenttyp
Sprache
- Englisch (6)
Referierte Publikation
- ja (6)
Schlagworte
- Friction stir welding (2)
- Al/Ti dissimilar joints (1)
- Aluminum alloy 2024-T3 (1)
- Antifouling (1)
- Atomistic models (1)
- Bacterial adhesion (1)
- Biofilm (1)
- Dissimilar friction stir welding (1)
- Finite element simulation (1)
- Heat generation (1)
Organisationseinheit der BAM
The paper deals with a numerical finite element simulation of the residual stress evolution in friction stir welding of 6 mm thick aluminum alloy AA2024-T3. The transient thermal field during the welding process was calculated with the commercial code COMSOL Multiphysics 5.0. Therefore, a thermal-pseudo-mechanical (TPM) heat source was implemented. A subsequent mechanical simulation was performed with varying hardening models for different welding speeds of 60 and 300 mm/min. The influence of softening of the material, which was due to hardening precipitation dissolution associated to the heating, was also investigated. Experiments in terms of thermocouple measurements as well as Vickers hardness and X-ray measurements of the residual stresses were conducted and compared to numerically obtained results. A qualitatively as well as quantitatively good agreement was found for different applied welding speeds.
Active antibacterial and antifouling surface coating via a facile one-step enzymatic cross-linking
(2017)
Prevention of microbial contamination of surfaces is one of the biggest challenges for biomedical applications. Establishing a stable, easily produced, highly antibacterial surface coating offers an efficient solution but remains a technical difficulty. Here, we report on a new approach to create an in situ hydrogel film-coating on glass surfaces made by enzymatic cross-linking under physiological conditions. The cross-linking is catalyzed by horseradish peroxidase (HRP)/glucose oxidase (GOD)-coupled cascade reactions in the presence of glucose and results in 3D dendritic polyglycerol (dPG) scaffolds bound to the surface of glass.
These scaffolds continuously release H2O2 as long as glucose is present in the system. The resultant polymeric coating is highly stable, bacterial-repellent, and functions under physiological conditions. Challenged with high loads of bacteria (OD540 = 1.0), this novel hydrogel and glucose-amended coating reduced the cell viability of Pseudomonas putida (Gram-negative) by 100% and Staphylococcus aureus (Gram-positive) by ≥40%, respectively. Moreover, glucose-stimulated production of H2O2 by the coating system was sufficient to kill both test bacteria (at low titers) with >99.99% Efficiency within 24 h. In the presence of glucose, this platform produces a coating with high effectiveness against bacterial adhesion and survival that can be envisioned for the applications in the glucose-associated medical/oral devices.
Ever more stringent regulations on greenhouse gas emissions from transportation motivate efforts to revisit materials used for vehicles. High-strength aluminium alloys often used in aircrafts could help reduce the weight of automobiles, but are susceptible to environmental degradation. Hydrogen ‘embrittlement’ is often indicated as the main culprit; however, the exact mechanisms underpinning failure are not precisely known: atomic-scale analysis of H inside an alloy remains a challenge, and this prevents deploying alloy design strategies to enhance the durability of the materials. Here we performed near-atomic-scale analysis of H trapped in second-phase particles and at grain boundaries in a high-strength 7xxx Al alloy. We used these observations to guide atomistic ab initio calculations, which show that the co-segregation of alloying elements and H favours grain boundary decohesion, and the strong partitioning of H into the second-phase particles removes solute H from the matrix, hence preventing H embrittlement. Our insights further advance the mechanistic understanding of H-assisted embrittlement in Al alloys, emphasizing the role of H traps in minimizing cracking and guiding new alloy design.
Understanding the void defect formation mechanism and simultaneous predicting the tool service life in friction stir welding are critical for optimizing the welding parameters. However, the void defect formation mechanism in friction stir welding is not yet elucidated. In this study, a novel integrated thermal-fluid-structure coupling model of the friction stir welding process was proposed for simultaneous prediction of the weld formation and tool service life. A new non-uniform distribution model of the tool-workpiece contact pressure was proposed to describe the interaction between the tool and the workpiece. The void defect formation mechanism was quantitatively studied using the proposed integrated thermal-fluid-structure coupling model. The results show that the plastic material flows in the horizontal direction and can completely fill the cavity behind the tool for the welding condition of forming a sound weld. While the tool-workpiece contact interfacial frictional shear stress in the rear of the tool is decreased significantly which leads to a severe decrease in the plastic material flow velocity. Therefore, after bypassing the tool from the retreating side, the plastic material at the bottom of the weld stagnates, and void defect forms in the middle and lower part of the weld at the advancing side. The difference between the maximum and the minimum tool-workpiece contact pressure could serve as a numerical criterion to predict void defects. A sound joint is formed when the difference is lower than the critical value of 15 MPa, while a void defect is formed in the weld if it is higher than this critical value. The maximum equivalent stress acting on the tool is located at the pin root with severe stress concentration at a high welding speed. The front of the tool is subjected to tensile stress while its rear is subjected to compressive stress, therefore the tool is apt to fracture at its root under an inappropriate welding condition. The average normal stress of the tool varies periodically with its period consistent with the rotation period of the tool. The service life of the tool is decreased with the increase in welding speed and the decrease in rotation speed. The model is validated by experimental results.
Friction stir welding (FSW) has the capacity to join the Al/Ti dissimilar structures with superior mechanical properties. The microstructures and mechanical characteristics of Al/Ti dissimilar FSW joints are determined by the heat and mass transfer during the welding process. However, a quantitative study of the Al/Ti dissimilar FSW process is lacking. Therefore, using the computational fluid dynamics (CFD) and volume of fluid (VOF) approach, a multi-phase model was constructed for quantitatively analyzing the heat and mass transfer behaviour in dissimilar FSW of TC4 titanium alloy and AA2024-T4 aluminium alloy. The mixed material was treated as a functionally graded material (FGM) to compute the thermophysical characteristics at the weld nugget zone (WNZ). Due to the vast disparity in the thermophysical characteristics of aluminum and titanium alloy, the temperature field in Al/Ti dissimilar FSW was severely asymmetric. The temperature of titanium alloy on the advancing side (AS) was higher than that of aluminium alloy on the retreating side (RS) at the same distance from the tool centre line near the tool shoulder, but it was lower than that of aluminium alloy on the RS without the influence of the shoulder. Due to the high flow stress of titanium alloy, plastic material flow mostly occurred on the RS of aluminium alloy in the Al/Ti dissimilar FSW, with its percentage exceeding 80%. This model was validated by experiment results.
The uncontrolled Li dissolution/deposition dynamics and rapid Li pulverizations hinder the widespread deployment of Li metal batteries (LMB). Designing a Li composite electrode possessing a mechanically robust and lithiophilic three-dimensional (3D) framework represents a promising strategy to address these challenges. This study involves the preparation of three uniquely tailored Li-B-Mg composites using a combined metallurgical process of melting, casting, and rolling, along with the synergistic application of in situ X-ray computed tomography (CT) and post-mortem failure analysis to explore the most promising composite electrode candidate for LMBs. During the in-depth investigation, the optimal 70Li-B-Mg composite electrode stands out due to its robust skeleton fiber structure, uniform Li dissolution/deposition characteristics and high capacity of free-Li. Its promising prospects for enabling high-performance LMBs are showcased by the superior performance of the built Li||O2, Li||LiFePO4, Li||NCM622 and Li||NCM811 battery systems. This work offers a novel approach for exploring universally applicable and robust Li composite electrodes to realize high-performance LMBs using in situ CT analysis.