Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (36) (entfernen)
Schlagworte
- Compression set (11)
- Ageing (6)
- Elastomer (6)
- Low temperature behaviour (6)
- Sealing material (6)
- Dynamic mechanical analysis (4)
- Leakage rate (4)
- Rubber (4)
- Seal (4)
- Compression (3)
Organisationseinheit der BAM
Paper des Monats
- ja (2)
Casks for the transport and storage of heat generating radioactive waste in Germany are normally provided with screwed lid systems, which are in most cases equipped with double jacket metal seals with an inner spring wire to provide long term resistance to the seal compression force. Preservation of the high sealing quality of those seals under operational and accidental stress conditions is essentially important to the safety of those casks. Relative displacements of the lid system surfaces caused by specific impact scenarios cannot be excluded and have to be evaluated with respect to a possible increase in the leakage rate.
To get representative data for such metal sealed lid systems, BAM has developed a special conceptualised flange system placed in an appropriate testing machine for relevant mechanical loading of the metal seals under static and cyclic conditions. Furthermore, the flange system enables continuous measurement of the standard helium leakage rate during each test.
The primary aim of the investigation is to identify the correlation between variation of installation conditions (axial displacements) caused by external loads and the standard helium leakage rate. An essential parameter in this case is the useable resilience ru of a metal seal under relevant stress conditions. The useable resilience ru is the vertical difference in the cross-section between the seal's assembling status and the point where the leakage rate, by means of external load relieving, exceeds the quality criterion of 10-8 Pa m3 s-1. Load relieving can instantly occur due to modification of the seal groove dimension caused by accident impacts and deformation of the lid system. Furthermore, component specific basis data for the development of finite element calculation models should be collected. In the tests, seals are subjected to static and cyclic loads. All tests are performed at ambient temperature.
This paper presents the test configuration, different test series and results of the current experiments. Typical load-displacement-leakage rate correlations are presented and discussed.
A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment.
Elastomers are widely used as the main sealing materials for containers for low and intermediate level radioactive waste and as an additional component to metal seals in spent fuel and high active waste containers. The safe encapsulation of the radioactive container inventory has to be guaranteed according to regulation and appropriate guidelines for long term storage periods as well as for temperatures as low as -40°C during transport. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of elastomers are strongly temperature dependent. At low temperatures, this is caused by the rubber-glass transition (abbreviated: glass transition). During continuous cooling, the material changes from a rubber-like entropy elastic to a stiff energy elastic behaviour, which allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition, but the minimum working temperature limit is not defined precisely; this can cause problems during the above noted applications. Therefore, the lower operation temperature limit of elastomer seals must be determined in dependence of the material properties. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) are combined with standardised measurements to determine the compression set according to ISO 815. To reduce the test time of the standard tests, a faster technique than normally used was developed. Additionally, the breakdown temperature of the sealing function of complete O ring seals was measured in a component test set-up to compare it with the results of the other tests. The experimental set-up is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. The materials (seals and test sheets) were purchased from a commercial seal producer.
The aging management system for the mechanical components of nuclear power plants (NPPs) must be established and used by the licensee in such a way that the quality of safety relevant components is guaranteed for the completely designed lifetime of the NPP. This demands an extensive plant life management with special emphases on the knowledge of the degradation in material properties. The basic safety concept in Germany observes this circumstance. Lifetime extension of the German NPPs is an aim of the current valid coalition agreement of the German government. Operational extension of interim storage facilities requires, in comparison to the aging management system for NPP, an aging management system adapted to the Special circumstances of spent fuel storage casks. Extension of interim storage periods for spent fuel casks beyond the designed lifetime requires, in comparison to the components of an NPP, an increasing knowledge of material degradation with potential impact on cask integrity, e.g. leak tightness. Dry interim storage in Germany has been approved for 40 years. After that time, according to the present strategy, a final repository should be available. However, until now, such a final facility still does not exist, and the German exploration and licensing process is heavily delayed. Currently, discussions are continuing regarding further exploration of the Gorleben salt mine. There is willingness to overcome this situation that is clearly described in the available coalition agreement of the federal government. Anyway, however, the prediction is viewed; a repository for heat generating radioactive waste in Germany will not be available in the near future and may not be available when first storage facilities and casks reach their 40 years of approved lifetime, which will occur in ~25 years starting from now. Therefore, the question must be asked:
what has to be done with the existing storage casks in the interim facilities? May these casks be fit for continued use, with an extension of the storage period? One option is to have an aging management system, which creates enough information about the technical condition of safety relevant cask properties. This is the basis for safety evaluation for extended storage periods. In the present paper, possible aging mechanisms for high level waste storage casks are discussed, as well as the influence of the time dependent changes of the component properties.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
The molecular dynamics of liquid-crystalline polymethacrylates with biphenyl in the side group forming a highly ordered smectic E phase at low temperatures is investigated by dielectric spectroscopy (DS). Although no glass transition is found by DSC, DS detects a relaxation in the smectic E phase resembling to glassy dynamics. The temperature dependence of its relaxation rate is Arrhenius like at low temperatures, which changes to a VFT law at higher temperatures. Such a behavior is found to be characteristic for glassy dynamics in confining space. It is discussed, considering the structure of the polymers as nanobiphasic consisting of liquid-crystalline layers while the backbones fill the interlayer space. A comparison is made to polymethacrylates having phenyl benzoate as mesogen.