Polyhedral oligomeric silsesquioxane with phenethyl substituents (PhenethylPOSS) as nanofiller was incorporated within Poly(bisphenol A carbonate) (PBAC) as matrix. Dielectric spectroscopy proved an almost complete miscibility of PhenethylPOSS up to 7 wt. %. At higher concentrations phase separation yields composites with a PBAC-rich matrix and POSS-rich domains which posses well shaped interfaces. The nanocomposites were also investigated with respect to their gas transport behaviour. An increase of the gas permeability was found at higher PhenethylPOSS concentrations, which is due to the phase separated structure.
The study of protein corona formation on nanoparticles (NPs) represents an actual main issue in colloidal, biomedical and toxicological sciences. However, little is known about the influence of polymer shells on the formation and time evolution of protein corona onto functionalized NPs. Therefore, silicapoly(ethylene glycol) core–shell nanohybrids (SNPs@PEG) with different polymer molecular weights (MW) were synthesized and exhaustively characterized. Bovine serum albumin (BSA) at different concentrations (0.1–6 wt%) was used as model protein to study protein corona formation and time evolution. For pristine SNPs and SNPs@PEG (MW = 350 g/mol), zeta potential at different incubation times show a dynamical evolution of the nanoparticle–protein corona. Oppositely, for SNPs@PEG with MW ≥2000 g/mol a significant suppression of corona formation and time evolution was observed.
Furthermore, AFM investigations suggest a different orientation (side-chain or perpendicular) and Penetration depth of BSA toward PEGylated surfaces depending on the polymer length which may explain differences in protein corona evolution.