Calcium alkaline phosphate scaffolds for bone regeneration 3D-fabricated by additive manufacturing
(2012)
Calcium alkaline phosphate granulates can be used for substitution of several bone defects but for the reconstruction of large skeletal parts in the maxillofacial and orthopaedic fields fitted scaffolds are preferable. Within the additive manufacturing methods, the 3D printing process offers exciting opportunities to generate defined porous scaffolds. We used a R1 printer from ProMetal Company, USA, for producing scaffolds directly from a ceramic powder. For this direct free form fabrication technology the powder has to possess a lot of specific properties both for the generation of a stable green body and also for the subsequent sintering preparation. For this printing process we prepared different granules in a fluidized bed process containing Ca2KNa(PO4)2 as main crystalline phase. Granules were characterized by different methods and several sieve fractions were used for preparing disc like and cylindrical parts. The suitability of granules for this printing process was determined by porosity and strength of produced bodies. Next to granules' performance both of these properties can be directly influenced by 3D printing process parameters. With knowledge of suitable process parameters scaffolds with different porosity in a respective desired design can be created. In this study, cylindrical scaffolds with graded porosity were produced for bone regeneration of segmental defects in maxillofacial surgery and dental implantology by tissue engineering.
Hydroxyapatite (HA) is a bioceramic material with excellent biological properties. However, these properties are strongly dependent of ist crystallinity degree, with high values of crystallinity associated to poor resorption rates and bioactivity. This work evaluates the properties of HA samples produced by two different free-forming conformation methods, CNC machining and 3D printing. In both cases, porous gypsum samples were produced and subsequently converted into HA in a reaction with di-ammonium hydrogen phosphate at 100°C and pH 8. A total conversion of the samples was achieved after 36 h independently of the conformation method used. The microstructure, however, before and after the conversion is showed to be dependent on the method used. After conversion the machined samples achieved a Maximum compressive strength of 3.5 MPaforporosities of circa 80%, while 3D printed samples achieved a tensile strength of 2.0 MPa by porosities of 61%.