The lifetime reduction of cyclically loaded AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2-saturated hot thermal water is demonstrated in in situ-laboratory experiments (60 °C, brine: Stuttgart Aquifer, flowing CO2: 30 L/h). SN plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion and corrosion fatigue behavior. Maximum number of cycles (here 12.5 × 106 cycles to failure) is reached at σa = 173 MPa. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists and pit corrosion prior to crack initiation may be identified as failure cause.
In corrosive environments such as CCS bore holes or geothermal power plants the materials loaded cyclically are also exposed constantly to the highly corrosive hot thermal water. The lifetime reduction of (X46Cr13, AISI 420C) is demonstrated in in-situ-laboratory experiments (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 Nl/h, CO2). S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue is most likely failure cause.