Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (89)
- Beitrag zu einem Tagungsband (50)
- Zeitschriftenartikel (30)
- Posterpräsentation (8)
- Beitrag zu einem Sammelband (5)
- Forschungsbericht (5)
- Buchkapitel (1)
- Dissertation (1)
- Sonstiges (1)
Schlagworte
- Tensile properties (15)
- BAM-Liste (14)
- Dangerous goods (14)
- Sealing materials (12)
- Biodiesel (11)
- Biofuels (11)
- Compatibility (11)
- BAM-List (9)
- Polyethylene grades (9)
- Shore hardness (9)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (27)
- 3.2 Gefahrguttanks und Unfallmechanik (27)
- 7 Bauwerkssicherheit (9)
- 7.6 Korrosion und Korrosionsschutz (9)
- 1 Analytische Chemie; Referenzmaterialien (3)
- 1.4 Prozessanalytik (3)
- 2 Prozess- und Anlagensicherheit (3)
- 2.1 Sicherheit von Energieträgern (3)
- 8 Zerstörungsfreie Prüfung (3)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (3)
Eingeladener Vortrag
- nein (89)
The notched impact strength at -30 °C is one of the selected properties, together with the corresponding test method and tolerances, for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk containers (IBCs) for the transport of dangerous goods.
The marginal drop heights determined with the drop test at -18 °C after pre-storage of the test samples with 55 % nitric acid at 40 °C only partly related to the notched impact strength at -30 °C. The Charpy method is only suitable for classifying the grade in relation to toughness behavior and using this classification for comparison with other grades. Notched impact strength can provide a qualitative indication if the test samples fail under shock forces.
Conditioning the design types with 55 % nitric acid for 21 days at 40 °C causes an increase in the marginal drop heights of the design types in drop tests at -18 °C when compared with design types without pre-storage. Post-crosslinking of the grades increases stiffness because of the acidic influence.
Resistance to stress cracking by wetting solution is one of the selected properties together with the corresponding test method FNCT and tolerances for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk Containers (IBCs) for the transport of dangerous goods.
The environmental stress crack resistance determined by Full Notch Creep Test (FNCT) represents the impacts from the stacking tests at 40 °C performed with Standard liquid wetting solution (without pre-storage) and with normal butyl acetate saturated wetting solution (pre-storage with normal butyl acetate). Environmental stress crack resistance determined with FNCT for the polyethylene grades was related to the times to failure of different jerrican samples made of these grades in stacking tests with 5 % wetting solution and a n-butyl acetate saturated wetting solution (pre-storage with n-butyl acetate) at 40 °C. The FNCT is suitable for comparison of polyethylene grades in relation to environmental stress crack resistance independent of their use as drum, IBC or jerrican material. The stiffness of polyethylene grades should be taken into account to the comparison as jerricans are not only chemically but also mechanically stressed.
Technically high-quality hollow articles made of polyethylene have proved many times their value as dangerous goods packagings. Design type tests according to the international regulations for the transport of dangerous goods - drop test, stacking test, hydraulic pressure test and leakproofness test must be performed for every design type and manufacturer. The properties melt flow rate (MFR), relative density (D), low temperature notched Impact strength (N.I.S.) at -30 °C, environmental stress crack resistance (FNCT) and resistance to oxidative degradation Ox by nitric acid (determined by the increase of MFR) have been selected together with the corresponding test methods and tolerances for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for dangerous goods packagings and intermediate bulk containers (IBCs) – EN 15507. We wanted to proof the practical relevance of this standard by comparing the relationship between the results of the FNCT and the times to failure of design types in stacking tests with wetting solution and normal butyl acetate saturated wetting solution.
Resistance to stress cracking by wetting solution is one of the selected properties together with the corresponding test method FNCT and tolerances for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk containers (IBCs) for the transport of dangerous goods.
The environmental stress crack resistance determined by Full Notch Creep Test (FNCT) represents the impacts from the stacking tests at 40 °C performed with standard liquid wetting solution (without pre-storage) and with normal butyl acetate saturated wetting solution (pre-storage with normal butyl acetate).
Environmental stress crack resistance determined with FNCT for the polyethylene grades was related to the times to failure of different jerrican samples made of these grades in stacking tests with 5% wetting solution and a n-butyl acetate saturated wetting solution (pre-storage with n-butyl acetate) at 40 °C. The FNCT is suitable for comparison of polyethylene grades in relation to environmental stress crack resistance independent of their use as drum, IBC or jerrican material. The stiffness of polyethylene grades should be taken into account to the comparison as jerricans are not only chemically but also mechanically stressed.
More than 400 Mt of dangerous materials are transported in Germany every year, of which 150 Mt are by road. Tank containers, tank vehicles and rail tank cars are used for the carriage of dangerous goods in large quantities. Data on the operating life of tanks are only available, in practice, to a minor degree. They are only partly published, mainly after accidents.
The BAM-List - Requirements for Tanks for the Carriage of Dangerous Goods, which has compatibility evaluations of metallic and polymeric materials, has been the basis for substance-related prototype approvals for tank containers and portable tanks designed for the carriage of dangerous goods by the BAM since publication of the first edition in 1989. These data are also used for the approval of rail tank cars and road tank cars and are used as a source of knowledge not only in Germany but also worldwide.
Tank leakages caused by tanks or rail tank cars being made of tank and sealing materials which are not resistant to the fill goods are avoided by using the material resistance data of the BAM.
Corrosion damage is among the main causes of damage. Uniform and non-uniform area corrosion without mechanical stress in aqueous substances is one of the most frequent types of corrosion during the transport of chemicals in tanks. Much damage by pitting corrosion occurs during the transport of substances containing chlorides or substances which separate chloride ions in the presence of moisture.
Operational stresses are caused by the effects of both the road and the dangerous goods being transported. Mechanical damage often results from long-term overstressing and occurs after longer operating times.
Operational failures cause damage which may appear during the service of tank containers, road tank cars or rail tank cars. The damage results from the inattention of employees when opening and closing the valves. Traffic accidents also cause damage to tanks and frames.
Many cases of damage are due to weld area cracks resulting from four basic errors in construction, material, manufacturing and operation. Manufacturing errors can be undetected and the starting point of cracks which only grow under service conditions.
Manufacturing errors result from variations in measurement and design, fittings, state of surface (hardness, abrasiveness) and mechanical surface damage (scratches, cracks). Incorrectly welded joints and errors during mechanical deformation are typical mistakes when installing the component parts. Variations in the wall thickness or combinations of different materials lead to manufacturing errors too. A lot of tanks are not used for the transport of dangerous goods before the end of their service life as they do not fulfil the revised technical safety requirements in the Dangerous Goods Regulations.
Predictions in the BAM-List based on literature data and corrosion test results are reflected in the service (operating) life. Rail tank cars made of carbon steel, for example, which are mainly used for the transport of petroleum products, can achieve a service life of 40 – 50 y.
Rail tank cars produced of austenitic CrNi- or CrNiMo-steel can reach an operating life of at least 30 y, whereby the corrosiveness of the transport substances plays an important role.
The notched impact strength at -30 °C is one of the selected properties, together with the corresponding test method and tolerances, for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk containers (IBCs) for the transport of dangerous goods.
The marginal drop heights determined with the drop test at -18 °C after pre-storage of the test samples with 55 % nitric acid at 40 °C only partly related to the notched impact strength at -30 °C. The Charpy method is only suitable for classifying the grade in relation to toughness behavior and using this classification for comparison with other grades. Notched impact strength can provide a qualitative indication if the test samples fail under shock forces.
Conditioning the design types with 55 % nitric acid for 21 days at 40 °C causes an increase in the marginal drop heights of the design types in drop tests at -18 °C when compared with design types without pre-storage. Post-crosslinking of the grades increases stiffness because of the acidic influence.
The material parameters melt flow rate MFR, density D, notched impact strength N.I.S. at -30 °C, stress crack resistance FNCT and resistance to oxidative degradation Ox (determined by the increase of MFR) have been selected for a comparison of polyethylene grades for one design type in the “European Standard EN 15507 - Transport packaging for dangerous goods - Comparative material testing of polyethylene grades”. The parameters have a systematic relationship with design type tests. The notched impact strength at -30 °C and the resistance to oxidative degradation of polyethylene grades determined with test specimens of compression moulded sheets are directly comparable with drop tests at -18 °C of design types produced of these grades after pre-storage with 55 % nitric acid for 21 days at 40 °C. The impact of the pre-storage time of jerricans with 55 % nitric acid at 40 °C and 23 °C on the marginal drop heights in drop tests at -18 °C, on the MFR and on the tensile properties tensile strength, breaking elongation and the elastic modulus were investigated. Packaging design types (jerricans) made of three polyethylene grades from different producers were pre-stored with 55 % nitric acid for 21,42 and 84 days at 40 °C as well as for six months at 23 °C. The MFR and tensile properties of test specimens taken from the design type side walls as well as the marginal drop heights of the jerricans in drop tests at -18 °C were determined.
The values of the notched impact strength at -30 °C of polyethylene grades are not comparable with the marginal drop heights determined in drop tests at -18 °C. The oxidative damaging impact of nitric acid has a greater effect on the grade with lower resistance to oxidative degradation by reducing more significantly the marginal drop heights with increasing pre-storage time.
Pre-damage with 55 % nitric acid for 21 days at 40 °C, as recommended in ISO 16101 and EN 15507 caused an increase in the marginal drop heights of most design types in drop tests when compared with design types without pre-damage. The test results demonstrated clearly that pre-storage of the jerricans for six months at 23 °C caused a higher increase in the MFR and lower marginal drop heights of the jerricans in drop tests at -18 °C compared with pre-storage of the jerricans for 21 days at40 °C.
The mechanical properties change as a result of diffusion of nitric acid into the polyethylene grades and the reaction of the nitric acid with the polymers. The percentage decrease and increase in the tensile strength, breaking elongation and elasticity modulus of test specimens taken from the design type side walls after different pre-storage times were only partly comparable with the marginal drop heights in drop tests at -18 °C.
The material parameters melt flow rate (MFR), density (D), notched impact strength (NIS) at –30°C, stress crack resistance [determined with the Full Notch Creep Test (FNCT)] and resistance to oxidative degradation (Ox) have been selected for a comparison of polyethylene grades in the European standard EN 15507. These parameters have a relationship with design type tests of packagings for the transport of dangerous goods.
This paper presents the results of additional investigations to determine the impact of the pre-storage time of jerricans with 55% nitric acid at 40°C and 23°C on the marginal drop heights in drop tests at –18°C, on the MFR and on the tensile properties. Jerricans made of different polyethylene grades were pre-stored with 55% nitric acid for 21, 42 and 84 days at 40°C and for six months at 23°C.
The tests showed that the NIS values at –30°C of polyethylene grades were not comparable with marginal drop heights determined in drop tests at –18°C.
Pre-damage with 55% nitric acid for 21 days at 40°C led to an increase in the marginal drop heights of the jerricans. Altering the test regulations by increasing pre-storage time with 55% nitric acid to 42 days would be an alternative.
The test results demonstrated clearly that pre-storage of the jerricans for six months at 23°C caused a higher increase in the MFR and lower marginal drop heights for the jerricans when compared with pre-stored jerricans for 21 days at 40°C.
The chemical industry has expressed great interest in using polyethylene terephthalate (PET) as material for packagings for the transport of dangerous goods. Due to the high strength and stiffness of PET, the wall thickness and weight of packagings can be reduced. This is a relevant cost factor. PET is a semi-crystalline thermoplast which is produced by polycondensation of terephthalic acid and ethylene glycol.
According to the European dangerous goods regulations RID and ADR, samples of PET design types of packagings for dangerous goods must be pre-stored with the original filling good for six months at 23°C, before the design type tests can be carried out. For packagings made of polyethylene (PE) tests to prove the stress cracking resistance by using laboratory methods are possible to reduce time and costs. Therefore, standard liquids, simulating the different types of damaging effects on PE are defined in RID and ADR. However, there is no information and research available about the damaging mechanisms on PET in comparison to PE, especially regarding to stress cracking resistance and test methods.
The aim of this work is to compare the stress cracking resistance of PE and PET with the Full Notch Creep Test (FNCT), which was developed by chemical industry and is described in the standards EN ISO 16101 and EN 15507. It was investigated whether testing specimens made of PE and PET with a full coplanar notch around the middle of the specimens show weakening after the impact of a tensile force in a wetting solution (Lutensol® FSA 10) at 50°C in a test device on the basis of the FNCT.
The test results confirmed the suitability of the method for eight PE grades. Unfortunately, this method couldn’t be used for PET because the specimens broke during notching. In addition the molding of the sheets and the following temper process for twelve hours are very time-consuming, and the specimens broke during notching due to the high brittleness of PET.
Another possibility to provide evidence of stress cracking resistance of PE packagings is laid down in BAM’s Dangerous Goods Rule BAM-GGR 015. This test was carried out with PE and PET bottles to compare both materials. Therefore 1l test bottles were filled with a 5% wetting solution and mounted with a clamping tool for 28 days at 40°C. Tensile test specimens were cut out afterwards from the middle of the bottles in the deformed areas. Tensile strength and breaking elongation of PE specimens were determined in comparison to the PET specimens. The tensile properties of the PET specimens couldn’t be determined due to the strength and the stiffness of the material.
In conclusion the only way to provide information about the stress cracking resistance of PET was to perform stacking tests. 1l bottles made of PE and PET were filled with a 5% wetting solution and stored with a stacking load for 28 days at 40°C according to EN ISO 16495. Design types of PE and PET both passed the stacking tests.
Comparison of the corrosion resistance to dangerous goods of austenitic CrNiMo and duplex steels
(2014)
The “BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” is the basis in Germany for substance-related prototype approvals for tank Containers in Germany. Compatibility evaluations of selected metallic materials and polymeric materials under the influence of approximately 7200 dangerous goods have been published in the BAM-List since 1989. The austenitic CrNi- and CrNiMo-steels - UNS S30403, UNS S31600, UNSS31603 and UNS S31635 - are the materials mostly used worldwide for transport tanks. The duplex Steel UNS S31803 has been put on the BAMList due to the great interest of tank producers and transport Companies. Using UNS S31803 instead of 316L, the weight of the tanks can be reduced, and the list of transportable goods can be extended. The objective of these investigations was to compare the corrosion resistance of duplex Steel UNS S31803 and austenitic Steel UNS S31603. Therefore, test specimens of both steels were exposed to selected corrosive substances, such as formic acid, acetic acid, phosphoric acid, sulfuric acid, nitrating acid, monochloroacetic acid and trichloroacetone at 55 °C (30 °C, 70 °C). The test results have shown that the duplex Steel UNSS31803 is a good alternative to austenitic CrNiMo-steel UNS S31603 for tanks carrying corrosive dangerous goods.
Comparison of the Corrosion Resistance to Dangerous Goods of Austenitic CrNiMo and Duplex Steels
(2014)
For the characterization and the comparison of polyethylene grades used for the manufacture of packaging and intermediate bulk container, the following parameters are required: melt flow rate (MFR), density (D), low-temperature notched impact strength, full notch creep test (FNCT) and increase of MFR by molecular degradation (resistance to oxidative degradation). The relationship between these material parameters determined on the basis of specimens prepared from compression-moulded sheets of polyethylene grades and the test behaviour of packaging has been investigated in several tests. The environmental stress crack resistance determined by FNCT represents the impacts from the stacking tests performed with standard liquid wetting solution (without pre-storage) and with normal butyl-acetate-saturated wetting solution (pre-storage with normal butyl acetate). Resistance to molecular degradation by the determination of MFR increase is related to the impacts in drop tests and stacking tests performed after pre-storage for 21 days with standard liquid 55% nitric acid at 40°C. The low-temperature impact strength is directly comparable with the impacts in drop tests at -18°C performed without pre-storage and after pre-storage with 55% nitric acid. A partly good relationship was found between the test results and the material parameters. Conditioning the design types with 55% nitric acid for 21 days causes an increase in the marginal drop heights of the design types in drop tests at -18°C when compared with design types without pre-storage. Post-cross-linking of the grades increases stiffness because of the acidic influence.
Materials compatibility is a major concern whenever the fuel composition is changed in a fuel system. Therefore frequently used sealing materials such as FKM (fluorocarbon rubber), FVMQ (methyl-fluoro-silicone rubber), VMQ (methyl-vinyl-silicone rubber), EPDM (ethylene-propylene-diene rubber), CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), IIR (butyl rubber), PA (polyamides), N8R (acrylonitrile-butadiene rubber) and PUR (polyester urethane rubber) were exposed to E1 0, diese I fuel with 5% biodiesel, non-aged and 2 year aged 810 (heating oil with 10% biodiesel), and for comparison to pure diese! fuel, standard heating oil and Super plus without bioethanol at 20 °C, 40 oc and 70 oc for 84 days. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens to the biofuels for 42 days.
There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore a threshold of 15% was determined for the evaluation of the compatibility.
The sealing materials FKM, EPDM, N8R, FMVQ, CSM and PA were evaluated on the basis of this threshold as resistant in E1 0 at 20 oc and 40 °C. FKM, FVMQ and PA were resistant at 40 oc , and none of the materials were resistant at 70 °C. FKM and FVMQ absorbed much less 810 and swelled less. CR, CSM, EPDM, IIR, N8R and VMQ were not resistant to 810 at all at 20 oc, 40 oc and 70 oc as the decrease in the tensile properties was significantly over 50%. FVMQ and PA could be evaluated as resistant in non-aged and two year aged 810 at 20 oc and 40 oc, whereas FKM was resistant up to 70 °C. FKM, PA and PUR were evaluated as resistant in standard heating oil and pure diese! fuel at temperatures up to 40°C, only FKM was resistant up to 70°C. FVMQ, FKM, N8R, VMQ, CR and IIR can be evaluated as resistant in premium grade fuel Super plus without ethanol at 20 oc. FKM, FVMQ, VMQ and IIR were still resistant at 40 °C. FKM and FVMQ were evaluated as resistant with restrictions at 70 °C.
ln summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one.