Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (22)
- Zeitschriftenartikel (16)
- Beitrag zu einem Sammelband (16)
- Vortrag (12)
- Buchkapitel (2)
- Posterpräsentation (2)
Sprache
- Englisch (70) (entfernen)
Schlagworte
- Acoustic emission (8)
- Concrete (8)
- Polypropylene fibres (6)
- Alkali-silica reaction (4)
- Explosive spalling (4)
- Fire (4)
- High performance concrete (4)
- Radar (4)
- Alkali-silica-reaction (3)
- Concrete pavements (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (12)
The long-term exposure of marble objects leads to a successive deterioration of the rock fabric and may cause severe damage on cultural heritage objects. The magnitude of disintegration depends on the rock fabric as well as on the climatic conditions. Some types of marble show no considerable damage even if they have been exposed in northern Europe for several decades or centuries. In contrast, other marble varieties are showing severe damage after a few years of weathering. The present study shows that marble decay, along with the initial thermal degradation, is mainly influenced by the hygric and thermo-hygric load, respectively.
The influence of the rock fabric on the resistivity against weathering is also documented. The factors causing marble decay were compared to extensive climate data, which were collected during a scientific project that was started with the aim to develop a covering system for marble sculptures in Berlin. Based on the hygrothermal material properties of the marble and on the climatic conditions, the heat and moisture Transport inside the material and hence the hygrothermal load changes were calculated with a high spatial resolution. The calculations showed that the temperature and moisture fluctuations inside the material are mainly controlled by the dimensions and orientation of the sculptural elements.
The current state of preservation was investigated by two-dimensional ultrasonic tomography. The results show a good correlation to the calculated distribution of the hygrothermal load. Based on this finding, requirements on a protective winter shelter system for the sculptures were defined.
The project results show that in addition to protective covers, regular inspection and maintenance combined with regular cleaning ensures an effective and sustainable protection of marble objects in northern Europe.
Water migration in one-side heated concrete: 4D in-situ CT monitoring of the moisture-clog-effect
(2019)
Explosive spalling due to fire exposure in concrete structures can lead severe damage and, in the worst case, to premature component failure. For this reason, an in situ investigation of water Migration in concrete due to surface heating was undertaken.
During these experiments, a miniaturized concrete specimen within a confining and insulating double-hull was subjected to surface heating during simultaneous X-ray computed tomography (CT) scanning. Through the use of subtraction-based Image analysis techniques, it was possible to observe and quantify not only drying within areas of the concrete matrix close to the heated surface, but also the migration of moisture to both pore and matrix regions deeper within the specimen. It was also discovered that the correction of CT images for specimen deformation using DVC and variable detector performance using calibrated image filters significantly improved the quality of the results. This clearly demonstrates the potential of X-ray CT for evaluation of other rapid-density-change phenomena in concrete and other building materials.
This paper presents the results of an
experimental study on the transient strain of high
strength concrete (HSC) under heating up to 750 °C
and the impact of polypropylene (PP) fibers. Concerning
this topic only few results are available in the
literature and systematic investigations are missing.
However, basic knowledge is necessary for the
understanding of the internal damage processes in
the material as well as for heated structures. The
transient strain during heating can be separated in two
basic components: the free thermal strain and the
mechanical strain. They were experimentally determined
exemplarily for one HSC. For the determination
of the mechanisms of transient strain and particularly
the influence of PP fibers different techniques were
applied. In this context the monitoring of the microcracking
was done for the first time with acoustic
emission analysis in combination with ultrasonic
measurements. This new approach helps fundamentally
to explain the impact of PP fibers on free thermal
strain and mechanical strain during heating up.
Furthermore weight loss measurements were carried
out to characterize the moisture transport. It was
shown that the PP fibers cause an acceleration of the
moisture transport in the temperature range from 200
to 250 °C which leads to drying shrinkage in opposite
direction to the free thermal strain. Hence this paper is
a contribution to the general understanding of the
impact of PP fibers in HSC at high temperatures and
emphasizes the important influence of PP fibers on the
thermal and mechanical induced strain of HSC.
Thermally-induced moisture transport in high-performance concrete studied by X-ray-CT and 1H-NMR
(2019)
The thermohydraulic damage mechanism is one of the primary causes for explosive spalling of highperformance concrete. This paper presents the spatially- and temporally-resolved analysis of the thermally-induced moisture transport and reconfiguration processes by means of X-ray-CT and 1HNMR.
Thermal testing results for a high-performance concrete, which is sensitive to explosive spalling and which was prepared with and without added polypropylene fibres, are presented in this paper. These results indicate that the addition of fibres leads to a faster and deeper migration of the drying front and, thus, to a lower likelihood of vapour-pressure induced explosive spalling.
It has been shown in fire tests that polypropylene fibres reduce or avoid explosive spalling of high performance concrete. In the critical temperature ränge up to 300 °C the permeability of HPC increases by using polypropylene fibre. Due to this the water vapour, which is the main reason for explosive spalling, can escape. There exist different theories in the literature conceming the micro structural mechanisms, which cause an increase in the permeability. Within the framework of an internal research project at BAM an innovative methodology was developed for experimental verifying of existing theories and to get new insights into this problem The methodology used is unique and has been undertaken here for the first time. This consists of the combination of acoustic emission and ultrasonic measurement during temperature loading and the non-destructive micro structural analysis of cooled down samples with the aid of micro X-ray computed tomography. For the validation of the nondestructive test methods scanning electron microscopic images of prepared samples were undertaken. The results show that due to the thermal decomposition of the polypropylene fibres micro canals emerge. These are connected due to a simultaneous micro cack formation.
High-strength concrete (HSC) will experience thermal microcracking, explosive spalling, and undesirable chemical changes when exposed to high temperatures, such as during fire, engulfment by lava flow, or nuclear meltdown. Knowledge of the resultant changes in mechanical, physical, and chemical properties is paramount for hazard mitigation. We present a multidisciplinary study on the influence of thermal-stressing on HSC. Our study shows that thermal microcracking in HSC initiates at 180 °C, is more prevalent during cooling, and exhibits the Kaiser 'temperature-memory' effect. We show that residual compressive strength, indirect tensile strength, ultrasonic wave velocities, and Youngs modulus and Poissons ratio decrease, whilst porosity and permeability increase with increasing temperature. We discuss these data in terms of the chemical changes during thermal-stressing, provided by thermo-gravimetric analysis, differential scanning calorimetry, and X-ray diffraction, and from optical microscopic analysis of thermally-stressed samples. We provide implications for thermally-damaged HSC structures and a new method for non-destructive monitoring.
The durability of concrete structures due to alkali-silica-reaction (ASR) is usually been assessed by ASR concrete prism tests (CPT). Therefore, the expansion of concrete specimens indicates an alkalisensitivity.
In Germany these tests are performed at 40°C or accelerated 60°C. Nevertheless, ASR prism tests are expensive, power and time-consuming. For these reasons, an alternative chemical test (“mod. BTU-test”) was developed in the past. The “mod. BTU-test” was correlated with German standard CPT.
In this test, the solubility of silica and alumina in the liquid phase is measured by ICP-OES.
For special requirements in concrete road construction, stricter test procedures are necessary. The specimens are repeatedly subjected to cyclic alternating storage in NaCl. On the one hand, the presence of NaCl increases the ASR expansion, on the other hand NaCl also changes the dissolution behaviour of silica and alumina.
For now is not possible to correlate the solubilities of “mod. BTU-test” and ASR expansions influenced by NaCl. Therefore, four aggregates with different ASR sensitivities were chosen and ASR concrete prism tests (in addition with NaCl) have been performed. According to the “mod. BTU-test” the solubilities of silica and alumina in presence of different NaCl concentrations were measured.
This paper is about the regression analysis of silica and alumina dissolution and ASR expansion tests in presence of NaCl. The regression analysis shows the influence of a quasi-continuous and an interrupted cyclic alternating storage. Additionally the effects of temperature and NaCl concentration are investigated. In the end, a suitable NaCl concentration of the “mod. BTU-test” for dissolution experiments is recommended. The “mod. BTU-Test” with NaCl might be a serious and reliable test method for ASR classification for concrete road construction.