The long-term exposure of marble objects leads to a successive deterioration of the rock fabric and may cause severe damage on cultural heritage objects. The magnitude of disintegration depends on the rock fabric as well as on the climatic conditions. Some types of marble show no considerable damage even if they have been exposed in northern Europe for several decades or centuries. In contrast, other marble varieties are showing severe damage after a few years of weathering. The present study shows that marble decay, along with the initial thermal degradation, is mainly influenced by the hygric and thermo-hygric load, respectively.
The influence of the rock fabric on the resistivity against weathering is also documented. The factors causing marble decay were compared to extensive climate data, which were collected during a scientific project that was started with the aim to develop a covering system for marble sculptures in Berlin. Based on the hygrothermal material properties of the marble and on the climatic conditions, the heat and moisture Transport inside the material and hence the hygrothermal load changes were calculated with a high spatial resolution. The calculations showed that the temperature and moisture fluctuations inside the material are mainly controlled by the dimensions and orientation of the sculptural elements.
The current state of preservation was investigated by two-dimensional ultrasonic tomography. The results show a good correlation to the calculated distribution of the hygrothermal load. Based on this finding, requirements on a protective winter shelter system for the sculptures were defined.
The project results show that in addition to protective covers, regular inspection and maintenance combined with regular cleaning ensures an effective and sustainable protection of marble objects in northern Europe.
Einfluss einer druckschwellinduzierten Degradation von Fahrbahndeckenbeton auf die schädigende AKR
(2020)
In den letzten Jahren sind im deutschen Bundesautobahnnetz verstärkt Schäden an vor 2005 errichteten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Neben dem AKR-fördernden Einfluss von alkalihaltigen Taumitteln werden Fahrbahndecken zyklischen mechanischen Belastungen infolge des Verkehrs und Zwangsspannungen durch klimatische Einwirkungen ausgesetzt. Solche mechanischen Belastungen werden bisher in keinem AKR-Prüfverfahren berücksichtigt. Die zyklischen Belastungen können zu einer Degradation des Betongefüges führen, die ggf. einen AKR-fördernden Einfluss hat. Dieser Beitrag stellt Untersuchungen vor, die zur Beantwortung der Frage nach dem Einfluss einer zyklischen mechanischen Belastung auf den AKR-Schadensprozess beitragen. Dabei wird der Hypothese nachgegangen, dass die ermüdungsinduzierte Degradation zu einer Erhöhung des Stofftransports führt.
Dieser hat einen Einfluss auf die AKR-Schadensentwicklung, da die Reaktionspartner zunächst zum Reaktionsort transportiert werden müssen. Daher wird angenommen, dass sich mit dem Stofftransport auch die AKR-Schädigung verstärkt. Es werden Betonproben aus typischen Fahrbahndeckenbetonen einer vorgeschalteten zyklischen Druckschwellbelastung ausgesetzt.
Die Degradation infolge der Vorbelastung wird simultan mittels ZfP-Verfahren charakterisiert. Anschließend werden die Auswirkungen der zyklischen Vorschädigung auf den Stofftransport sowie auf die AKR vergleichend an Prüfkörpern ohne und mit Vorschädigung untersucht. Die Ergebnisse lassen den Schluss zu, dass die zyklische Vorschädigung sowohl den Stofftransport als auch die AKR fördert.
In this work, which is part of a larger research program, a framework called “virtual data fusion“ was developed to provide an automated and consistent crack detection method that allows for the cross-comparison of results from large quantities of X-ray Computed Tomography (CT) data. A partial implementation of this method in a custom program was developed for use in research focused on crack quantification in Alkali-Silica Reaction (ASR)-sensitive concrete aggregates. During the CT image processing, a series of image analyses tailored for detecting specific, individual crack-like characteristics were completed. The results of these analyses were then “fused” in order to identify crack-like objects within the images with much higher accuracy than that yielded by any individual image analysis procedure. The results of this strategy demonstrated the success of the program in effectively identifying crack-like structures and quantifying characteristics, such as surface area and volume. The results demonstrated that the source of aggregate has a very significant impact on the amount of internal cracking, even when the mineralogical characteristics remain very similar. River gravels, for instance, were found to contain significantly higher levels of internal cracking than quarried stone aggregates of the same mineralogical type.
Die Kenntnis von Materialeigenschaften spielt bei der Entwicklung oder Optimierung von Betonen und Bauweisen für den Straßenbau sowie der Qualitätssicherung eine bedeutende Rolle. Gleichermaßen bilden physikalische Materialkennwerte die Grundlage für die rechnerische Dimensionierung und die Restsubstanzbewertung von Betonfahrbahndecken. Eine relevante Kenngröße bei der Untersuchung thermisch induzierter Spannungs- und Verformungszustände stellt der thermische Ausdehnungskoeffizient dar. Im Zuge der systematischen Weiterentwicklung der rechnerischen Dimensionierung, aber auch im Zusammenhang mit der gezielten Verbesserung der Gebrauchseigenschaften von Betonfahrbahndecken gilt es zu hinterfragen, ob lastunabhängige Formänderungseigenschaften der verwendeten Betone aktuell ausreichend Beachtung finden, ob allgemeine Literaturwerte für die heutigen Fahrbandeckenbetone stets Gültigkeit besitzen und ob deren Implementierung in numerische Modelle zu realitätsnahen Vorhersagen führt. Für eine empirische Herangehensweise ist die Verfügbarkeit adäquater Prüfverfahren von entscheidender Bedeutung. In Deutschland existiert aktuell jedoch kein standardisiertes oder genormtes Verfahren für die prüftechnische Bestimmung des thermischen Ausdehnungskoeffizienten von Beton. Daher wurden unter Beachtung straßenbauspezifischer Gesichtspunkte zwei Prüfansätze entwickelt, die in diesem Beitrag vorgestellt sowie hinsichtlich möglicher Messunsicherheiten und Messungenauigkeiten diskutiert werden. Außerdem werden ausgewählte Ergebnisse aus Analysen an Bestandsbetonen aus dem BAB-Netz dargestellt. Im Ergebnis sollen die Untersuchungen einen Beitrag zur Schaffung der prüftechnischen Voraussetzungen für eine abgesicherte Quantifzierung der thermischen Dehnung von Fahrbahndeckenbetonen leisten.
Die Oberflächentexturierung der Betonfahrbahndecken mittels Grinding- und Grooving steht seit einigen Jahren im Mittelpunkt der Forschung und Entwicklung des Betonstraßenbaus in Deutschland. In den vergangenen Jahren wurden die vorteilhaften Oberflächenperformances derartiger Texturen wie z.B. Griffigkeit, Ebenheit, Lärmminderung in zahlreichen Forschungsprojekten umfassend untersucht und daraus die Technologie „Texturgrinding“ entwickelt.
Im Kontext des gegenwärtig verfolgten ganzheitlichen performanceorientierten Ansatzes liegt der Fokus nun verstärkt auf der Analyse und Charakterisierung der Oberflächentopografie von Grinding- bzw. Groovingtexturen. Insbesondere gilt ein Hauptaugenmerk hierbei der zeitlichen Entwicklung der Oberflächentexturen in Abhängigkeit von äußeren Einwirkungen durch Klima und Verkehr.
Dieser Beitrag zeigt, dass durch den Einsatz eines auf Streifenlichtprojektion basierenden Messsystems, eine hochaufgelöste dreidimensionale Erfassung der Oberflächentopografie verschiedenartiger Grinding- und Groovingtexturen möglich ist. Darauf aufbauend wurden messtechnische Voraussetzungen zur Gewährleistung reproduzierbarer Messungen geschaffen, die eine Dokumentation der zeitlichen Texturveränderungen infolge klimatischer Beanspruchung ermöglichen. Anschließend wurden Auswerteroutinen zur quantitativen und statistischen Charakterisierung der Oberflächentextur entwickelt und angewandt, um exemplarisch die Veränderungen der Oberflächentopografie infolge klimatischer Beanspruchung quantitativ abzubilden.