In Germany, about 60 million tons of demolition waste are generated annually. Approximately 70% of the demolition waste is currently recycled. Most recycling applications, for example in roadbed substructures, can be seen as a kind of downcycling. However, there are also some high-level applications for demolition waste. For instance, crushed and sieved concrete demolition waste can be used as concrete aggregate instead of natural materials. Depending on the crushing process, about a third of the broken concrete is currently concrete sand. At present, concrete sand fraction (0-4 mm) is rarely reused as a concrete aggregate. This is due to the fact that some important characteristics of crushed concrete sand are different from those of natural sand. As a result, it does not reach the standards required for aggregates. Concrete containing such aggregate is of lower quality than concrete made of natural aggregate. This paper describes an experimental investigation on the treatment of concrete sand gained from demolition waste by wet processing using a jig whereby the sand is separated by grain size and, more importantly, by density. Concrete produced with concrete sand which has been treated in this manner should have the same quality as concrete prepared with natural aggregate. Recycled sand used as aggregate substitutes natural resources and avoids disposal of waste. It has all the characteristics of an Ecomaterial. (author abst.)
Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence.
A sustainable recycling of photovoltaic (PV) thin film modules gains in importance due to the considerable growing of the PV market and the increasing scarcity of the resources for semiconductor materials. The paper presents the development of two strategies for thin film PV recycling based on (wet) mechanical processing for broken modules, and combined thermal and mechanical methods for end-of-life modules. The feasibility of the processing steps was demonstrated in laboratory scale as well as in semi-technical scale using the example of CdTe and CIS modules. Pre-concentrated valuables In and Te from wet mechanical processing can be purified to the appropriate grade for the production of new modules.
An advantage of the wet mechanical processing in comparison to the conventional procedure might be the usage of no or a small amount of chemicals during the several steps.
Some measures are necessary in order to increase the efficiency of the wet mechanical processing regarding the improvement of the valuable yield and the related enrichment of the semiconductor material.
The investigation of the environmental impacts of both recycling strategies indicates that the strategy, which includes wet mechanical separation, has clear advantages in comparison to the thermal treatment or disposal on landfills.
Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.