Filtern
Erscheinungsjahr
Dokumenttyp
Schlagworte
- Coupling methods (2)
- Plasma modification (2)
- Adhesion promoting interlayers (1)
- Adhesion promotion (1)
- Attenuated total reflectance-Fourier transorm infrared spectroscopy (1)
- Carbon fiberepoxy resin laminates (1)
- Chemical conversion of functional groups (1)
- Chemical reduction of functional groups (1)
- Copolymers (1)
- Electrospray ionization (ESI) (1)
Thin coatings of poly(acrylic acid) (PAA) and poly(hydroxyethylmethacrylate) (PHEMA) were deposited onto carbon fibers by means of the electrospray ionization (ESI) technique in ambient air. These high-molecular weight polymer layers were used as adhesion promoters in carbon fiberepoxy resin composites. Within the ESI process, the carbon fibers were completely enwrapped with polymer in the upper 10 plies of a carbon fiber roving. As identified with scanning electron microscopy also shadowed fibers in a bundle as well as backsides of fiber rovings were pinhole-free coated with polymers (electrophoretic effect'). Under the conditions used, the layers have a granular structure. Residual solvent was absent in the deposit. PAA and PHEMA films did not show any changes in composition and structure in comparison with the original polymers as analyzed by X-ray photo-electron spectroscopy and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Single-fiber pullout tests of coated fibers embedded in epoxy resin showed significantly increased interfacial shear strength. It is assumed that chemical bonds between carbon fiber poly(acrylic acid) and epoxy resin contribute significantly to the improved interactions.
Polybutadienes (PB) and polyisoprenes (PI) with various molecular weights and polydispersities were epoxidized applying two different synthetic routes. The degree of epoxidation was determined by means of matrix-assisted laser desorption/ionization-time of flight mass spectrometry (MALDI-TOF MS). It has been found that the degree of functionalization of polybutadiene is generally lower than that for polyisoprenes. Additionally, PB shows lower degrees of epoxidation at higher masses, whereas the level of functionalization of PI was unaffected by the molar mass. Coupling of gel permeation chromatography (GPC) with MALDI-TOF mass spectrometry was successfully used for the investigation of epoxidized polymers with higher masses. Using mass spectra of single fractions, the degree of epoxidation could be determined and applied for a calibration of GPC.
Chemical heterogeneities and molecular weight distributions of poly(ethylene oxide) (PEO)-co-polymethylene (PM) model oligomers, which are relevant to the synthesis of commonly used tensides, were investigated. For analytical characterization, the well-known principle of liquid adsorption chromatography at 'critical conditions' (LACCC) was modified. Near the critical conditions of adsorption of the PEO unit, e.g., at slight adsorption conditions of PM, the copolymers could be separated according to their PM chain length. The eluates were separated and single fractions of each peak were continuously transferred onto the MALDI target by means of a commercially available device. Simultaneously, the MALDI matrix solution was continuously added with a second pump. This procedure offers the possibility of the formation of homogeneous matrix-polymer textures. By MALDI-MS a complete characterization of the chemical composition (PEO and PM chain length) of each peak could be achieved. The obtained MALDI mass spectra of the eluates at different retention times could be used for the molecular weight calibration of the LAC system. In this way, an additional application of SEC, as in conventional 2D-chromatography, was avoided by using the MALDI method as quasi chromatographic separation