Five new catalysts are prepared from dibutyltin oxide and catechol (HCa),
2,3-dihydroxynaphthalene (NaCa), 4-tert-butyl catechol (BuCa), 4-cyano
catechol (CyCa), and 4-benzoyl catechol (BzCa), but only BuCa gives useful
results. When benzyl alcohol is used as an initiator, linear chains having
benzyl ester end groups are formed in a slow polymerization process. In
contrast to cyclic or noncyclic dibutyltin bisalkoxides, neat BuCa yields
cyclic poly(l-lactide)s via a fast ring-expansion polymerization. Under certain
conditions, a high-melting crystalline phase (Tm = 191 °C) is obtained.
At 160 °C and short reaction times even-numbered cycles are slightly
prevailing, but, surprisingly, at 120 °C, odd-numbered cycles are predominantly
formed. These results definitely prove that a ring-expansion mechanism
is operating.
A comparison of tributyltin chloride, dibutyltin dichloride,and butyltin trichloride as catalysts of ring-opening polymerizations(ROPs) of l-lactides at 160°C in bulk reveals increasing reactivity in the above order, but only the least reactive catalysts, Bu3SnCl, yield a uniform reaction product, namely cyclic poly(L-lactide)s with weight average molecular weights (Mw ́s) in the range of 40,000–80,000. A comparison of dimethyltin , dibutyltin , and diphenyltin dichlorides resulted in the following order of reactivity: Me2SnCl2<Bu2SnCl2<<Ph2SnCl2. In this series also, the most reactive catalyst yields cyclic polylactides, but the extent of cyclization varies with the molecular weight. The formation of cyclic polylactides is explained by ROP combined with simultaneous polycondensation involving end-to-end cyclization (ROPPOC method). ROP of meso-lactide at 80 or 60°C yields even-numbered linear chains as main products, a result supporting the ROPPOC mechanism.
For the development of selective and sensitive chemical sensors, we have developed a new family of poly(etherphosphoramide) polymers. These polymers were obtained with satisfactory yields by nucleophilic aromatic polycondensation using isosorbide as green resources, and bisphenol A with two novel difluoro phosphinothioic amide monomers. Unprecedented, the thiophosphorylated aminoheterocycles monomers, functionalized with two heterocyclic amine, N-methylpiperazine and morpholine were successfully obtained by nucleophilic substitution reaction of P(S)–Cl compound. The resulting polymers were characterized by different analytical techniques (NMR, MALDI–ToF MS, GPC, DSC, and ATG). The resulting partially green polymers, having tertiary phosphine sulfide with P–N side chain functionalities along the main chain of polymers are the sensitive film at the surface of a gold electrode for the impedimetric detection of Cd, Ni, Pb and Hg. The bio-based poly(etherphosphoramide) functionalized with N-methylpiperazine modified sensor showed better analytical performance
than petrochemical based polymers for the detection of Ni2+. A detection limit of 50 pM was obtained which is very low compared to the previously published electrochemical sensors for nickel detection.
MALDI-ToF mass spectrometry for the characterization of biobased polymers suitable for depollution
(2022)
In this work, bio-based polymers were synthesized and designed as polymers phases for adsorption of a variety of pollutants from aqueous solutions. The obtained adsorption results showed that the integration of bio-sourced synthons generate attractive hydrophilicity, and wettability of the resulting adsorbent phase. Such polymers phases enable stronger interactions with the organic and inorganic pollutants in water.
A wide variety of different bio-based polymers structures (e. g. poly(ethersulfones, poly(etherphosphines or poly(etherpyridines) with different functional groups were successfully designed in order to adapt chemical structure to different pollutants type and matrice nature.
In order to characterize and to determine the correlation between polymer structures and nature of interaction with pollutants, different analytical technics (NMR, GPC, ATG, DSC, Mass spectrometry) were successfully used. Amongst them, MALDI TOF mass spectrometry plays a superior role since this technique enables the simultaneous determination of the polymer structure, polymer end groups and molecular weight.
This work focusses on the characterization of synthesized polymers. The chemical structure of the repeating unit, the nature of the end groups, as well as the molecular weight, which are all important for the specific interactions of the polymer with the pollutants were clearly determined and suggestions to improve these interactions by changing the synthetic pathway could be given.
This article describes the elaboration and characterization of diethylphosphonate-containing polymers coated electrodes as sensors for the detection of heavy metalstraces, by electrochemical impedance spectroscopy. Diethylphosphonate groupswere chosen as heavy metals binding sites. Two different series of polymers bearingthese anchoring groups were synthesized. Whereas the diethylphosphonate groupsare directly incorporated in the aromatic macromolecular chain in some polymers, analiphatic spacer is removing the chelating site from the polymer backbone in others.The influence of the macromolecular structure on the sensing response was studied,especially for the detection of Pb2+,Ni2+,Cd2+and Hg2+. Polymer P6, including thehigher amount of diethylphosphonate groups removed from the polymer chain by ashort alkyl spacer gave the higher sensitivity of detection of lead ions, with a detec-tion limit of 50 pM
Cyclic and linear poly(L-lactide)s by ring-expansion polymerization with Bu2SnO, Oct2SnO, and Bu2SnS
(2023)
To elucidate the usefulness of commercial Bu2SnO as catalyst for syntheses of linear and/or cyclic polylactides L-Lactide was polymerized in bulk with variation of the LA/Cat ratio, temperature and time. Based on a ring-expansion polymerization (REP) mechanism cyclic polylactides (PLAs) with weight average molecular weights in the range of 200,000–300,000 are obtained at the highest temperature (180 °C). Polymerizations at 150 °C yielded crystalline, mainly cyclic polylactides which, after annealing, showed high melting temperatures (up to 197.5 °C) and high crystallinities (>80%). Polymerization at 120 °C confirmed the trend towards more linear chains with lower temperatures but yielded extended-ring crystals showing a “saw-tooth pattern” in the mass spectra. Oct2SnO gave similar results as Bu2SnO. Bu2SnS proved a sluggish polymerization catalyst, but a good transesterification catalyst in solid PLA.
Glycolide was polymerized in bulk by means of four different ROPPOC catalysts: tin(II) 2-ethylhexanoate (SnOct2), dibutyltin bis(pentafluoro-phenoxide) (BuSnOPF),zinc biscaproate (ZnCap), and zinc bis(pentafluoro-phenyl sulfide) (ZnSPF). The temperature was varied between 110 and 180°C and the time between 3 h and 7 days. For the few polyglycolides (PGAs) that were soluble extremely high molecular masses were obtained. The MALDI TOF mass spectra had all a low signal-to-noise ration and displayed the peaks of cyclic PGAs with a“saw-tooth pattern ”indicating formation of extended-ring crystallites in the mass range below m/z 2500. The shape of DSC curves varied considerably with catalyst and reaction conditions, whereas the long-distance values measured by SAXS were small and varied little with the polymeriza-tion conditions.
MALDI TOF Massenspektrometrie wurde verwendet, um Kristallisationsprozesse in Polyestern (Polylactide, Polyglycolide) zu untersuchen. Dabei konnte gezeigt werden, dass Zyklen und Linearen simultan, aber in unterschiedlichen Kristalliten, kristallisieren. Die dabei ablaufenden Umesterungen (Transesterifizierungen) konnten mit der MALDI TOF Massenspektrometrie nachgewiesen werden. Damit wurde ein völlig neues Anwendungsgebiet dieser MS Methode demonstriert.
Alcohol-initiated polymerizations of glycolide (GL) catalyzed by tin(II) 2-ethylhexanoate (SnOct2) were carried out in bulk with variation of GA/In ratio, temperature and time. Due to a rather strong competition of cyclization polyglycolide (PGA) free of cycles were never obtained. When the cyclic catalysts 2,2-dibutal-2-stanna − 1,3-dithiolane (DSTL) or 2-stanna 1,3-dioxo-4,5,6,7 bibenzepane (SnBiph) were used in combination with 1,4-butanediol the influence of cyclization was even stronger. Furthermore, the degrees of polymerization were higher than the GA/alcohol ratio due to rapid polycondensation in the solid state. At 160 °C or below, the matrixassisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectra indicated separate crystallization of low molar mass cyclic and linear PGAs from the same reaction mixture (also observed for poly(L-lactide)s).
The Na salt of chloroacetic acid is condensed in suspension. Furthermore,glycolic acid is condensed in bulk or in concentrated solution by means of SnCl2 or 4-toluene sulfonic acid (TSA) as catalysts. The temperatures are varied from 160 to 200°C and the time from 1 to 5 days. Low molar mass cyclic poly(glycolic acid) (PGA) is detected by means of matrix-assisted laser desorption ionization time-of-flight (MALDI TOF) mass spectrometry in most PGAs. A predominance of certain cycles having an even number of repeat units is observed suggesting a thermodynamically favored formation of extended-ring crystals. Extremely high melting temperatures (up to 237.5°C)and high melting enthalpies are found for polycondensations with TSA in 1,2-dichlorobenzene.
Solvent-free sample preparation offers some advantages over solvent-based techniques, such as improved accuracy, reproducibility and sensitivity, for matrix-assisted laser desorption/ionization (MALDI) analysis. However, little or no information is available on the application of solvent-free techniques for the MALDI analysis of polymer blends. Solvent-free sample preparation by ball milling was applied with varying sample-to-matrix ratios for MALDI time-of-flight mass spectrometry analysis of various polymers, including polystyrenes, poly(methyl methacrylate)s and poly(ethylene glycol)s. The peak intensity ratios were compared with those obtained after using the conventional dried droplet sample preparation method. In addition, solvent-assisted milling was also applied to improve sample homogeneities.
Depending on the sample preparation method used, different peak intensity ratios were found, showing varying degrees of suppression of the signal intensities of higher mass polymers. Ball milling for up to 30 min was required to achieve constant intensity ratios indicating homogeneous mixtures. The use of wet-assisted grinding to improve the homogeneity of the blends was found to be disadvantageous as it caused partial degradation and mass-dependent segregation of the polymers in the vials.The results clearly show that solvent-free sample preparation must be carefully considered when applied to synthetic polymer blends, as it may cause additional problems with regard to homogeneity and stability of the blends.