Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (39)
- Beitrag zu einem Tagungsband (16)
- Posterpräsentation (13)
- Zeitschriftenartikel (9)
- Beitrag zu einem Sammelband (9)
- Buchkapitel (2)
Referierte Publikation
- nein (88) (entfernen)
Schlagworte
- MALDI-TOF MS (7)
- MALDI (5)
- Mass spectrometry (4)
- Polylactide (4)
- Ionization (2)
- MALDI TOF MS (2)
- Pollen (2)
- Polymers (2)
- Ring-opening polymerization (2)
- Transesterification (2)
Organisationseinheit der BAM
- 6 Materialchemie (12)
- 6.3 Strukturanalytik (12)
Eingeladener Vortrag
- nein (39)
Hyphenated techniques
(2012)
Polymeroberflächenfunktionalisierungen im gepulsten Plasma mit nachfolgender chemischer Behandlung
(2000)
Characterization of randomly branched polymers utilizing liquid chromatography and mass spectrometry
(2014)
Branching in polymers is an important way to modify the materials properties, however the characterization of random branching in polymeric materials is a challenge in polymer analysis. In this work, liquid adsorption chromatography methods are developed for a commercially available hyperbranched polyester (Boltorn™). This Chromatographie techniques was then coupled to offline MALDI-TOF MS analysis, a first in the analysis of randomly branched polymers. The coupling of these two techniques provides superior MALDI-TOF spectra, enabling the easy identification of structural subdistributons based on theoretical molecular weight. Detailed analysis of the MALDI-TOF spectra shows that these Chromatographie conditions separate cyclic Boltorn polymers (with no core molecule) from non-cyclic polymers (with core molecule), and these are the only two architectures observed. MALDI MS also confirms that the Chromatographie Separation mode is adsorption, but further analysis is needed to determine if there is a Separation by degree of branching.
The catalytic potential of tin(II)acetate, tin(IV)acetate, dibutyltin-bis-acetate and dioctyl tin-bis-acetate was compared based on polymerizations of L-lactide conducted in bulk at 160 or 130°C. With SnAc2 low-Lac/Cat ratios (15/1–50/1) were studied and linear chains having one acetate and one carboxyl end group almost free of cyclics were obtained. Higher monomer/catalyst ratios and lower temperatures favored formation of cycles that reached weight average molecular weights (Mw's) between 100,000 and 2,500,000. SnAc4 yielded mixtures of cycles and linear species under all reaction conditions. Dibutyltin- and dioctyl tin bis-acetate yielded cyclic polylactides under most reaction conditions with Mw's in the range of 20,000–80,000. Ring-opening polymerizations performed with ε-caprolactone showed similar trends, but the formation of COOH-terminated linear chains was significantly more favored compared to analogous experiments with lactide. The reactivity of the acetate catalysts decreased in the following order: SnAc2> SnAc4>Bu2SnAc2~Oct2SnAc2
Twice recrystallized L-lactide was polymerized with a dozen of different tin or bismuth catalysts in bulk at 160°C for 24 h and was annealed at 150°C afterwards. In two cases Tm values above 197.0°C were obtained. The parameters causing a scattering of the DSC data were studied and discussed. The samples prepared with SnCl2, 2,2-dibutyl-2-stanna-1,3-ditholane (DSTL) or cyclic tin(II) bisphenyldioxide (SnBiph) were subject to annealing programs with variation of time and temperatures, revealing that the Tm´s did not increase. However, an increase of Hm was achieved with maximum values in the range of 93-96 J g-1 corresponding to crystallinities off around 90%. Further studies were performed with once recrystallized L-lactide. Again, those samples directly crystallized from the polymerization process showed the highest Tm values. These data were compared with the equilibrium Tm0 and Hm0 data calculated by several research groups for perfect crystallites. A Tm0 of 213+/-2°C and a Hm0 of 106 J g-1 show the best agreement with the experimental data. The consequences of annealing for the thickness growth of crystallites are discussed on the basis of SAXS measurements. Finally, a comparison of cyclic and linear poly L-lactide)s is discussed.