Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (168) (entfernen)
Referierte Publikation
- ja (168) (entfernen)
Schlagworte
- MALDI-TOF MS (55)
- Polylactide (40)
- Cyclization (26)
- MALDI (16)
- Polycondensation (15)
- Ring-opening polymerization (15)
- Polymerization (8)
- MALDI TOF MS (7)
- Crystallization (6)
- Pollen (6)
Organisationseinheit der BAM
- 6 Materialchemie (73)
- 6.3 Strukturanalytik (73)
- 1 Analytische Chemie; Referenzmaterialien (5)
- 1.2 Biophotonik (2)
- 1.7 Organische Spuren- und Lebensmittelanalytik (2)
- 6.6 Physik und chemische Analytik der Polymere (2)
- 7 Bauwerkssicherheit (2)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (2)
- 1.0 Abteilungsleitung und andere (1)
- 1.3 Instrumentelle Analytik (1)
The MALDI-TOF MS analysis of copolymers very often results in complex spectra. A chromatographic separation/fractionation prior to the MALDI investigation can be advantageous since the MALDI mass spectra of fractions very often reveal well-resolved peaks of distinguishable copolymer series. For this purpose, different modes of chromatography have been applied. Chromatographic runs were transferred to MALDI targets utilizing a combined air/electrospray deposition device. Using the new MassChrom2D software, fraction-dependent 2D copolymer compositions plots were obtained providing additional information on the chromatographic mode, and enabling fast modification of conditions to increase separation.
In the present study the incorporation of iron into an organic polymer, composed of formamidine subunits [R–N=C(H)–NH–R], has been examined. The catalytic ability of the recyclable material was investigated in the iron-catalyzed formation of C–C bonds. After optimization of the reaction conditions, excellent yields and chemoselectivities were feasible.
A recently introduced procedure involving a mechanistic switch from reversible addition–fragmentation chain transfer (RAFT) polymerization to ring-opening polymerization (ROP) to form diblock copolymers is applied to synthesize ABA (star) block copolymers. The synthetic steps include the polymerization of styrene with R-group designed RAFT agents, the transformation of the thiocarbonyl thio end groups into OH functionalities, and their subsequent chain extension by ROP. The obtained linear ABA poly(ε-caprolactone)-block-poly(styrene)-block-poly(ε-caprolactone) (pCL-b-pS-b-pCL) (12 500 g mol1 ≤ Mn ≤ 33 000 g mol1) and the star-shaped poly(styrene)-block-poly(ε-caprolactone) (Mn = 36 000 g mol1) copolymers were analyzed by size exclusion chromatography (SEC), nuclear magnetic resonance (NMR), infrared (IR) spectroscopy, and matrix-assisted laser desorption/ionization (MALDI) mass spectrometry. The focus of the current study is on the detailed characterization of the ABA (star) block polymers via multidimensional chromatographic techniques specifically high performance liquid chromatography coupled to size exclusion chromatography (HPLC-SEC). In particular, we demonstrate the first time separation of poly(ε-caprolactone) (pCL) homopolymer and additionally poly(styrene) (pS) from the ABA poly(ε-caprolactone)-b-poly(styrene)-b-poly(ε-caprolactone) and star-shaped poly(styrene)-b-poly(ε-caprolactone) block copolymer utilizing critical conditions (CC) for pCL with concomitant gradient elution liquid chromatography (GELC).
Systems containing multiple photochromic units possibly display a synergistic interplay of individual switching events and hence potentially give rise to unprecedented photoresponsive behavior. Among such systems photoswitchable foldamers are attractive as the photoisomerization events are coupled to the helixcoil conformational transition. To gain comprehensive insight into the role of the number of switching units (statistics) as well as their specific location and relative orientation in the helix backbone, several series of foldamers have been synthesized and characterized. In these series of foldamers, the local environment of the photoswitchable units was precisely tuned as π,π-stacking interactions were enforced to occur between specific pairs, i.e. azobenzene–azobenzene, azobenzene–tolane, or phenylene–phenylene units. These particular arrangements are reflected not only in the stability of the helical conformation, but also affect the photoresponsive behavior, i.e. the rate of photoisomerization and extent of denaturation. Furthermore, determining the intramolecular spin–spin distance in a series of TEMPO-labeled foldamers with variable chain lengths and different spatial locations of the spin-labels deduced an independent verification of the photoinduced helix–coil transition by ESR spectroscopy. Quantitative analysis of the corresponding ESR spectra shows an excellent correlation of the extent of intramolecular spin–spin coupling and the intensity of the Cotton effect in CD spectroscopy. From all of these results an unusual relationship between the rate of photoisomerization and the extent of photoinduced denaturation could be unraveled, as they are not going hand-in-hand but compete with each other, i.e. the easier the individual switching event is, the harder it becomes to achieve a high degree of unfolding. This insight into the effect of microenvironment on the ease of individual switching events and the role of statistics on the resulting degree of the overall conformational transition is of general interest for the design of multi-switch architectures with improved photoresponse.
L-lactide (LA) was polymerized in toluene by means of neat tin(II) 2-ethylhexanoate (SnOct2). Concentration, time and temperature were varied. The isothermally crystallized polyLAs (PLA) were characterized in the virgin state with regard to topology, molar mass, melting temperature (Tm), crystal modification, high or low Tm morphology, crystallinity and crystal thickness. Even a small amount of solvent favored cyclization relative to polymerization in bulk, so that cyclic polylactides were obtained at 115 ◦C and even at 95 ◦C. At all temperatures the α-modification of PLA was obtained along with crystallinities up to 90%. With 6 M solution the high Tm morphology with Tm’s > 190 ◦C was obtained at 115 ◦C. The crystal thickness of crystallites grown from solution at 115 ◦C was on the average 10–20% higher than that of PLA polymerized in bulk. At a polymerization temperature of 75 ◦C cyclization was incomplete and fewer perfect crystallites were formed. A new hypothesis for the crystal growth of cyclic polyLAs is proposed.
For the development of selective and sensitive chemical sensors, we have developed a new family of poly(etherphosphoramide) polymers. These polymers were obtained with satisfactory yields by nucleophilic aromatic polycondensation using isosorbide as green resources, and bisphenol A with two novel difluoro phosphinothioic amide monomers. Unprecedented, the thiophosphorylated aminoheterocycles monomers, functionalized with two heterocyclic amine, N-methylpiperazine and morpholine were successfully obtained by nucleophilic substitution reaction of P(S)–Cl compound. The resulting polymers were characterized by different analytical techniques (NMR, MALDI–ToF MS, GPC, DSC, and ATG). The resulting partially green polymers, having tertiary phosphine sulfide with P–N side chain functionalities along the main chain of polymers are the sensitive film at the surface of a gold electrode for the impedimetric detection of Cd, Ni, Pb and Hg. The bio-based poly(etherphosphoramide) functionalized with N-methylpiperazine modified sensor showed better analytical performance
than petrochemical based polymers for the detection of Ni2+. A detection limit of 50 pM was obtained which is very low compared to the previously published electrochemical sensors for nickel detection.
L-Lactide was polymerized in bulk at 140 °C with three different cyclic tin catalysts and the time was varied from 1 d up to 14 d. The MALDI TOF spectra confirmed the formation of cyclic polylactides (PLAs) and displayed a characteristic change of peak intensity distribution with formation of a “saw tooth pattern”. This pattern confirms a previous hypothesis that cyclic PLAs tend to form crystallites with extended ring conformation and relatively smooth surface. This type of crystallites is formed under thermodynamic control by transesterification on the surface of the crystallites. In this way PLAs with extraordinarily high melting temperatures (Tm's up to 200.6 °C) and extraordinarily high melting enthalpy were obtained (ΔHm's up to 105 J g−1). These ΔHm values require a revision of the maximum ΔHm value calculated in the literature for ideal PLA crystals.
Ring-expansion polymerizations (REPs) catalyzed by two cyclic tin catalysts(2-stanna-1.3-dioxa-4,5,6,7-dibenzazepine [SnBiph] and
2,2-dibutyl-2-stanna-1,3-dithiolane [DSTL) are performed at 140 °C in bulk.
Small amounts (4 vol%) of chlorobenzene or other solvents are added to facilitate transesterification reactions (ring–ring equilibration) in the solid poly(l-lactide)s. In the mass range up to m/z 13 000 crystalline PLAs displaying a so-called saw-tooth pattern in the MALDI-TOF mass spectra are obtained indicating the formation of extended-ring crystals. The characteristics of extended-ring crystallites and folded-ring crystallites are discussed. Furthermore, extremely high melting temperatures (Tm’s up to 201.2 °C) and melting enthalpies (𝚫Hm’s up to 106 J g−1)) are found confirming that 𝚫Hmmax, the 𝚫Hm of a perfect crystal, is around or above 115 J g−1 in contrast to literature data.
This article reviews the usefulness of tin(II) and tin(IV) salts and compounds as catalysts for the polymerization of lactides. The text is subdivided into nine parts mainly reflecting different polymerization strategies, such as ring-opening polymerization (ROP), ring-expansion polymerization (REP), ROP combined with simultaneous polycondensation (ROPPOC), various catalysts with unknown polymerization mechanisms, and polycondensation of lactic acid. Since the toxicity of tin salts and compounds is a matter of concern and frequently mentioned in numerous publications, the first section deals with facts instead of myths about the toxicity of tin salts and compounds.
Formation Mechanism of a Nano-Ring of Bismuth Cations and Mono-Lacunary Keggin-Type Phosphomolybdate
(2022)
A new hetero-bimetallic polyoxometalate (POM) nano-ring was synthesized in a one-pot procedure. The structure consists of tetrameric units containing four bismuth-substituted monolacunary Keggin anions including distorted [BiO8] cubes. The nano-ring is formed via self-assembly from metal precursors in aqueous acidic medium. The compound (NH4)16[(BiPMo11O39)4] ⋅ 22 H2O; (P4Bi4Mo44) was characterized by single-crystal X-ray diffraction, extended X-ray absorption fine structure spectroscopy (EXAFS), Raman spectroscopy, matrix-assisted laser desorption/ionisation-time of flight mass spectrometry (MALDI-TOF), and thermogravimetry/differential scanning calorimetry mass spectrometry (TG-DSC-MS). The formation of the nano-ring in solution was studied by time-resolved in situ small- and wide-angle X-ray scattering (SAXS/WAXS) and in situ EXAFS measurements at the Mo−K and the Bi−L3 edge indicating a two-step process consisting of condensation of Mo-anions and formation of Bi−Mo-units followed by a rapid self-assembly to yield the final tetrameric ring structure.