Filtern
Dokumenttyp
- Zeitschriftenartikel (5)
- Vortrag (2)
- Dissertation (1)
- Posterpräsentation (1)
Schlagworte
- Flame retardancy (3)
- Aryl phosphate (2)
- Flame retardance (2)
- Polycarbonate (PC) blends (2)
- Pyrolysis (2)
- 29Si NMR (1)
- BDP (1)
- Bisphenol A bis(diphenyl)phosphate (BDP) (1)
- Bisphenol-A bis(diphenyl)phosphate (BDP) (1)
- Decomposition (1)
Eingeladener Vortrag
- nein (2)
Novel routes in flame retardancy of bisphenol A polycarbonate/impact modifier/aryl phosphate blends
(2013)
The massive use of electronic engineering products accompanied by high demands on fire safety has led to increasing interest in environmentally friendly flame retardancy of bisphenol A polycarbonate (PC) based materials. In this work, novel routes for enhancing the flame retardancy of PC/Impact Modifier/Aryl phosphate were studied with respect to pyrolysis (TG, TG-FTIR, ATR-FTIR, NMR), flammability (LOI and UL 94) and fire behavior (cone calorimeter at different irradiations). To improve charring of PC/ABSPTFE+Aryl phosphate, the exchange of bisphenol A bis(diphenyl phosphate) (BDP) with novel aryl phosphates was proposed. Two novel flame retardants were synthesized: 3,3,5-trimethylcyclohexylbisphenol-bis(diphenyl phosphate) (TMC-BDP) and bisphenol A- bis(diethylphosphate) (BEP). TMC-BDP was more stable than BDP, thus gave a potential to increase the chemical reactions between the components of the PC/ABSPTFE+Aryl phosphate, whereas more reactive BEP was expected to increase the cross linking activity with the polymer matrix. Nevertheless, the corresponding blends did not enhance the flame retardancy compared to PC/ABSPTFE+BDP. BEP in PC/ABSPTFE preferred to cross-link with itself instead of with PC, thus it showed poor fire protection performance. TMC-BDP gave as good results as BDP in PC/ABSPTFE material. The results delivered evidence that BDP possesses a high degree of optimization in PC/ABSPTFE system. To provide a novel impact modifier improving not only mechanical properties but also the fire retardancy of PC/BDP material, the replacement of highly flammable acrylonitrilebutadiene- styrene (ABS) with silicon acrylate rubber (SiR) with high content of polydimethylsiloxane (PDMS) was studied. In PC/SiRPTFE/BDP the replacement of ABS is beneficial, but PDMS worsened the BDP gas phase and condensed phase action. PDMS reacted also with PC during combustion. PDMS-PC and PDMS-BDP interactions led to silicon dioxide. In fact, the inorganic residue of PC/SiRPTFE/BDP contributed to fire residue and greatly improved the LOI of about 10 % in comparison to PC/ABSPTFE+BDP system. Thus, the use of SiR with high PDMS content is proposed as replacement of ABS in PC/Impact Modifier/BDP blend. To enhance the fire protection, the PC/SiRPTFE/BDP was combined with several adjuvants: (i) layered fillers: talc and organically modified layered silicate (LS), (ii) metal hydroxides: magnesium hydroxide (Mg(OH)2) and boehmite (AlO(OH)), (iii) metal oxides and carbonate: magnesium oxide (MgO) and silicium dioxide (SiO2) and calcium carbonate (CaCO3) as well as (iiii) hydrated metal borates: zinc borate (ZnB), calcium borate (CaB) and magnesium borate (MgB). It was demonstrated that the blend PC/SiRPTFE/BDP+filler is very sensitive to chemical (e.g. hydrolysis) and physical (e.g. viscosity) effects. Additionally,the large deformations of PC/SiRPTFE/BDP materials make difficult to optimize the char. Overall, the ZnB, MgB and CaB are proposed for enhancing the flame retardancy of PC/SiR/BDP with respect to flammability results, reduction of fire hazard and maximum of heat release rate. The results of this work enable the understanding of various mechanisms controlling the fire behavior and thus effective selection of the most appropriate flame retardant, impact modifier and inorganic fillers for producing fire resistant PC based polymers.
The reactivity of the flame retardant and its decomposition temperature control the condensed-phase action in bisphenol A polycarbonate/acrylonitrile–butadiene–styrene/polytetrafluoroethylene (PC/ABSPTFE) blends. Thus, to increase charring in the condensed phase of PC/ABSPTFE + aryl phosphate, two halogen-free flame retardants were synthesized: 3,3,5-trimethylcyclohexylbisphenol bis(diphenyl phosphate) (TMC-BDP) and bisphenol A bis(diethyl phosphate) (BEP). Their performance is compared to bisphenol A bis(diphenyl phosphate) (BDP) in PC/ABSPTFE blend. The comprehensive study was carried out using thermogravimetry (TG); TG coupled with Fourier transform infrared spectrometer (TG-FTIR); the Underwriters Laboratory burning chamber (UL 94); limiting oxygen index (LOI); cone calorimeter at different irradiations; tensile, bending and heat distortion temperature tests; as well as rheological studies and differential scanning calorimeter (DSC). With respect to pyrolysis, TMC-BDP works as well as BDP in the PC/ABSPTFE blend by enhancing the cross-linking of PC, whereas BEP shows worse performance because it prefers cross-linking with itself rather than with PC. As to its fire behavior, PC/ABSPTFE + TMC-BDP presents results very similar to PC/ABSPTFE + BDP; the blend PC/ABSPTFE + BEP shows lower flame inhibition and higher total heat evolved (THE). The UL 94 for the materials with TMC-BDP and BDP improved from HB to V0 for specimens of 3.2 mm thickness compared to PC/ABSPTFE and PC/ABSPTFE + BEP; the LOI increased from around 24% up to around 28%, respectively. BEP works as the strongest plasticizer in PC/ABSPTFE, whereas the blends with TMC-BDP and BDP present the same rheological properties. PC/ABSPTFE + TMC-BDP exhibits the best mechanical properties among all flame-retarded blends.
Various inorganic additives belonging to four different groups: layered materials, metal hydroxides, metal oxides/carbonate and metal borates are investigated in bisphenol A polycarbonate/silicon rubber/bisphenol A bis(diphenyl phosphate) (PC/SiR/BDP) to improve flame retardancy. The pyrolysis, reaction to small flame and fire behaviour of the blends are characterised and structure–property relationships discussed. Among the added layered materials, talc functions as an inert filler with potential for commercialisation, whereas organically modified montmorillonite (LS) enhances decomposition. PC/SiR/BDP + talc and PC/SiR/BDP + LS reinforce the char and induce a flow limit. The different dispersion and location of boehmite (AlO(OH)) nano-particles and Mg(OH)2 micro-particles determine the impact on performance. PC/SiR/BDP + Mg(OH)2 shows additional hydrolysis and thus reduced flame retardancy. AlO(OH) is embedded in SiR and thus behaves as an inert filler. Both additives worked as smoke suppressants. Using selective filling with nano-particles is proposed as an interesting route for flame retardancy in PC/SiR blends. Adding metal oxides and carbonate (MgO, CaCO3 and SiO2) changes the decomposition pathways of PC/SiR/BDP, worsening the fire performance of PC/SiR/BDP. CaCO3 harbours the potential to intumescence, even though an early collapse of the char structure occurred. Adding hydrated metal borates, CaB, MgB and ZnB, changes the pyrolysis and flame retardancy action. Smoke suppression occurs; LOI is improved as well as UL 94 classification. ZnB performs better than MgB and CaB. The comprehensive study, also based on systematic material variation, delivers valuable guidelines for future development of flame-retarded multi-component PC blends.
Are novel aryl phospates competitors for BDP in halogen-free flame retarded PC/ABS/PTFE blend?
(2011)
The pyrolysis and flame retardancy of a bisphenol A polycarbonate/silicon rubber/bisphenol A bis(diphenyl phosphate) (PC/SiR/BDP) blend were investigated and compared to those of PC/BDP and PC/SiR. The impact modifier SiR consists mainly of poly(dimethylsiloxane) (PDMS > 80 wt %). The pyrolysis of PC/SiR/BDP was studied by thermogravimetry (TG), TG–FTIR to analyze the evolved gases, and a Linkam hot stage cell within FTIR as well as 29Si NMR and 31P NMR to analyze the solid residue. The fire performance was determined by PCFC, LOI, UL 94, and a cone calorimeter under different external irradiations. The fire residues were studied by using ATR-FTIR as well as the additional binary systems PC + PDMS, PC + BDP, and BDP + PDMS, focusing on the specific chemical interactions. The decomposition pathways are revealed, focusing on the competing interaction between the components. Fire retardancy in PC/SiR/BDP is caused by both flame inhibition in the gas phase and inorganic-carbonaceous residue formation in the condensed phase. The PC/SiR/BDP does not work as well superimposing the PC/SiR and PC/BDP performances. PDMS reacts with PC and BDP, decreasing BDP's mode of action. Nevertheless, the flammability (LOI > 37%, UL 94 V-0) of PC/SiR/BDP equals the high level of PC/BDP. Indeed, SiR in PC/SiR/BDP is underlined as a promising impact modifier in flame-retarded PC/impact modifier blends as an alternative to highly flammable impact modifiers such as acrylonitrile–butadiene–styrene (ABS), taking into account that the chosen SiR leads to PC blends with a similar mechanical performance.
Structural changes in the condensed phase of bisphenol A polycarbonate (containing 0.45 wt% poly (tetrafluoroethylene))/silicone acrylate rubber/bisphenol A bis(diphenyl-phosphate) (PC/SiR/BDP) and PC/SiR/BDP/zinc borate (PC/SiR/BDP/ZnB) during thermal treatment in nitrogen atmosphere and in fire residues were investigated by solid-state NMR. H-1, B-11, C-13 and P-31 NMR experiments using direct excitation with a single pulse and H-1-P-31 cross-polarization (CP) were carried out including 31P(1 H) and C-13{P-31}double-resonance techniques (REDOR: Rotational Echo Double Resonance) on a series of heat-treated samples (580 K-850 K). Because many amorphous phases occur in the solid residues, and solid-state NMR spectroscopy addresses the most important sites carbon, phosphorus and boron, this paper is the key analytical approach for understanding the pyrolysis and flame retarding phenomenon in the condensed phase of PC/SiR/BDP and PC/SiR/BDP/ZnB.
For the system PC/SiR/BDP it is shown that (i) at temperatures around 750-770 K (main decomposition step) carbonaceous charring of PC occurs and arylphosphate structures are still present, reacted in part with the decomposing PC; (ii) for higher temperatures from 770 K the phosphorus remaining in the solid phase increasingly converts to amorphous phosphonates and inorganic orthophosphates with a minor amount of crystalline orthophosphates; and (iii) H-1-P-31{H-1} CP REDOR and H-1-C-13{P-31} CP REDOR NMR experiments suggest that the phosphates and phosphonates are bound via oxygen to aromatic carbons, indicating the interaction with the carbonaceous char.
When ZnB is added to the system PC/SiR/BDP, (i) ZnB leads to a slightly enhanced PC decomposition for temperatures below 750 K; (ii) alpha-Zn-3(PO4)(2) and borophosphate (BPO4) are formed in small amounts at high temperatures suggesting a reaction between BDP and ZnB during thermal decomposition; and (iii) most of the borate remains in the solid residues, forming an amorphous pure borate network, with the BO3/BO4 ratio increasing with higher temperatures.
The NMR data of thermal and fire residues are highly correlated, underlining the importance of this work for understanding the pyrolysis and flame retardancy mechanisms in the condensed phase during the burning of the PC/SiR blends. (C) 2010 Elsevier Ltd. All rights reserved.
Solid residues of bisphenol A polycarbonate (containing 0.45 wt% poly(tetrafluoroethylene))/silicone acrylate rubber/bisphenol A bis(diphenyl-phosphate) (PC/SiR/BDP) and PC/SiR/BDP/zinc borate (PC/SiR/BDP/ZnB) after thermal treatment were investigated by solid-state and liquid-state NMR, focusing on the role and interaction of SiR with the other components of the polymer blend.
In PC/SiR/BDP, part of the SiR reacts to an amorphous silicate network rather than being completely released in the gas phase. The silicate network consists of Q4 and Q3 groups formed via intermediate D and T groups. The D groups are formed by a reaction of SiR with bisphenol-A units as well as phenyl groups of PC and BDP. In addition a small amount of silicon diphosphate was observed after thermal treatment at temperatures higher than 810 K. The same decomposition products (without SiP2O7) occur in the solid residues of PC/SiR/BDP/ZnB samples. The formation of intermediate D and T groups occurs earlier, at slightly lower temperatures. Any formation of a borosilicate network was excluded. The results also apply for the fire residues of PC/SiR/BDP and PC/SiR/BDP/ZnB and are thus valuable for understanding the impact of SiR on pyrolysis and flame retardancy mechanisms in the condensed phase during the burning of PC/SiR/BDP blends. SiR was found to influence the pyrolysis and the char formed. Beyond the replacement of highly combustible mechanical modifiers, SiR harbours the potential to enhance flame retardancy.