Patches of white etching layers on rail surfaces were investigated using sophisticated techniques like cross-sectional transmission electron microscopy (XTEM) and synchroton X-ray diffraction. Optical microscopy failed to resolve the microstructure, but in the TEM submicron grains with high dislocation densities and occasional twins, which are characteristic features of high carbon martensite, were observed. The martensitic structure was confirmed by evaluation of synchroton X-ray diffraction line profiles. The latter technique also allowed to determine dislocation densities of the order of 1012 cm-2 and residual compressive stresses of about 200 MPa.
The development of two metallizations based on the solid-phase regrowth principle is presented, namely Pd/Sb(Zn) and Pd/Ge(Zn) on moderately doped In0.53Ga0.47As (p=4×1018 cm-3). Contact resistivities of 23×10-7 and 67×10-7 ?cm2, respectively, have been achieved, where both systems exhibit an effective contact reaction depth of zero and a Zn diffusion depth below 50 nm. Exhibiting resistivities equivalent to the lowest values of Au-based systems in this doping range, especially Pd/Sb(Zn) contacts are superior to them concerning metallurgical stability and contact penetration. Both metallizations have been successfully applied for contacting the base layer of InP/In0.53Ga0.47As heterojunction bipolar transistors.
The melting behaviour of metal–organic frameworks (MOFs) has aroused significant research interest in the areas of materials science, condensed matter physics and chemical engineering. This work first introduces a novel method to fabricate a bimetallic MOF glass, through meltquenching of the cobalt-based zeolitic imidazolate Framework (ZIF) [ZIF-62(Co)] with an adsorbed ferric coordination complex. The high-temperature chemically reactive ZIF-62-(Co) liquid facilitates the formation of coordinative bonds between Fe and imidazolate ligands, incorporating Fe nodes into the framework after quenching. The resultant Co–Fe bimetallic MOF glass therefore shows a significantly enhanced oxygen evolution reaction performance. The novel bimetallic MOF glass, when combined with the facile and scalable mechanochemical synthesis technique for both discrete powders and surface coatings on flexible substrates, enables significant opportunities for catalytic device Assembly
The elastic energy of mixing for multi-component solid solutions is derived by generalizing Eshelby's sphere-in-hole model. By surveying the dependence of the elastic energy on the chemical composition and lattice misfit, we derive a lattice strain coefficient λ*. Studying several high-entropy alloys and superalloys, we propose that most solid solution multi-component alloys are stable when λ*<0.16, generalizing the Hume-Rothery atomic-size rule for binary alloys. We also reveal that the polydispersity index δ, frequently used for describing strain in multi-component alloys, directly represents the elastic energy e with e=qδ², q being an elastic constant. Furthermore, the effects of (i) the number and (ii) the atomic-size distribution of constituting elements on the phase stability of high-entropy alloys were quantified. The present derivations and discussions open for richer considerations of elastic effects in high-entropy alloys, offering immediate support for quantitative assessments of their thermodynamic properties and studying related strengthening mechanisms.
The need for standardization in fluorescence measurements to improve quality assurance and to meet regulatory demands is addressed from the viewpoint of National Metrology Institutes (NMIs). Classes of fluorescence standards are defined, including instrument calibration standards for the determination and correction of instrument bias, application-specific standards based on commonly used fluorescent labels, and instrument validation standards for periodic checks of instrument performance. The need for each class of standard is addressed and on-going efforts by NMIs and others are described. Several certified reference materials (CRMs) that have recently been developed by NMIs are highlighted. These include spectral correction standards, developed independently by both NIST and BAM (Germany), and fluorescence intensity standards for flow cytometry, developed by NIST. In addition, future activities at both institutes are addressed such as the development of day-to-day intensity standards.
A surface-labeled lyophilized lymphocyte (sLL) preparation has been developed using human peripheral blood mononuclear cells prelabeled with a fluorescein isothiocyanate conjugated anti-CD4 monoclonal antibody. The sLL preparation is intended to be used as a reference material for CD4+ cell counting including the development of higher order reference measurement procedures and has been evaluated in the pilot study CCQM-P102. This study was conducted across 16 laboratories from eight countries to assess the ability of participants to quantify the CD4+ cell count of this reference material and to document cross-laboratory variability plus associated measurement uncertainties. Twelve different flow cytometer platforms were evaluated using a standard protocol that included calibration beads used to obtain quantitative measurements of CD4+ T cell counts. There was good overall cross-platform and counting method agreement with a grand mean of the laboratory calculated means of (301.7 ± 4.9) µL-1 CD4+ cells. Excluding outliers, greater than 90% of participant data agreed within ±15%. A major contribution to variation of sLL CD4+ cell counts was tube to tube variation of the calibration beads, amounting to an uncertainty of 3.6%. Variation due to preparative steps equated to an uncertainty of 2.6%. There was no reduction in variability when data files were centrally reanalyzed. Remaining variation was attributed to instrument specific differences. CD4+ cell counts obtained in CCQM-P102 are in excellent agreement and show the robustness of both the measurements and the data analysis and hence the suitability of sLL as a reference material for interlaboratory comparisons and external quality assessment.
Implant-associated infections present severe and difficult-to-treat complications after surgery, related to implant biofilm colonization. Systemic administration of antibiotics cannot reach sufficient concentrations at the infected site and may be toxic. Here we describe how mussel-inspired dendritic material coated on a titanium surface can locally activate a prodrug of daptomycin (pro-dapto) to treat methicillin-resistant Staphylococcus aureus. The mechanism of the prodrug activation is based on bio-orthogonal click chemistry between a tetrazine (Tz) and trans-cyclooctene (TCO). The former is attached to the dendritic polymer, while the later converts daptomycin into a prodrug. Characterization of the material's properties revealed that it is hydrophobic, non-toxic, and stable for a prolonged period of time. We envision that the titanium coated dendritic material will be able to improve the treatment of implant-associated infections by concentrating systemically administered antibiotic prodrugs, thus converting them into active localized medicines.
This report focuses on the characterization of CD4 expression level in terms of equivalent number of reference fluorophores (ERF). Twelve different flow cytometer platforms across sixteen laboratories were utilized in this study. As a first step the participants were asked to calibrate the fluorescein isothiocyanate (FITC) channel of each flow cytometer using commercially available calibration standard consisting of five populations of microspheres. Each population had an assigned value of equivalent fluorescein fluorophores (EFF denotes a special case of the generic term ERF with FITC as the reference fluorophore). The EFF values were assigned at the National Institute of Standards and Technology (NIST). A surface-labelled lyophilized cell preparation was provided by the National Institute of Biological Standards and Control (NIBSC), using human peripheral blood mononuclear cells (PBMC) pre-labeled with a FITC conjugated anti-CD4 monoclonal antibody. Three PBMC sample vials, provided to each participant, were used for the CD4 expression analysis. The PBMC are purported to have a fixed number of surface CD4 receptors. On the basis of the microsphere calibration, the EFF value of the PBMC samples was measured to characterize the population average CD4 expression level of the PBMC preparations. Both the results of data analysis performed by each participant and the results of centralized analysis of all participants' raw data are reported. Centralized analysis gave a mean EFF value of 22,300 and an uncertainty of 750, corresponding to 3.3% (level of confidence 68%) of the mean EFF value. The next step will entail the measurement of the ERF values of the lyophilized PBMC stained with labels for other fluorescence channels. The ultimate goal is to show that lyophilized PBMC is a suitable biological reference cell material for multicolor flow cytometry and that it can be used to present multicolor flow cytometry measurements in terms of ABC (antibodies bound per cell) units.
Particle size gradation is regarded as an effective method for overcoming the contradicting requirements in three-dimensional printing (3DP). In present work, particle size gradation was optimized to obtain both acceptable flowability of the powder material and high-strength 3D-printed glass-ceramic products. The effect of gradation on the printing process, sintering process and performance of the 3D-printed glass-ceramic products was investigated comprehensively. The glass-ceramic powders with three size ranges were mixed in certain proportions and applied to print parts. The result showed parts printed with powder mixed by 60 wt% 45–100 µm and 40 wt% 0–25 µm particles had satisfactory density of 1.60 g/cm³ and bending strength of 13.8 MPa. The flowability decreased with an increasing proportion of fine particles. Part density was determined by the powder bulk density in the powder bed as well as the shrinkage during sintering while strength of part was found to be dependent on the sintering degree.