Filtern
Erscheinungsjahr
Dokumenttyp
Referierte Publikation
- ja (44) (entfernen)
Schlagworte
- Weathering (13)
- Artificial weathering (6)
- Chemiluminescence (6)
- Degradation (4)
- Flame retardant (4)
- Nanocomposite (4)
- UV radiation (4)
- Durability (3)
- Active thermography (2)
- Additive manufacturing (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (14)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (14)
- 6 Materialchemie (5)
- 6.3 Strukturanalytik (4)
- 3 Gefahrgutumschließungen; Energiespeicher (3)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (3)
- 5 Werkstofftechnik (3)
- 4 Material und Umwelt (2)
- 5.3 Polymere Verbundwerkstoffe (2)
- 6.6 Physik und chemische Analytik der Polymere (2)
Scientific publications addressing the durability of the flame retardance of cables during their long-term application are rare and our understanding lacks. Three commercial flame retardants, aluminum hydroxide, aluminum diethyl phosphinate (AlPi-Et), and intumescent flame retardant based on ammonium polyphosphate, applied in ethylene-vinyl acetate copolymer (EVA) model cables, are investigated. Different artificial aging scenarios were applied: accelerated weathering (UV-irradiation/temperature/rain phases), humidity exposure (elevated temperature/humidity), and salt spray exposure. The deterioration of cables’ surface and flame retardancy were monitored through imaging, color measurements, attenuated total reflectance Fourier transform infrared spectroscopy, and cone calorimeter investigations. Significant degradation of the materials’ surface occurred. The flame retardant EVA cables are most sensitive to humidity exposure; the cable with AlPi-Et is the most sensitive to the artificial aging scenarios. Nevertheless, substantial flame retardance persisted after being subjected for 2000 h, which indicates that the equivalent influence of natural exposure is limited for several years, but less so for long-term use.
A systematic approach was used to investigate the weathering-induced degradation of a common water–based intumescent coating. In this study, the coatings are intended for humid indoor applications on steel substrates. The coating contains ammonium polyphosphate, pentaerythritol, melamine, and polyvinyl acetate. By replacing each ingredient with a less water-soluble substance, the most vulnerable substances, polyvinyl acetate and pentaerythritol, were identified. Furthermore, the weathering resistance of the system was improved by exchanging the ingredients. The coatings were stressed by artificial weathering tests and evaluated by fire tests. Thermogravimetry and Fourier-transform infrared spectroscopy were used to study the thermal decomposition. This study lays the foundation for the development of a new generation of water-based intumescent coatings.
Investigation on the Durability of a Polypropylene Geotextile under Artificial Aging Scenarios
(2024)
Geosynthetics are widely used in various civil engineering applications, such as geotextiles in coastal protection, and display a sustainable alternative to natural mineral materials. However, the full benefits of using geosynthetics can only be gained with a long service lifetime of the products. With the use of added stabilizers to the polymers, service lifetimes can be achieved in the range of 100 years. Therefore, accelerated aging methods are needed for the assessment of the long-term performance of geotextiles. In the present study, the behavior of geosynthetic materials made of polypropylene was investigated under artificial aging conditions involving elevated temperatures ranging from 30 to 80 °C, increased oxygen pressures ranging from 10 to 50 bar in water-filled autoclaves, and UV irradiation under atmospheric conditions. ATR-IR spectroscopy was employed to detect the increase in the carbonyl index over various aging durations, indicating the oxidative degradation of the geotextile. The most pronounced increase was observed in the case of aging through UV irradiation, followed by thermal aging. Elevated pressure, on the other hand, had a lower impact on oxidation. High-temperature size exclusion chromatography was utilized to follow the reduction in molar mass under different degradation conditions, and the results were consistent with those obtained from ATR-IR spectroscopy. In polyolefins such as polypropylene, Hindered Amine Stabilizers (HAS) are used to suppress oxidation caused by UV radiation. The quantitative analysis of HAS was carried out using a UV/Vis method and HPLC. The degradation of UV stabilizers during the aging of geotextiles is responsible for the oxidation and the reduction in the molar mass of polypropylene. From the results, it can be concluded that applications of PP geotextile without soil or sand cover might cause the risk of the formation of microplastic particles. Material selection, design, and maintenance of the construction must follow best practices, including the system’s removal or replacement at end-of-life. Otherwise, a sustainable use of geotextiles in civil engineering is not possible.
Recycled plastic granules of high-density polyethylene, polyvinyl chloride and polystyrene the size of microplastics were exposed to artificial aging conditions (2000 h; photooxidative and thermo-oxidative) to simulate their fate outdoors. Their potential to leach into water during the aging process was investigated using column percolation tests.
Aging-related changes on the surface of the material were characterised by IR measurements indicating oxidation reactions with the formation of new adsorption bands (C=O, C–O and OH), especially in the case of photooxidative aging.
These findings were confirmed by the identification of leachable organic compounds. Leaching of total organic carbon, Cl, Ca, Cu and Zn is clearly affected by changes due to aging, and their release is increased after photooxidative aging.
In general, exposure to photooxidative conditions shows a greater influence on aging and thus on leaching and seems to be the more important mechanism for the aging of microplastic in the environment. Comparison with the total content of inorganic species revealed that, for most elements, less than 3% of the total content is released after 2000 h of photooxidative aging.