Schlagworte
- Weathering (13)
- Artificial weathering (6)
- Chemiluminescence (6)
- Degradation (4)
- Flame retardant (4)
- Nanocomposite (4)
- UV radiation (4)
- Durability (3)
- Active thermography (2)
- Additive manufacturing (2)
- Ageing (2)
- Automobillacke (2)
- Automotive coatings (2)
- Chemilumineszenz (2)
- Cone calorimeter (2)
- Crosslinking (2)
- DOPO (2)
- Epoxy resin (2)
- Intumescence (2)
- Irradiation (2)
- Multilayer graphene (2)
- Nitric acid (2)
- Oxidation (2)
- Packaging (2)
- Polyethylene (2)
- Polymer (2)
- Polyurethane (2)
- Rubber (2)
- UV (2)
- 3-dimensional microscopy (1)
- ADF (1)
- Accelerated aging (1)
- Accelerated weathering (1)
- Additives (1)
- Aging (1)
- Alterung (1)
- Aluminum hydroxide (ATH) (1)
- Artificial turf (1)
- Athletic tracks (1)
- Back-sheet foil (1)
- Bacterial attachment (1)
- Bewitterung (1)
- Cable (1)
- Cables (1)
- Carbon nanotubes (1)
- Chemiluminescence (CL) (1)
- Coating (1)
- Coatings (1)
- Colour center (1)
- Column percolation tests (1)
- Contamination (1)
- Dielectric relaxation (1)
- Dispersion (1)
- Eigenschaftsänderung (1)
- Elastomer (1)
- Encapsulation foil (1)
- Ethylene-vinyl acetate (1)
- FTIR (1)
- Fire protective coatings (1)
- Fire resistance (1)
- Fire retardancy (1)
- Friction (1)
- Fuel sorption (1)
- Geotextiles (1)
- Graphene (1)
- HDPE (1)
- Heavy metals (1)
- High density polyethylene (1)
- High-density polyethylene (1)
- Humidity (1)
- Künstliche Bewitterung (1)
- LDPE (1)
- Leaching (1)
- Liquid-cristalline conjugated Polymer (1)
- Magnesium hydroxide (1)
- Mechanical properties (1)
- Micro-CT scanning (1)
- Microplastic (1)
- Middle Pleistocene (1)
- Mildew (1)
- Moisture (1)
- Molecular mass distribution (1)
- Molecular masses (1)
- Nanocomposites (1)
- Numerical simulation (1)
- Optical transmission stability (1)
- Outdoor weathering (1)
- Photo-oxidation (1)
- Photooxidation (1)
- Polarized fluorescence measurements (1)
- Polymer degradation (1)
- Polymer optical fiber (1)
- Polymer optical fibers (POFs) (1)
- Polymers (1)
- Polymerwerkstoff (1)
- Polyolefins (1)
- Quantification (1)
- Release (1)
- Resistance (1)
- Rubber granules (1)
- Sensitive detection (1)
- Siloxane (1)
- Silver nanoparticles (1)
- Size exclusion chromatography (1)
- Snail trails (1)
- South Florida (1)
- Spectral irradiation (1)
- Spectral sensitivity (1)
- Stone Age (1)
- Sulfur containing polymers (1)
- Synergy (1)
- Synthesis (1)
- TG-FTIR (1)
- TPU (1)
- Temperature (1)
- Temperature dependency (1)
- Thermal degradation (1)
- Thermo-oxidation (1)
- Thermo-oxidative stability (1)
- Thermogravimetric analyses (1)
- Thermoluminescence (1)
- Thermolumineszenz (1)
- Thermoset (1)
- Throwing-stick (1)
- Transparency (1)
- Triazine (1)
- UHMWPE (1)
- UV degradation (1)
- UV-irradiation (1)
- UV/VIS spectroscopy (1)
- Weathering resistance (1)
- Wood (1)
- Yellowness index (1)
- biodiesel (1)
- biofuels (1)
- carbon black (1)
- degradation (1)
- multilayer graphene (1)
- nanocomposites (1)
- plasticization (1)
- polyethylene (1)
- rubber (1)
- sorption (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (14)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (14)
- 6 Materialchemie (5)
- 6.3 Strukturanalytik (4)
- 3 Gefahrgutumschließungen; Energiespeicher (3)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (3)
- 5 Werkstofftechnik (3)
- 4 Material und Umwelt (2)
- 5.3 Polymere Verbundwerkstoffe (2)
- 6.6 Physik und chemische Analytik der Polymere (2)
Combined impact of ultraviolet and chemical fluids on high-density polyethylene packaging material
(2012)
To investigate the ageing behaviour of filled plastic containers outdoors, square cuts of the wall of two high-density polyethylene (HDPE) types were exposed to ultraviolet (UV) radiation at their front side and to specific liquid chemicals (de-ionized water, surfactant or White Spirit) at their back. The UV radiant exposure at the front side was 80 MJ/m².
To compare the actions of the different exposures, separate dark backside fluid exposures were performed, in parallel. Besides, UV weathering was carried out until a UV radiant exposure of 325 MJ/m², being roughly comparable to outdoor exposure of one year in Northern Australia.
An unpigmented HDPE included in the investigation gave no sufficient protection for the White Spirit. In addition, it showed clear degradation after several of these exposures. In combination with the White Spirit, an increase of carbonyl bonds was measured, presumably assignable to degradation products of the White Spirit.
For a pigmented HDPE material, with the implemented combined exposures, no relevant damage was observed, within applied the exposure period.
As the results of a 14 weeks outdoor exposure of a series of automotive coatings in South Florida, the panels were found to be overgrown with an almost closed layer of mildew. Pinholes remained as permanent surface damage after removing the mildew mycelium. The extent of the damage differed in dependence of the kind of the coating. By tracing the images and profiles of the coating surfaces systematically over all phases of weathering and the subsequent cleaning procedure, a connection between formation of pinholes and mildew growth could be found. Outdoor weathering tests in other regions of Florida as well as in Europe and Australia showed that pinholes caused by mildew attack could also be found in all other locations, but always to a lower extent than in South Florida. The standardised mildew tests EN ISO 846 and MIL-STD 810F for laboratory exposure failed to reproduce the formation of pinholes.
Chemiluminescence for the early detection of weathering effects of coatings - Part I: Fundamentals
(2010)
For polypropylene of varied stabilization, spectral sensitivity as well as temperature dependence of irradiation caused crack formation was determined in artificial irradiation tests. UV radiant exposure HUV necessary to generate crack formation was measured both in spectrally dispersed irradiation and artificial irradiation in a Fluorescent UV lamp device. Dependencies were fitted to a plateau function and an Arrhenius function, respectively, to describe the action of irradiation by response functions. Applied to weather data from Phoenix, the results were compared with respective outdoor exposure results.
The influence of weathering on the fire retardancy of polymers is investigated by means of a cone calorimeter test, before and after artificial weathering. The surface degradation was monitored using different techniques (ATR–FTIR, microscopy, colour measurement). Different kinds of polymeric materials were chosen, all as they are used in practice: polycarbonate (PC) blends, polyamide (PA) and polypropylene (PP) flame-retarded with arylphosphate, melamine cyanurate (MC) and intumescent formulation based on ammonium polyphosphate (APP), respectively.
All samples show material degradation at the surface due to weathering. No significant weathering influence occurs on the flame retardancy when it is a bulk property, as was observed for aryl phosphates in PC blends and MC in PA. When the fire retardancy is dominated by a surface mechanism, dependence on the duration of weathering is detected: for intumescent formulations based on ammonium APP in PP, a worsening in the formation of the intumescent network was observed.
Chemiluminescence (CL) is a sensitive method of investigating the thermo-oxidative stability of polymers in the early stages of degradation. Therefore, CL measurements were applied to different automotive coatings to evaluate their degradation behavior during artificial weathering. In this work, CL measurements were carried out for different automotive coatings to follow their degradation behavior during artificial weathering. The CL emission depends on sample-specific parameters like stabilizer, matrix, or hardener; experimental parameters like the oxygen partial pressure; and exposure parameters like the duration of weathering. The potential of CL could be demonstrated by classifying materials into categories of good, medium, and low degradation performance at a much earlier stage of weathering exposure than in combination with the usual visual detection of weathering effects.
The optical transmission stability was investigated for commercially available polymer optical fibers (POFs) which were exposed to a climate of 92°C and 95% relative humidity for about 3300 h. The optical transmission stability of POFs was correlated to their thermooxidative stability. POFs possessed identical core material, poly(methyl methacrylate), but they differed in the materials used for the claddings. The optical transmission was measured online using a prototype device called multiplexer. The chemiluminescence (CL) technique was applied to characterize the thermooxidative stability and degradation of POFs. CL analysis reveals the thermooxidative degradation of bare POFs (core and cladding), predominantly of the claddings, as a result of climatic exposure. Ultraviolet-visible transmittance measurements demonstrated more changes in the claddings as compared to the cores due to degradation. The CL and optical measurements data indicated that the optical transmission stability of POFs was dependent mainly on the thermooxidative stability of the claddings and their chemical compositions.
The thermo-oxidative stability of commercially available polymer optical fibers (POFs) and their components (cores and claddings) was investigated. All the bare POFs (core and cladding only) studied here were based on poly(methyl methacrylate) (PMMA) core. The fibers were exposed to 100 °C/low humidity for about 4200 h. Chemiluminescence (CL) technique was applied to investigate the thermo-oxidative stability and for measuring the transmission loss during exposure a prototype device called multiplexer was used. POFs exhibited variation in thermo-oxidative stability although they possessed identical core material PMMA. This was due to difference in the chemical compositions of claddings. Claddings were more susceptible to the thermo-oxidative degradation compared to cores. The thermo-oxidative degradation of both the cladding and the core was found in POFs as a result of climatic exposure. POFs showed an early drop-off followed by a slow decline of transmission. The early drop-off of transmission was attributed to physical changes like thermal expansion and the slow decline of transmission to chemical changes like oxidative degradation of POFs. A good linear relationship between optical transmission stability and thermo-oxidative stability of POFs was established from these studies.