The tribological behaviour under dry sliding conditions of Magneli phase Ti4O7 and e-phase Ti2Cr2O7 with α-alumina as a sliding partner has been characterised at room temperature by oscillating sliding. The mechanical properties as well as Vickers hardness measurements do not reveal big differences between the materials, and 4-point bending strengths are around 200 MPa for both materials. Although the friction coefficients are in the medium range of 0.6 and do not differ much between the materials, the wear behaviour is very different. At room temperature, the wear coefficient of Ti2O7 is strongly dependent on relative humidity, and wear is highest under dry conditions when relative humidity is low as it is typically found for many ceramic materials. Ti2Cr2O7 shows remarkably different wear behaviour with the lowest wear in dry conditions. The measured coefficients of wear at low relative humidity of 4% are more than 2 orders of magnitude lower than those for Ti2O7.
Stribeck curve
(2014)
The importance of lubricants in virtually all fields of the engineering industry is reflected by an increasing scientific research of the basic principles. Energy efficiency and material saving are just two core objectives of the employment of high-tech lubricants. The encyclopedia presents a comprehensive overview of the current state of knowledge in the realm of lubrication. All the aspects of fundamental data, underlying concepts and use cases, as well as theoretical research and last but not least terminology are covered in hundreds of essays and definitions, authored by experts in their respective fields, from industry and academic institutes.
COMPOSITE MATERIALS OF A 99.7 % ALPHA-ALUMINA MATRIX WITH PLATELETS OF SILICON CARBIDE (SICP) HAVE BEEN PREPARED BY GELCASTING. DENSIFICATION WAS CARRIED OUT BY GAS-PRESSURE SINTERING WITHOUT FURTHER SINTERING AIDS. FIVE DIFFERENT COMPOSITIONS WITH 0, 5, 10, 15, AND 20 VOL.% SICP RESP. HAVE BEEN INVESTIGATED AND TRIBOLOGICAL PROPERTIES WERE CHARACTERIZED. INCREASING AMOUNT OF SICP AS RIGID PARTICLES IN THE FINE GRAINED MATRIX COMPLICATE THE DENSIFICATION PROCESS. WITH THE APPLICATION OF 50 BAR AR PRESSURE DURING THE FINAL SINTERING STEP AT A TEMPERATURE OF 1700 DEGREE C THE DENSITY OF THE SAMPLES COULD BE INCREASED BY 3-5%. INVESTIGATION OF THE TRIBOLOGICAL PROPERTIES AGAINST STEEL AS A COUNTERBODY UNDER UNLUBRICATED OSCILLATING SLIDING CONDITIONS SHOWED A HIGH COEFFICIENT OF FRICTION AND AN INCREASING WEAR RATE UP TO A SICP CONTENT OF 10 VOL. % . AT 15 AND 20 VOL. % SICP RESP. BOTH THE COEFFICIENT OF FRICTION AND THE COEFFICIENT OF WEAR DROP DOWN.
Fretting
(2014)
The importance of lubricants in virtually all fields of the engineering industry is reflected by an increasing scientific research of the basic principles. Energy efficiency and material saving are just two core objectives of the employment of high-tech lubricants. The encyclopedia presents a comprehensive overview of the current state of knowledge in the realm of lubrication. All the aspects of fundamental data, underlying concepts and use cases, as well as theoretical research and last but not least terminology are covered in hundreds of essays and definitions, authored by experts in their respective fields, from industry and academic institutes.
Tribological Characterisation of a Sl3N4-TiN Composite Ceramic in Fretting Tests at Room Temperature
(2004)