The influence of temperature and counterbody material on the tribological properties of a-C:H coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk contact situation. The results show, that the wear volumes of the system increase exponentially with increasing temperature. Two different wear mechanisms seem to have a major influence: First, the abrasive action due to materials hardness and second, the tribooxidation when silicon nitride is counter material.
The influence of temperature and counterbody material on the tribological properties of a-C:H
coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk
contact situation with alpha-alumina and silicon nitride as counterbodies. The results show, that the wear volumes of the systems increase exponentially with increasing temperature, for alpha-alumina more than for silicon nitride. Two different wear mechanisms seem to have a
major influence: First, the abrasive action due to materials hardness and second, the tribo-oxidation when silicon nitride is counter material.
Wear mechanisms, as adhesion, abrasion, fatigue and tribochemical wear, are complex in their physical and chemical nature. A theoretical description and prediction of wear are in most cases still far from reality. It is, therefore, important to use test rigs before a practical application of a given material combination under tribological loading.
On the other hand, model equations can be helpful for wear description, if a single wear mechanism is dominant.
Under oscillating and continuous sliding contact conditions, equations for wear calculation are presented to describe running-in and stationary wear behaviour of metals and ceramics. By using shear energy density, real area of contact, flash temperature, activation energy and numerical simulations with the method of movable cellular automata (MCA), wear data were calculated and compared to experimental laboratory results.
Ceramic particulate composites in the system SiC-TiC-TiB2 sliding against SiC and Al2O3 under water
(1999)
The tribological behaviour of SiC, SiC-TiC and SiC-TiC-TiB2 was determined in oscillating sliding against SiC and -Al2O3 in water at room temperature. The tribo-systems with the composite materials containing TiC and TiB2 differ significantly from the systems with the single phase SiC: The wear is reduced and the friction is increased. The wear reduction up to a factor of 10 is mainly due to the formation of an oxide film containing titanium oxides which is soft, stable in water and well adhering to the bulk material. This oxide film is transferred to the alumina ball but not to the silicon carbide ball.
Different fretting tests of thin steel wires under different conditions (loads, strokes, number of cycles and mean pressures) were performed. The wires used had 0.45 mm in diameter and the material was a cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength over 2800 MPa. The tests were carried out with 90° "crossed cylinders" configuration varying the stroke, normal load and testing time (number of cycles). Afterwards the volumetric wear was obtained using surface profilometry with diamond stylus.
With a classical study of the coefficient of wear with respect to the sliding distance, the results show that the wear coefficient increases with normal load and stroke, consequently, for the same sliding distance, the wear produced was higher when the load and/or stroke is increased. In this work, the coefficient of wear is decreasing continuously as the test is running. In order to analyze better the wear behaviour, another method, in which the volumetric wear is compared with respect to the Archard's loading factor, is proposed. As result of this method, two distinctive behaviours were detected; one corresponds to the running-in period with a more aggressive wear behaviour and the second one to the stable steady state period. In all the tests the running-in period was similar with regard to the wear rates but in the stable period the wear rates were increasing with higher loads or strokes.
Pristine, reduced, and alkylated graphene oxides are applied as lubricating additives in paraffin grease. It has revealed that their crystalline structure governs the tribological properties of grease for steel tribo-pair. The microstructural analyses of grease samples showed that a loose fiber network of soap in the presence of graphene-based additive allows their facile release for efficient lubrication. The surface analyses based on the microscopic and elemental mapping show the development of a graphene-derived protective film on the worn scars, which protected the tribo-surfaces and subsided the wear. The reduced graphene oxide (rGO) with the interlamellar distance of 0.35 nm in the (002) plane provided minimum resistance to shear and exhibited maximum reduction in coefficient of friction (COF) for the paraffin grease. The presence of oxygen functionalities in the basal of pristine and alkylated graphene oxide (GO) compromised the interlamellar shearing under tribo-stress; consequently, higher COF than that of rGO.