The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose.
The production of Portland cement causes a substantial environmental impact, since the calcination of limestone results in high emissions of carbon dioxide. The use of supplementary cementitious materials such as calcined clays as partial replacement for Portland cement offers a solution to limit this environmental impact. This paper investigates four clays from deposits in central Germany with the aim of obtaining pozzolans for the production of Portland-pozzolana cement. The results obtained show that the calcined clays possess pozzolanic properties, which differ depending on calcination temperature and the relative amounts of Kaolinite and 2:1 clay minerals.