The chemical and microstructural changes occurring during braking simulation tests at the surface of a conventional brake pad material were investigated mainly by scanning and transmission electron microscopy and surface analytical techniques. It can be shown that patches of a third body material develop, comprising a compositional mix of all constituents of the pad and iron oxides from the disk. Milled debris particles still have the crystal structure of barite, the major phase of the pad material, but the grain size is reduced drastically to the nanometer scale. The major wear mechanism is delamination of filler particles from the organic binder, supported by local degradation of the phenolic resin during asperity heating. Quartz crystals are preserved thereby adopting the function of primary contact areas.
The formation of a third body layer on a conventional friction material during braking tests was studied in some detail using TEM, SEM, and X-ray photoelectron spectroscopy (XPS) techniques. Plate shaped micro-contact areas representing a compositional mix of all components of the tribocouple and exhibiting a nanocry stalline microstructure were identified after a run-in period.
Ti/TiN multilayer coatings with multilayer periods in the range 550 nm and a final thickness of 2 µm were deposited on steel substrates by cyclic modulation of nitrogen gas flow into the chamber of a PVD sputtering device. Coating characterization was performed by cross-sectional transmission electron microscopy, glancing-angle X-ray diffraction and instrumental indentation testing. Individual a-titanium and titanium nitride layers were always observed, although for the finer microstructures, the TiN layers were thicker than the Ti layers by a factor three. The plastic hardness of the films increased steadily with decreasing layer spacing, following a HallPetch relationship. Finally, a hardness value of 42 GPa was reached, which is similar to that of a thick TiN monolayer, prepared under the same coating conditions.