Several approaches were investigated to produce monosort functionalized polymer surfaces with a high density and homogeneity of functional groups: (i) Plasma oxidation followed by wet-chemical reduction, (ii) formation of radicals and grafting on of functional group carrying molecules, (iii) plasma bromination followed by (iv) Williamson or Gabriel-like synthesis of spacer molecules, and (v) a pulsed plasma polymerization of functional groups bearing monomers or (vi) their copolymerisation with other comonomers. The formation of hydroxyl (OH), primary amino (NH2), and carboxyl (COOH) groups was studied in detail. The oxygen plasma treatment (i) in a low-pressure non-isothermal glow discharge results in the formation of a wide variety of O functional groups, polymer degradation and crosslinking. Low power densities and short exposure times (0.1 to 2 s) are required to functionalize a surface while preserving the original polymer structure. Carbonate, ester, and aromatic groups are rapidly degraded by an oxygen plasma treatment leading to scissions of polymer backbones and loss in molecular weight. Also the formation of macrocycles and C=C bonds was observed in a region of around 4 nm in depth. The investigated polymers could be classified by their degradation behaviour on exposure to the oxygen plasma.___TAGSTART___BR___TAGEND___ In order to maximize the process selectivity for OH groups, the variety of oxygen functionalities formed by the oxygen plasma was wet-chemically reduced by diborane, vitridetrade (Na complex), and LiAlH4. Typical yields were 9 to 14 OH groups per 100 carbon atoms.___TAGSTART___BR___TAGEND___ Plasma bromination (iii) (40 Br per 100 C atoms) of polymers, followed by grafting of spacer molecules (iv), has been proved to be a highly selective reaction.___TAGSTART___BR___TAGEND___ Another way to produce high densities of monosort functionalities was the pulsed plasma polymerization of functional group bearing monomers such as allylamine, allylalcohol or acrylic acid (v). The retention of chemical structure and functional groups during plasma polymerization was achieved by using low power densities and the pulsed plasma technique. The maximum yields were 30 OH, 18 NH2, and 24 COOH groups per 100 C atoms. To vary the density of functional groups a chemical copolymerization with ''chain-extending'' comonomers such as butadiene and ethylene was initiated in the pulsed plasma (vi). Additionally, the often-observed post-plasma oxidations of such layers initiated by reaction of trapped radicals with oxygen from the air were successfully suppressed by using NO gas as radical quencher.
This new functionalization method consists of the deposition of very thin plasma polymer layers (20 to 100 nm) of functional group bearing monomers in pulsed plasma. With allylalcohol, a maximum of 30 OH groups per 100 C atoms was measured with a selectivity of about 90% and a significant stability at long-time exposure to air. Allylamine was used to produce primary amino groups, with a maximum of 18 NH2 groups per 100 C atoms. Side reactions were observed during the storage in air, such as oxidation of the amino groups. Carboxylic groups could be produced using acrylic acid with a maximum concentration of 24 COOH groups per 100 C atoms. The most prominent side reaction was the decarbonylation/ decarboxylation of the acid group during plasma deposition.___TAGSTART___BR___TAGEND___ The variation of the density of functional groups using the pulsed-plasma polymerization of functional-group-bearing monomers was possible by the chemically-initiated radical copolymerization with either a chain-extending monomer, such as ethylene, or a cross linker, such as butadiene, in plasma. The density of functional groups could be adjusted continuously (0 to 30 OH, 0 to 18 NH2 and 0 to 24 COOH groups per 100 C atoms).___TAGSTART___BR___TAGEND___ The successful application of these densely functionalized polymer surfaces for producing biocompatible surfaces and for use in metalpolymer composites is proposed.
Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms).
Pulsed plasma-deposited polystyrene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited polystyrene films was investigated. From these data, information on the chemical character of the plasma polystyrene films was derived. In the range of deposition conditions applied in this study, the fragmentation of styrene is a minor process. The main process is probably the radical chain propagation to polymers. All the polystyrene plasma polymers, relying on ToF-SIMS, seem to be rather similar to a reference polystyrene oligomer sample. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. Oxygen uptake was found to alter the emission probabilities of secondary ions. A relation between the regularity of the plasma polymers and the amount of oxygen incorporation was found. The result was that the chemical regularity of the plasma polystyrene decreases when the effective power in the plasma is increased.
Organic thin films with defined chemical structures and physical properties are required for various applications. Plasma polymerization is of technological interest, since the deposition of plasma polymers is possible on any material of any shape in the desired thickness. We report on the TOF-SIMS (TOF: time-of-flight) and XPS investigations of pulse plasma poly(acetylene) and alkali metal doped pulse plasma poly(acetylene) films. The combination of TOF-SIMS and XPS supplies detailed information on the surface chemistry of these films. Application of both methods provides the possibility for cross-checking certain results. Moreover the different sensitivities of the methods can be utilized. According to the TOF-SIMS and XPS data it can be concluded that the interaction of alkali metals with plasma poly(acetylene) results in electrovalent bonds of the type Me?+C?- between carbon and metal. Furthermore carbonoxygenmetal interactions were observed. These interactions are of the type C=O?-cdots, three dots, centeredMe?+ and/or CO?-Me?+.
Pulsed plasma deposited styrene and ethylene films were studied by Time of Flight Static Secondary Ion Mass Spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma deposited films was investigated. Approaches for the interpretation of SSIMS spectra of organic materials were reviewed and applied to the evaluation of SSIMS data of plasma deposited films. From these data, information on the chemical character of the plasma deposited films was derived.
When the plasma polymers are exposed to air oxygen incorporation occurs. The oxygen uptake is high at the beginning and then it levels of.
A relation that higher the regularity of the film lower is the oxygen uptake was found. Harder plasma conditions, which could be obtained by applying higher plasma power or lower monomer flow rate, result in higher oxygen uptake and vice versa.
Plasma polymerised films of acrylic acid, allyl alcohol and allyl amine were prepared and studied by XPS (X-ray photoelectron spectroscopy) and XAS (X-ray absorption spectroscopy). The influence of external plasma parameters on certain chemical aspects of the films was investigated. The use of XPS and NEXAFS (near edge X-ray absorption fine structure) as complimentary tools in the surface characterisation of thin films has been highlighted. Certain chemical aspects of the plasma polymerised films such as presence of ROCdouble bond; length as m-dashO in the case of plasma polymerised acrylic acid films, presence of RCdouble bond; length as m-dashO and RCOR bonds in case of plasma polymerised allyl alcohol films and presence of RCdouble bond; length as m-dashN and C?N in case of plasma polymerised allyl amine films were studied. The concentration of ROCdouble bond; length as m-dashO species was found to decrease with increase in r.f. duty cycle in the case of plasma polymerised acrylic acid films. In case of plasma polymerised allyl alcohol films there is a decrease in the concentration of RCdouble bond; length as m-dashO species and increase in the concentration of RCOR species at higher pressures, while in the case of plasma polymerised allyl amine films the concentration of RCdouble bond; length as m-dashN and C?N increases at higher powers, with an increase in C?N more pronounced at higher powers.
Chemical properties of plasma-polymerized styrene films can be effectively controlled by the appropriate choice of external plasma parameters, such as duty cycle, power and monomer pressure. Chemical properties here are the regularity of the primary structure, the amount of long living radicals and branching or cross-linking or both in plasma polymerized styrene films, which can be indirectly monitored by X-ray photoelectron spectroscopy (XPS) and near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Principally, XPS and NEXAFS spectra of plasma-polymerized styrene show all the spectroscopic fingerprints characteristic of atactic polystyrene indicating an inherent similarity of the respective primary chemical structures. There is an increase in irregularity and radical concentration for the plasma deposited films with increasing duty cycle or power. With an increase in monomer pressure, a decreased level of monomer fragmentation and, consequently, an increase in regularity must be concluded from the experimental data. The applied power regulates the fragmentation of the monomers as monitored by spectroscopic signals correlated to the aromatic rings. A trend in the extent of the post-plasma oxygen incorporation according to the variation of the various external plasma parameters was deduced, which agrees with earlier ToF-SIMS findings
Pulsed-plasma-deposited ethylene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited ethylene films was investigated. From these data, information on the chemical character of the plasma-deposited ethylene films was derived. The investigation of the effect of external plasma parameters on the chemical character of the plasma-deposited ethylene films revealed that there were some drastic changes in the secondary ion mass spectra of the films. It was found that fragmentation and re-arrangement of the monomer molecules in the plasma, which affects the chemical character of the deposited films, vary according to the external plasma parameters. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. The oxygen uptake is high at the beginning and then it levels of. Some indications for the formation and decay of peroxy radicals (COO) and, subsequently, hydroperoxides (COOH) are found. It was observed that the oxygen uptake of the plasma deposited ethylene films increase when the plasma conditions become harder.
Selected FTIR, XPS and NEXAFS spectroscopy results obtained with films deposited with different plasma polymerization processes and different monomers (styrene, acetylene, ethylene and butadiene) are presented. In detail FTIR spectra, XPS surveys, XPS valence bands and core level signals including shake-up features as well as carbon K-edge absorption spectra are qualitatively and, in some cases, semi-quantitatively considered. Information on the film formation, the chemistry of the films and the film stability against air exposure are derived from spectroscopic features. With styrene chemically rather well defined plasma polymer layers can be formed with rather high deposition rates applying a pulse plasma process. Using ethylene, acetylene or butadiene as a monomer in the plasma deposition process the deposition rates are smaller. Using these monomers plasma polymer films can be obtained with a primary chemical structure which is similar to each other but more or less different from those of the respective conventional polymers. The main difference between these samples is their individual concentration of unsaturated carbon species. Finally, a technologically relevant example, i.e. a plasma deposited polymer barrier layer deposited on the inner wall of a poly(ethylene) vessel is briefly considered.