Filtern
Dokumenttyp
- Zeitschriftenartikel (17)
- Posterpräsentation (2)
Sprache
- Englisch (19) (entfernen)
Schlagworte
- EBSD (11)
- Lattice parameters (5)
- Kikuchi patterns (4)
- Pattern matching (4)
- Electron backscatter diffraction (3)
- Kikuchi diffraction (3)
- Electron diffraction (2)
- Electron microscopy (2)
- Kikuchi (2)
- Martensite (2)
Organisationseinheit der BAM
Approximant-based orientation determination of quasicrystals using electron backscatter diffraction
(2020)
Orientation mapping of quasicrystalline materials is demonstrated using crystalline approximant structures in the technique of electron backscatter diffraction (EBSD). The approximant-based orientations are symmetrised according to the rotational point group of the quasicrystal, including the visualization of orientation maps using proper colour keys for quasicrystal symmetries. Alternatively, approximant-based orientation data can also be treated using pseudosymmetry post-processing options in the EBSD system software, which enables basic grain size estimations. Approximant-based orientation analyses are demonstrated for icosahedral and decagonal quasicrystals.
To visualize the varying tetragonal distortions in high carbon martensitic steels by EBSD, two different approaches have been applied on backscattered Kikuchi diffraction (BKD) patterns. A band-edge refinement technique called Refined Accuracy (RA) (Oxford Instruments) is compared with a technique called Pattern Matching (PM), which optimizes the fit to a simulated BKD signal. RA distinguishes between hypothetical phases of different fixed 𝑐∕𝑎, while PM determines a best fitting continuous 𝑐∕𝑎 by projective transformation of a master pattern. Both techniques require stored BKD patterns.
The sensitivity of the 𝑐∕𝑎-determination was tested by investigating the microstructure of a ferritic steel with an expected 𝑐∕𝑎 = 1. The influence of the Kikuchi pattern noise on 𝑐∕𝑎 was compared for a single or 40 averaged frames per measuring point, and turned out to be not significant. The application of RA and PM on the martensitic microstructure delivered qualitatively similar maps of 𝑐∕𝑎. The comparison of RA and PM shows that RA is suitably fast and precise during mapping the martensite 𝑐∕𝑎 ratio in analyses of high carbon martensite, especially for fast initial surveys. As RA leads quantitatively to higher noise in 𝑐∕𝑎, the PM analysis can be used for higher precision results.
In this paper, the accurate determination of the size and size distribution of bipyramidal anatase nanoparticles (NPs) after deposition as single particles on a silicon substrate by correlative Scanning Electron Microscopy (SEM) with Atomic Force Microscopy (AFM) analysis is described as a new measurement procedure for metrological purposes. The knowledge of the exact orientation of the NPs is a crucial step in extracting the real 3D dimensions of the particles. Two approaches are proposed to determine the geometrical orientation of individual nano‐bipyramides: (i) AFM profiling along the long bipyramid axis and (ii) stage tilting followed by SEM imaging. Furthermore, a recently developed method, Transmission Kikuchi Diffraction (TKD), which needs preparation of the crystalline NPs on electron‐transparent substrates such as TEM grids, has been tested with respect to its capability of identifying the geometrical orientation of the individual NPs. With the NPs prepared homogeneously on a TEM grid, the transmission mode in a SEM, i.e., STEM‐in‐SEM (or T‐SEM), can be also applied to extract accurate projection dimensions of the nanoparticles from the same sample area as that analysed by SEM, TKD and possibly AFM. Finally, Small Angle X‐ray Scattering (SAXS) can be used as an ensemble technique able to measure the NPs in liquid suspension and, with ab‐initio knowledge of the NP shape from the descriptive imaging techniques, to provide traceable NP size distribution and particle concentration.
In this paper one refined approach is applied to determine the exact orientation of bipyramidal TiO2 nanoparticles prepared with good dispersion as almost isolated particles on a carbon TEM grid. The advantages of the recently developed high-throughput Transmission Kikuchi Diffraction (TKD) are used to identify quickly and reliably the geometrical orientation of the crystalline TiO2 nanoparticle bipyramids (anatase) on a statistically relevant number of particles.
A historical tool for crystallographic analysis is provided by the Hilton net, which can be used for manually surveying the crystal lattice as it is manifested by the Kikuchi bands in a gnomonic projection. For a quantitative analysis using the Hilton net, the projection centre as the relative position of the signal source with respect to the detector plane needs to be known. Interplanar angles are accessible with a precision and accuracy which is estimated to be ≤0.3o. Angles between any directions, e.g. zone axes, are directly readable. Finally, for the rare case of an unknown projection-centre position, its determination is demonstrated by adapting an old approach developed for photogrammetric applications.
It requires the indexing of four zone axes [uvw]i in a backscattered Kikuchi diffraction pattern of a known phase collected under comparable geometric conditions.
A pseudosymmetric description of the crystal lattice derived from a single wideangle Kikuchi pattern can have several causes. The small size (<15%) of the sector covered by an electron backscatter diffraction pattern, the limited precision of the projection centre position and the Kikuchi band definition are crucial. Inherent pseudosymmetries of the crystal lattice and/or structure also pose a challenge in the analysis of Kikuchi patterns. To eliminate experimental errors as much as possible, simulated Kikuchi patterns of 350 phases have been analysed using the software CALM [Nolze et al. (2021). J. Appl. Cryst. 54, 1012–1022] in order to estimate the frequency of and reasons for pseudosymmetric crystal lattice descriptions. Misinterpretations occur in particular when the atomic scattering factors of non-equivalent positions are too similar and reciprocal-lattice points are systematically missing. As an example, a pseudosymmetry prediction depending on the elements involved is discussed for binary AB compounds with B1 and B2 structure types. However, since this is impossible for more complicated phases, this approach cannot be directly applied to compounds of arbitrary composition and structure.
The derivation of a crystal structure and its phase-specific parameters from a single wide-angle backscattered Kikuchi diffraction pattern requires reliable extraction of the Bragg angles. By means of the first derivative of the lattice profile, an attempt is made to determine fully automatically and reproducibly the band widths in simulated Kikuchi patterns. Even under such ideal conditions (projection centre, wavelength and lattice plane traces are perfectly known), this leads to a lattice parameter distribution whose mean shows a linear offset that correlates with the mean atomic number Z of the pattern-forming phase. The consideration of as many Kikuchi bands as possible reduces the errors that typically occur if only a single band is analysed. On the other hand, the width of the resulting distribution is such that higher image resolution of diffraction patterns, employing longer wavelengths to produce wider bands or the use of higher interference orders is less advantageous than commonly assumed.
A band width determination using the first derivative of the band profile systematically underestimates the true Bragg angle. Corrections are proposed to compensate for the resulting offset Δa/a of the mean lattice parameters derived from as many Kikuchi band widths as possible. For dynamically simulated Kikuchi patterns, Δa/a can reach up to 8% for phases with a high mean atomic number Z, whereas for much more common low-Z materials the offset decreases linearly. A predicted offset Δa/a = f(Z) is therefore proposed, which also includes the unit-cell volume and thus takes into account the packing density of the scatterers in the material. Since Z is not always available for unknown phases, its substitution by Zmax, i.e. the atomic number of the heaviest element in the compound, is still acceptable for an approximate correction. For simulated Kikuchi patterns the offset-corrected lattice parameter deviation is Δa/a < 1.5%. The lattice parameter ratios, and the angles α, β and γ between the basis vectors, are not affected at all.1.5%. The lattice parameter ratios, and the angles , and between the basis vectors, are not affected at all.
A new software is presented for the determination of crystal lattice parameters from the positions and widths of Kikuchi bands in a diffraction pattern. Starting with a single wide-angle Kikuchi pattern of arbitrary resolution and unknown phase, the traces of all visibly diffracting lattice planes are manually derived from four initial Kikuchi band traces via an intuitive graphical user interface. A single Kikuchi bandwidth is then used as reference to scale all reciprocal lattice point distances. Kikuchi band detection, via a filtered Funk transformation, and simultaneous display of the band intensity profile helps users to select band positions and widths. Bandwidths are calculated using the first derivative of the band profiles as excess-deficiency effects have minimal influence. From the reciprocal lattice, the metrics of possible Bravais lattice types are derived for all crystal systems. The measured lattice parameters achieve a precision of <1%, even for good quality Kikuchi diffraction patterns of 400 x 300 pixels. This band-edge detection approach has been validated on several hundred experimental diffraction patterns from phases of different symmetries and random orientations. It produces a systematic lattice parameter offset of up to ±4%, which appears to scale with the mean atomic number or the backscatter coefficient.
The locally varying tetragonality in martensite grains of a high-carbon steel (1.2 mass percent C) was resolved by electron backscatter diffraction (EBSD) with a spatial resolution in the order of 100 nm. Compared to spatially integrating X-ray diffraction, which yielded an average tetragonality fo c/a=1.05, the EBSD measurements in the scanning electron microscope allowed to image a local variation of the lattice papameter ration c/a in the range of 1.02 ≤ c/a ≤ 1.07. The local variation of tetragonality is confirmed by two different EBSD data analysis approaches based on the fitting of simulated to experimental EBSD patterns. The resulting EBSD-based tetragonality maps are pointing to a complex interaction of carbon concentration and local lattice distortions during the formation process of martensitic structures.