A key limitation of the most constitutive models that reproduce a Degradation of quasi-brittle materials is that they generally do not address issues related to fatigue. One reason is the huge computational costs to resolve each load cycle on the structural level. The goal of this paper is the development of a temporal Integration scheme, which significantly increases the computational efficiency of the finite element method in comparison to conventional temporal integrations.
The essential constituent of the fatigue model is an implicit gradient-enhanced formulation of the damage rate. The evolution of the field variables is computed as amultiscale Fourier series in time.On a microchronological scale attributed to single cycles, the initial boundary value problem is approximated by linear BVPs with respect to the Fourier coefficients. Using the adaptive cycle jump concept, the obtained damage rates are transferred to a coarsermacrochronological scale associated with the duration of material deterioration. The performance of the developedmethod is hence improved due to an efficient numerical treatment of the microchronological problem in combination with the cycle jump technique on the macrochronological scale. Validation examples demonstrate the convergence of the obtained solutions to the reference simulations while significantly reducing the computational costs.
Accurate models for the long term behavior of concrete structures are important to ensure a durable and reliable design.
A variety of interacting phenomena, such as the loss of prestress, the degradation due to chemical reactions or creep and shrinkage, influence the fatigue resistance. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required.
The presented fatigue model is an extension of a static damage model to allow easy coupling in a multiphysics context. The evolution equation of the damage driving variable is enhanced to allow damage growth below the static limit. The model is defined in the time domain and does not include the number of cycles as a parameter.
Thus, it can capture both static and cyclic failure.
Additionally, this allows calibrating the majority of the model parameters static experiments. The model is integrated by resolving each loading cycle, requiring about ten time steps per cycle. The high computational costs are handled via a time scale separation.
The short time scale describes one cycle with marginal changes in the internal variables. These changes are integrated along the large time scale of material deterioration. Various high-order time integration schemes are compared.
Wöhler curves relate loading amplitudes to the number of cycles that the material endures. They are used to validate the model against experimental data.
Lifetime aspects including fatigue failure of concrete structures were traditionally only of minor importance. Because of the growing interest in maxing out the capacities of concrete, its fatigue failure under compression has become an issue. A variety of interacting phenomena such as e.g. loss of prestress, degradation due to chemical reactions or creep and shrinkage influence the fatigue resistance. Failure due to cyclic loads is generally not instantaneous, but characterized by a steady damage accumulation. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required, which accurately captures order effects and full three-dimensional stress states.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales.
However, a key limitation of those models is that they generally do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles. This is due to the computational effort necessary to explicitly resolve every cycle which exceeds the currently available computational resources. The limitation can only be overcome by the application of multiscale methods in time.
The objective of the paper is the development of numerical methods for the simulation of concrete under fatigue loading using temporal multiscale methods.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses [1]. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from static tests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level.
Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach [2]. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
Finally, the developed methods will be validated and compared to experimental data.