Intermediate-scale testing is indispensable when investigating the fire resistance under simultaneous compressive load of components made of glass- and carbon-fibre-reinforced composites (GFRP and CFRP). BAM is successfully operating an intermediate-scale test stand, developed for a specimen size of 500 mm x 500 mm (1000 mm). The fire resistance in terms of fire stability of CFRP and GFRP sandwiches are investigated, e.g. at 20 % of their compressive failure load at room temperature. Times to failure increase by up to a factor of 4 due to intumescent coatings. For GFRP sandwiches, different core structures with and without additional flame retardants show an astonishing impact on time to failure. CFRP shell structures are investigated on the intermediate scale with and without stringer reinforcements, resulting in completely different mechanical failure behaviour in the ultimate load test as opposed to the fire resistance test. The stringers become the only load-carrying part, while the shell acts as a protective layer. Thus the design exploiting this self-protection potential, i.e. the residue of the front skin protecting the load-bearing structure, is highlighted as a most promising route to enhance the fire resistance of lightweight materials.
The application of lightweight materials for tanks for transportation appears promising. Besides saving weight and therefore transportation costs, new complex geometries that depart from common cylindrical shapes of steel tanks can be manufactured. For transportation of dangerous goods, fire and explosion safety must be maintained to prevent accidents with serious consequences. In this work the fire behavior of lightweight tanks made from glass fiber reinforced plastics (GFRP) with complex geometries is investigated. Pretests on intermediate scale GFRP plates are conducted to identify suitable fire protection systems and surface treatments for composite tanks. The fire resistance is shown to be improved by addition of fire protective coatings and integrated layers. Finally, a complex rectangular GFRP tank with a holding capacity of 1100 liters is fire protected with an intumescent fire coating. The tank is filled up to 80 % with water and burned under an engulfing fully developed fire. It was shown that the intumescent layer could expand before the decomposition of the resin occurred. Furthermore, the adhesion between tank surface and coating was maintained. The structure could withstand a fire for more than 20 min.