The impact of very high cycle fatigue (VHCF) load conditions on the microstructure of specimens consisting of nodular cast iron is analyzed by means of micro-computed tomography (µCT) utilizing both monochromatic synchrotron radiation and polychromatic X-ray tube radiation. Using 3D µCT, the microstructure in the region of the smallest cross-sections of shouldered round specimens is imaged in different stages of the VHCF loading. By digital image correlation (DIC) of these tomograms strain fields are analyzed three-dimensionally. Strain levels in the range of a few percent were detected. It is proven that a localization of strain allows to predict the site of the crack which precedes and induces the macroscopic failure of the specimens.
The in situ analysis of the damage evolution in a metal Matrix composite (MMC) using synchrotron X-ray refraction radiography (SXRR) is presented. The investigated material is an Al alloy (6061)/10 vol% Al2O3 MMC after T6 heat treatment.
In an interrupted tensile test the gauge section of dog bone-shaped specimens is imaged in different states of tensile loading. On the basis of the SXRR images, the relative change of the specific surface (proportional to the amount of damage) in the course of tensile loading was analyzed. It could be shown that the damage can be detected by SXRR already at a stage of tensile loading, in which no Observation of damage is possible with radiographic absorption-based imaging methods.
Moreover, the quantitative analysis of the SXRR images reveals that the amount of damage increases homogeneously by an average of 25% with respect to the Initial state. To corroborate the experimental findings, the damage distribution was imaged in 3D after the final tensile loading by synchrotron X-ray refraction computed tomography (SXRCT) and absorption-based synchrotron X-ray computed tomography (SXCT). It could be evidenced that defects and damages cause pronounced indications in the SXRCT images.