Filtern
Dokumenttyp
- Vortrag (6)
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (1)
- Dissertation (1)
Schlagworte
- Erstarrungsriss (4)
- MVT (4)
- Solidification cracking (4)
- Varestraint test (4)
- Heißriss (3)
- Heißrisse (3)
- LTT (3)
- Schweißen (3)
- Welding (3)
- Hot cracking (2)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (13) (entfernen)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (6)
The Varestraint test and its variant Transvarestraint are one of the most widely used techniques for evaluating a material solidification cracking sensitivity during welding. The result of such tests is a crack length which is proportional to the material’s cracking susceptibility. Nevertheless, the welding and load parameters can unintentionally influence the crack length, which in some cases can distort the material evaluation. An approach is described as to how these effects can be assessed with the aid of a digital crack analysis. The crack lengths are compared position-dependently with their possible propagation due to the weld pool movement during continuous loading. The index derived from this can be used by the operator to evaluate his test parameters. In addition, a comparison of the results of different Varestraint setups is made possible. Alongside experimental results, a numerical sensitivity analysis is presented on how individual welding and loading parameters can affect the crack lengths.
Various test methods are available for assessing the susceptibility of materials to solidification cracking during welding. In the widely used Varestraint test, the crack length is selected as a criterion as a function of the applied bending strain.
Unfortunately, the crack length does not characterize the material behavior alone but depends to varying degrees on the individual test parameters used, which makes the interpretation of the results difficult. In addition, the crack length is not comparable under different test conditions. To overcome these disadvantages, we have developed a novel evaluation methodology that decouples the machine influence from the material behavior. The measured crack length is related to the maximum possible value specified by welding speed and deformation time. This relative crack length is calculated numerically, considering the orientation of the cracks. Experiments on two high-alloy martensitic welding consumables show that, in contrast to the conventional evaluation, a comparison of different welding parameters becomes possible. Furthermore, the strain rate proved to be a suitable crack criterion in agreement with Prokhorov's hot cracking model.
Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe
(2023)
Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unter-schiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium.
Die im MVT-Test standardmäßig erfasste Gesamtrisslänge erlaubt keine direkten Rückschlüsse auf die Heißrissanfälligkeit des untersuchten Werkstoffs. Der vorliegende Beitrag erläutert, inwiefern aus der Morphologie von Oberflächenrissen an MVT-Proben dennoch auf das Werkstoffverhalten geschlossen werden kann.
Zur Prüfung der Erstarrungsrissanfälligkeit von Werkstoffen existiert eine Vielzahl von Prüfverfahren, die jedoch oft nur in ihren Grundzügen standardisiert sind. Ein Beispiel ist der an der Bundesanstalt für Materialforschung und -prüfung entwickelte und angewendete Modifizierte Varestraint-/Transvarestraint-Test (MVT), der eine von vielen Umsetzungen des Varestraint-Verfahrensprinzips darstellt. Hierbei werden durch Biegung während des Schweißens gezielt Erstarrungsrisse erzeugt und anschließend lichtmikroskopisch vermessen. Die Ergebnisse von Varestraint-Prüfungen charakterisieren jedoch nicht allein das Werkstoffverhalten, sondern sind in hohem Maße von der Konstruktion der jeweiligen Prüfmaschine sowie den verwendeten Prüfparametern abhängig. Dies erschwert die Vergleichbarkeit von Ergebnissen, welche nicht unter exakt identischen Bedingungen ermittelt wurden, und kann darüber hinaus zu einer ungenauen oder unvollständigen Bewertung des Werkstoffverhaltens führen.
Die vorliegende Arbeit widmet sich zunächst der detaillierten Ausgestaltung der geometrischen Zusammenhänge rund um die Ausbreitung von Erstarrungsrissen während der Varestraint-Prüfung. Mit Blick auf Prokhorovs Technological Strength Theory und die sich daraus ergebenden erstarrungsrisskritischen Temperaturen wird anschließend eruiert, wie aus den Anfangs- und Endkoordinaten der entstandenen Risse auf das charakteristische Erstarrungsrissverhalten geschlossen werden kann. Die daraus entwickelte Bewertung der Rissanfälligkeit
ist weitestgehend von den Prüfparametern und weiteren verfahrensspezifischen Einflüssen entkoppelt, wodurch eine deutlich bessere Übertragbarkeit der Ergebnisse gewährleistet ist. Zur Erprobung der neu entwickelten Bewertungsansätze wurden zunächst MVT-Prüfungen an mehreren hochlegierten, martensitischen Schweißzusatzwerkstoffen, sowie am Nickelbasiswerkstoff Alloy 602 CA durchgeführt. So konnten einerseits verschiedene Legierungen hinsichtlich ihres Erstarrungsrissverhaltens charakterisiert und Empfehlungen für die schweißtechnische Fertigung generiert werden. Zum anderen dienten die Proben zur vollständigen Konzipierung, Entwicklung und Validierung einer digitalen Auswertemethodik.
Die eigens programmierte Software ermöglicht die schnelle und praxisgerechte Auswertung von MVT-Proben, und implementiert dabei zusätzlich die zuvor entwickelten, prozessunabhängigen Bewertungsansätze. Als Ergebnis konnten kritische Dehnraten identifiziert werden,ab deren Überschreitung die betrachteten Werkstoffe unter den verwendeten Prüfbedingungen gesteigerte Erstarrungsrissanfälligkeiten aufweisen. So ergibt sich ein direkter Zusammenhang zwischen MVT-Prüfergebnissen und der Technological Strength Theory
von Prokhorov. Die Bewertung des Werkstoffverhaltens anhand der kritischen Dehnraten erwies sich gegenüber den üblicherweise betrachteten Gesamtrisslängen als deutlich zuverlässiger.
Zusammenfassend konnte gezeigt werden, dass die digitale Auswertung eine sinnvolle Verbesserung der analogen Standardauswertung darstellt.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour (Fig. 1). During testing, energy input per unit length and bending speed were varied (especially the latter is usually kept at standard values), in addition to the most commonly altered factor - total deformation.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach - microscopic analysis of the specimen surface. It was found that not all parameter changes had the expected outcome. For the Cr8Ni6 and Cr11Mn5 filler materials, influences of energy input per unit length and welding speed were in direct opposition.
In order to investigate those apparent contradictions, µCT scans of MVT specimens were made. The results consistently show sub surface cracking, to significant, yet varying extents. Different primary solidification types were found using WDX-analysis, an aspect that is believed to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach. Subsequently, μCT scans were performed on the specimens. The results consistently show sub surface cracking, to significant, yet varying extents. Different Primary solidification types were found using WDX-analysis, an aspect that is regarded to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Für moderne Hochleistungswerkstoffe scheinen Standardparameter der Erstarrungsrissprüfung mittels MVT-Test in vielen Fällen ungeeignet. Dieser Vortrag erläutert die charakteristischen Besonderheiten der betrachteten Werkstoffe, und zeigt überdies alternative Analysemethoden auf, mit denen fehlerhafte Einschätzungen von Erstarrungsrissanfälligkeiten vermieden werden können.
Die Verwendung von Low Transformation Temperature (LTT) Schweißzusatzwerkstoffen ist eine innovative Möglichkeit, um beim Schweißen von hochfesten Stählen die schweißbedingten Zugeigenspannungen zu reduzieren. Durch die Zugabe von Legierungselementen, wie beispielsweise Nickel oder Mangan haben diese Werkstoffe eine, im Vergleich zu herkömm-lichen Schweißzusatzwerkstoffen deutlich herabgesetzte Martensitstarttemperatur (MS). Dadurch ist es möglich, die schweißbedingten Zugeigenspannungen mit LTT-Schweißzusatz-werkstoffen gezielt zu reduzieren oder sogar Druckeigenspannungen zu erzeugen.
Im Verlauf vorangegangener Arbeiten hat sich herausgestellt, dass einige der untersuchten LTT-Legierungen aufgrund ihres Erstarrungs- bzw. Seigerungsverhaltens eine gegenüber vielen konventionellen Schweiß-zusatzwerkstoffen erhöhte Heißrisssensibilität aufweisen.
Die aktuellen Arbeiten zielen darauf, die Heißrissneigung neuartiger LTT-Schweißzusatzwerkstoffe weiter zu ergründen.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour. During testing, energy input per unit length and bending speed were varied (especially the latter is usually kept at standard values), in addition to the most commonly altered factor - total deformation.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach - microscopic analysis of the specimen surface. It was found that not all parameter changes had the expected outcome. For the Cr8Ni6 and Cr11Mn5 filler materials, influences of energy input per unit length and welding speed were in direct opposition.
In order to investigate those apparent contradictions, μCT scans of MVT specimens were made. The results consistently show sub surface cracking, to significant, yet varying extents. Different primary solidification types were found using WDX-analysis, an aspect that is believed to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.