Aim of the investigation is to characterize selected PEEK-composites in vacuum environment. Oscillating sliding friction was investigated with a pin-on-disc configuration in high vacuum (10-5 mbar) at room temperature, -40 °C, +100 °C and +160 °C. The contact pressure was 1 MPa and 7 MPa respectively , the maximum sliding velocity 0.1 m/s. Furthermore, tests in ultra high vacuum (10-9 mbar) were carried out with flat and spherical pins at 1 MPa and 60 MPa respectively. Among the tested materials MoS2 filled PEEK shows the best tribological performance in vacuum. Particularly, in the lower temperature range and at higher loads the friction behaviour is improved by MoS2 content.
In the development of hydrogen technology, special attention is paid to the technical problems of
hydrogen storage. One possible way is cryogenic storage in liquid form. Generally cryotechnical
machines need components with interacting surfaces in relative motion such as bearings, seals or
valves, which are subjected to extreme conditions. Materials of such systems have to be resistant to
friction-caused mechanical deformation at the surface, low temperatures and hydrogen environment.
Since materials failure can cause uncontrolled escape of hydrogen, new material requirements are
involved for these tribo-systems, in particular regarding operability and reliability. In the past few
years several projects dealing with the influence of hydrogen on the tribological properties of friction
couples were conducted at the Federal Institute for Materials Research and Testing, (BAM), Berlin.
This paper reports some investigations carried out with polymer composites. Friction and wear were
measured for continuous sliding and analyses of the worn surfaces were performed after the
experiments. Tests were performed at room temperature in hydrogen as well as in liquid hydrogen.
This study deals with the development of PEEK (polyehteretherketone) and PTFE (polytetrafluoroethylene) based composites, optimized for low friction and low wear performance under extreme environments. It is demonstrated that the incorporation of a harder polymer component into PTFE (such as PEEK particles), a short fiber reinforcement (e.g. carbon fibers CF), and internal lubricants (e.g. PTFE particles), helps to reduce the friction and to improve the wear resistance over a very wide temperature range.
In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear.
The polymer chemical structure of the polyimide has a major influence on the tribological behaviour. The addition of graphite in PI2 has a beneficial effect in hydrogen on the friction and wear. The low friction of graphite is associated with a lubricant film in hydrogen. The influence of hydrogen on graphite is more effective than humidity. CNTs have a similar effect to that of graphite in PEEK composites. TiO2 particles improve significantly the wear rate both in vacuum and hydrogen environment. In LH2 friction and wear decrease for unfilled polymers. Friction of graphite filled composites increases slightly and wear rate is stable.