This paper presents investigations on the tribological behaviour of PTFE composites against steel at cryogenic temperatures. The results showed that the friction coefficient decreases with temperature down to 77 K, but did not follow a linear evolution further down to extreme low temperatures. It can be stated that the cryogenic environment has a significant influence on the tribological performance of the polymer composites. The effect of low temperatures was more clearly detected at low sliding speed, where friction heat is reduced. A change in wear mechanism from adhesive to abrasive was observed in this case. SEM and AFM analyses showed that the PTFE matrix composites investigated under these experimental conditions have transferred material onto the disc down to very low temperatures. Chemical analyses indicate the presence of iron fluorides.
Windings in superconducting magnets operating at 4.2 K are highly susceptible to quenching caused by small frictional heat inputs. Small movements in the magnet system are inevitable during ramping due to the increasing electromagnetic forces. Friction pairs of polymer based materials have been investigated at 4.2 K to gain an understanding of their sliding behavior in conditions representative of superconducting MRI systems. The results indicate that polymer-polymer pairs experience unstable sliding behavior with repeated stick-slip whereas polymer-aluminum couples have stable sliding behavior up to high contact pressures of 20 MPa.
Aim of the investigation is to characterize selected PEEK-composites in vacuum environment. Oscillating sliding friction was investigated with a pin-on-disc configuration in high vacuum (10-5 mbar) at room temperature, -40 °C, +100 °C and +160 °C. The contact pressure was 1 MPa and 7 MPa respectively , the maximum sliding velocity 0.1 m/s. Furthermore, tests in ultra high vacuum (10-9 mbar) were carried out with flat and spherical pins at 1 MPa and 60 MPa respectively. Among the tested materials MoS2 filled PEEK shows the best tribological performance in vacuum. Particularly, in the lower temperature range and at higher loads the friction behaviour is improved by MoS2 content.
Tribologisches Verhalten der Werkstoffpaarung Polymerverbundwerkstoff/Stahl bei tiefen Temperaturen
(2005)
Outstanding features favour the application of polymers and polymer composites in low-temperature technology. The booming hydrogen technology is a challenge for these materials, which are considered as seals and bearings in cryogenic pumps. In the present study, three types of thermoplastics, i.e., polyetheretherketone (PEEK), polyetherimide (PEI) and polyamide 6,6 (PA6,6), and one epoxy were considered as matrix materials. Micron-sized fillers, i.e., short carbon fibres, graphite flakes, and PTFE powders, were incorporated into these polymers together with nano-sized TiO2 particles. Optimised compositions of each matrix were selected from our previous works at room temperature in order to be studied at very low temperature conditions. In particular, frictional tests were carried out with polymer composite pins against polished steel surfaces under constant load over a certain distance in liquid hydrogen and liquid nitrogen. Afterwards, worn surfaces were analysed by using scanning electron microscopy (SEM). It was found out that the tribological properties in liquid hydrogen are dominated by the matrix materials, in particular thermoplastics perform generally slightly better than thermosetting resins.
Influence of the Temperature on the Tribological Behaviour of PEEK Composites in Vacuum Environment
(2008)
This paper describes tribological experiments carried out with polyetheretherketone (PEEK), filled with carbon fibres and solid lubricants (polytetrafluoroethylene (PTFE), graphite or MoS2), against steel discs. Oscillating sliding tests were performed in high vacuum environment in the temperature range between -40°C and +160°C. Results indicate that MoS2 filled PEEK show the best tribological performance in vacuum. Particularly, in the lower temperature range and at higher loads the friction behaviour is improved by the MoS2 content.
This study deals with the development of PEEK (polyehteretherketone) and PTFE (polytetrafluoroethylene) based composites, optimized for low friction and low wear performance under extreme environments. It is demonstrated that the incorporation of a harder polymer component into PTFE (such as PEEK particles), a short fiber reinforcement (e.g. carbon fibers CF), and internal lubricants (e.g. PTFE particles), helps to reduce the friction and to improve the wear resistance over a very wide temperature range.