The light-weight approach and fuel economy targets in today's automotive engineering require tribosystems, which can withstand higher contact pressures associated with low coefficients of friction. The application of high-performance coatings represents one approach among others. This paper presents some recently developed DLC coatings (a-C:H and ta-C) as well as a novel coating-substrate system (Zr(C,N)) in a benchmark test procedure under slip-rolling conditions in the presence of liquid lubricants. Various coatings with different thickness, interlayer and substrates were evaluated for their slip-rolling resistance in different lubricants at ambient temperature and at 120 °C. Results indicate that some of these coating systems can withstand at least 10 million cycles under initial Hertzian contact pressures of up to Pmax = 3.500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions. Surface of the coatings and the counter bodies were analysed and compared with untreated substrates.
Le secteur automobile doit faire face actuellement à de nouveaux challenges au niveau de la construction allégée, des économies de carburant et des coûts. Ces exigences motivent la mise au point de tribosystèmes pouvant résister à des pressions de contact de plus en plus élevées avec de faibles coefficients de frottement. L'optimisation de systèmes existants par l'application de revêtements de surface performants représente une alternative intéressante. Ce texte présente les performances de couches minces dans des conditions d'essais de slip-rolling (roulement à composante de glissement) en présence de lubrifiants liquides. Après une première sélection à température ambiante, les revêtements les plus performants ont été testés à 120 °C. Il s'agit de revêtements DLC en carbone hydrogéné (a-C:H) et en carbone tétraédrique (ta-C) de dernières générations ainsi qu'un nouveau système « revêtement/substrat ». Certains des revêtements DLC développés récemment sont résistants en slip-rolling au moins jusq'à 10 millions de cycles à 120 °C dans l'huile moteur sous des pressions hertziennes de contact de P0max = 2600 / 2940 MPa. De plus, le nouveau système revêtement Zr(C,N)x/substrat peut résister au moins à 1 million de cycles sous des pressions hertziennes initiales de contact allant jusqu'à P0max = 3500 MPa et à des températures de lubrifiant d'au moins 120 °C. -----------------------------------------------------------------------------------------------------------------------------------------------
The light-weight approach and fuel economy targets in today's automotive engineering require tribosystems, which can withstand higher contact pressures associated with low coefficients of friction. The application of surface coatings represents one approach among others. This paper presents thin film coatings performances in a bench mark test procedure exerting slip-rolling conditions in the presence of liquid lubricants. After a first selection at room temperature, the most resistant coatings were evaluated at 120 °C. These are newly developed DLC coatings (a-C:H & ta-C) as well as a novel coating-substrate system. Some of the newly developed DLC-coatings are slip-rolling resistant for at least up to 10 million cycles at 120 °C oil temperature) under Hertzian contact pressures of P0max = 2600 / 2940 MPa. Furthermore, this novel Zr-based thin film coating can withstand at least 1 million cycles under initial Hertzian contact pressures of up to P0max = 3500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions.
Costs reduction is one of the major objectives in mechanical applications with a parallel increase of the power output. Another driver represents new environmental standards and their increasing restrictions in the automotive industry leading to the question, if materials based concepts may substitute harmful EP/AW additives in lubricants. This paper presents the slip-rolling resistance of different DLC/THC coatings on steel substrates with a definite slip rate of 10%. Industrial DLC coatings of ta-C and a-C:H types from various manufacturers were deposited on steels SAE 52100 and AMS 5898 to compile the slip-rolling resistance under initial average Hertzian contact pressures between 1.5 GPa and 2 GPa. The tests were carried out on Amsler-type twin disc tribometer under the regime of mixed/boundary lubrication in unadditivated paraffinic oil (ISO VG 46) and a factory fill engine oil. The spherical steel sample was uncoated and the cylindrical coated with DLC. Some coatings achieved 10 million cycles without any damage under a maximal Hertzian contact pressure Pmax well over 2.25 GPa, thus exceeding FZG 12.