This paper presents investigations on the tribological behaviour of PTFE composites against steel at cryogenic temperatures. The results showed that the friction coefficient decreases with temperature down to 77 K, but did not follow a linear evolution further down to extreme low temperatures. It can be stated that the cryogenic environment has a significant influence on the tribological performance of the polymer composites. The effect of low temperatures was more clearly detected at low sliding speed, where friction heat is reduced. A change in wear mechanism from adhesive to abrasive was observed in this case. SEM and AFM analyses showed that the PTFE matrix composites investigated under these experimental conditions have transferred material onto the disc down to very low temperatures. Chemical analyses indicate the presence of iron fluorides.
Windings in superconducting magnets operating at 4.2 K are highly susceptible to quenching caused by small frictional heat inputs. Small movements in the magnet system are inevitable during ramping due to the increasing electromagnetic forces. Friction pairs of polymer based materials have been investigated at 4.2 K to gain an understanding of their sliding behavior in conditions representative of superconducting MRI systems. The results indicate that polymer-polymer pairs experience unstable sliding behavior with repeated stick-slip whereas polymer-aluminum couples have stable sliding behavior up to high contact pressures of 20 MPa.
Aim of the investigation is to characterize selected PEEK-composites in vacuum environment. Oscillating sliding friction was investigated with a pin-on-disc configuration in high vacuum (10-5 mbar) at room temperature, -40 °C, +100 °C and +160 °C. The contact pressure was 1 MPa and 7 MPa respectively , the maximum sliding velocity 0.1 m/s. Furthermore, tests in ultra high vacuum (10-9 mbar) were carried out with flat and spherical pins at 1 MPa and 60 MPa respectively. Among the tested materials MoS2 filled PEEK shows the best tribological performance in vacuum. Particularly, in the lower temperature range and at higher loads the friction behaviour is improved by MoS2 content.
Tribologisches Verhalten der Werkstoffpaarung Polymerverbundwerkstoff/Stahl bei tiefen Temperaturen
(2005)
This paper presents the mechanical and tribological properties of
Polytetrafluoroethylene (PTFE) and Polyetheretherketone (PEEK)
matrix composites filled with short carbon fibers in cryogenic
environments. Tensile tests were performed at room temperature (RT)
in air and in LN2. Tribological experiments were carried out with a
pin-on-disc configuration at RT, in LN2, in LH2 and in LHe. PEEK
composites have a better tribological performance than PTFE materials
especially regarding the wear resistance.