LTCC-modules with integrated ferrite layers - Strategies for material development and co-sintering
(2008)
Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics
(2009)
LTCC-Modules with integrated ferrite layers - Strategies for material development and co-sintering
(2009)
The integration of passive components (resistors, capacitors, inductors) into LTCC modules is a challenging task in multilayer ceramics technology. We report on multilayer assemblies consisting of combined layers of ferrite and dielectric LTCC tapes. Ni-Cu-Zn ferrites with maximum shrinkage at 900°C were processed to green tapes and laminated with dielectric LTCC tapes. Cosintering at 900°C led to multilayers with different defects such as incomplete densification of the ferrite layers, cracks, and warpage. Since ferrite tapes do not really allow compositional changes without deterioration of magnetic properties, the dielectric tape was modified with the following objectives: (i) matching of the shrinkage curves of dielectric and ferrite materials, (ii) adjusting the coefficients of thermal expansion to avoid cracking during cooling, and (iii) controlling of interface reactions. Using this concept we fabricated dense and defect-free multilayers consisting of dielectric and ferrite layers. However, compositional changes of the individual ferrite tapes require the development of a specific dielectric tape material with tailored properties.
Low-κ dielectric LTCC was developed, to realize successful co-firing with NiCuZn ferrite tapes. A critical high-temperature process in the production of highly integrated LTCC modules is the migration of silver from inner conductors into the LTCC glass phase. Intensive silver migration causes strong deformation of LTCC multilayers during firing in air.
Silver migration into the LTCC glass phase depends on oxygen content of the sintering atmosphere and can be minimized by sintering in nitrogen atmosphere. However, partial decomposition of NiCuZn-ferrite and formation of cuprite was observed during sintering in nitrogen and, consequently, the permeability of the ferrite decreases. As shown by a combined XRD/thermogravimetric study the co-firing of LTCC modules with silver metallization and integrated ferrite layer demands precise adjustment of oxygen partial pressure.
The sintering behavior and the thermoelectric performance of Ca3Co4O9 multilayer laminates were studied, and a multilayer thermoelectric generator was fabricated. Compacts and multilayer samples with anisotropic microstructure and residual porosity were obtained after conventional sintering at 920 °C, whereas dense and isotropic multilayer samples were prepared by firing at 1200 °C and reoxidation at 900 °C. A hot-pressed sample has a dense and anisotropic microstructure. Samples sintered at 920 °C exhibit low electrical conductivity due to the low density, whereas the Seebeck coefficient is not sensitive to preparation conditions. However, thermal conductivity of multilayers is very low, and, hence acceptable ZT values are obtained. A ransversal multilayer thermoelectric generator (TMLTEG) was fabricated by stacking layers of Ca3Co4O9 green tapes, AgPd conductor printing, and co-firing at 920 °C. The TMLTEG has a power output of 3 mW at ΔT =200 K in the temperature interval of 25 °C to 300 °C.
We have studied the integration of Ni-Cu-Zn ferrite spinels as well as substituted hexagonal Co2Y-and M-type ferrites into LTCC (Low Temperature Ceramic Co-firing) modules. The cofiring behavior and the magnetic properties of these materials were investigated and evaluated for multilayer applications. Ni-Cu-Zn ferrites exhibit permeabilities of µ=300–500 for operating frequencies in the MHz range. Cu-substituted Y-type ferrites Ba2Co2-x-yZnxCuyFe12O22 in combination with sintering additives display sufficient shrinkage and densification at 900°C. A permeability of µ=10 is observed; however, substituted Co2Y-type ferrites do not exhibit long-term stability at 900°C. Co/Ti-substituted M-type ferrites BaFe12-2yCoyTiyO19 (y=1.2) with planar magneto-crystalline anisotropy exhibit excellent soft magnetic behavior. Using sintering additives, complete densification is reached at 900°C and a permeability of µ=15 and a resonance frequency of larger than 1?GHz are observed. Integration of ferrite multilayer inductor components into LTCC modules using free and constrained cofiring technologies is demonstrated.
Integration of magnetic functional components in LTCC circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of µ = 900 were fully densified at the standard LTCC sintering temperature of 900°C. Co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal contraction during the cooling period – especially in the temperature range below the transformation point of the glass phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer laminates composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found using microprobe analysis. Pure ferrite laminates show homogeneous microstructure with large grains up to 50 µm in diameter. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between permeability and volume fraction of large ferrite grains. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, that is a decrease of more than 50%.