Geopolymer-zeolite composites were synthesized using a silica-rich industrial byproduct from chlorosilane production and sodium aluminate. Pastes were cured at 80 °C and 80% RH, and subsequently dried in two different climates: at 23 °C and 50% RH, and under vacuum. 1H MAS, 23Na MAS and 29Si MAS NMR and XRD measurements were performed after the drying procedures as well as after subsequent aging. Zeolite Na-A was found beside traces of faujasite-type zeolite and zeolite EMT as major crystalline phases in the cured composites; the fraction of geopolymeric gel in the reaction products was determined to be ~18% on a molar basis. Various water species could be distinguished using 1H MAS and 1H-29Si CP MAS NMR, applying rotorsynchronized echo experiments. The largest fraction of the pore water resides in the α-cages of the zeolite Na-A and in the geopolymeric gel; in addition, water exists in the β-cages of the zeolites and adsorbed at sodium ions. The water species in α-cages and in the pores of the geopolymeric gel exhibit slightly different chemical shifts of 4.7 ppm and 4.9 ppm, respectively, in the 1H MAS NMR spectra. Changes of the water content in the geopolymer pores of differently dried samples were observed and led to slightly varied chemical shifts in the 29Si MAS NMR spectra too. Measurements after more than 500 days revealed no significant aging effects of the composites, which confirm their chemical stability.
One-part geopolymers, synthesized from three different silica sources and sodium aluminate, were investigated regarding their microstructure and the evolution of their compressive strength on curing at slightly elevated temperatures. The effect of thermal treatment was studied up to 1000 °C and for the investigation of the chemical durability specific samples were treated with sulfuric acid (H2SO4, pH = 1).
Depending on the silica feedstock, different degrees of reaction were observed. One of the silicas had a significantly higher reactivity. For two of the silicas, significant amounts of zeolites occurred as reaction products besides geopolymeric gel, whereas the more reactive silica source lead to the formation of a rather fully condensed geopolymeric network.
The composites indicated promising behavior on heating in so far as no distinct shrinkage step occurred in the temperature range of dehydration. Up to 400 °C the residual strength of those mixes increased. Above 800 °C the samples underwent new phase formation. After exposure to sulfuric acid (pH 1; 70 d) specimens showed a residual compressive strength of about 77 % of the reference, indicating high acid resistance.