One-part geopolymers offer advantages over conventional geopolymers with regard to handling and storage of feedstocks. However, they often suffer from a low degree of reaction, a high amount of crystalline byproducts, and consequently low strength. In this study, one-part geopolymers were produced from rice husk ash (RHA) and sodium aluminate, and investigated by XRD, ATR-FTIR, SEM and compressive strength testing. The compressive strength of the material was 30 MPa, i.e. significantly higher than for comparable one-part geopolymers. This is attributed to an almost complete reaction of the RHA and the absence of crystalline byproducts (zeolites) in the hardened geopolymer.
This contribution presents the results of structural and compressive strength investigations on cured andhigh-temperature treated silica-based one-part geopolymer-zeolite composites. The specimens weresynthesized from two different silica sources, sodium aluminate and water. The phase content as well asthe compressive strength of the cured composites varied depending on the starting mix-design and thesilica feedstock. Besides geopolymeric gel, A-type zeolites and hydrosodalites were the major reactionproducts. One of the silica feedstocks yielded significantly higher compressive strength (19 MPa), whilethe other one appears to cause less variation in phase content. Strength testing indicated an improvementon heating up to
200–400 °C (28 MPa) followed by a moderate decrease up to 700 °C. Above 700 °C the sys-tems underwent new phase formation and shrinkage (volume decrease) deformations. After exposureat 1000 °C the different mixes consisted of a mix of several stuffed silica phases, almost pure hexago-nal nepheline or amorphous phase. Depending on the mix-design, the onset temperature of the hightemperature phase transformations varied.