Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (16)
- Beitrag zu einem Tagungsband (15)
- Dissertation (1)
- Posterpräsentation (1)
Schlagworte
- Geopolymers (10)
- Alkali-activated materials (8)
- Alkali-activation (3)
- Monitoring (3)
- One-part geopolymers (3)
- One-part mix (3)
- SealWasteSafe (3)
- Acid resistance (2)
- Blended cement (2)
- Brick clay (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (19)
- 7.4 Baustofftechnologie (19)
- 6 Materialchemie (4)
- 6.3 Strukturanalytik (4)
- 8 Zerstörungsfreie Prüfung (4)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (3)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (3)
- 8.6 Faseroptische Sensorik (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.1 Anorganische Spurenanalytik (1)
Paper des Monats
- ja (2)
The production and processing of ordinary Portland cement are responsible for nearly 5% of the world C02 emissions. Due to the world’s increasing requirement for building materials, this air pollution is growing up in the next decades. Alternative cement such as geopolymers can reduce these emissions effectively, Conventional geopolymer binders, produced ffom fly ash or metakaolin as aluminosilicate source and water-glass or alkali hydroxide Solutions as activator, are often used and studied. It is known that under appropriate conditions the starting materials form a three-dimensional aluminosilicate structure and create a gel-like matrix, In our case, a silica source from wastewater treatment of chlorosilane production and solid sodium aluminate as starting materials are initiated to harden by water. This procedure is known as “just add water” or “one-part” geopolymer formulation. These composites have significant advantages for use on construction site, but their Chemical structure is not extensively analyzed. In this work, a well known one-part geopolymer is investigated by 'H and 27A1 magic-angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy. Furthermore, it is shown that overlapping NMR lines can resolved with echo experiments and
The influence of starting materials and synthesis route on the properties and the structure of cementitious sodium aluminosilicate gels is not fully understood, partly due their amorphous nature and the fact that they often contain residual reactants, which can make the results of single-pulse NMR spectroscopy applied to these materials difficult to interpret or ambiguous. To overcome some of these limitations, 29Si{27Al} TRAPDOR NMR as well as 27Al{29Si} and 27Al{1H} REDOR NMR spectroscopy were applied to materials synthesized by the one-part alkali-activation route from three different amorphous silica starting materials, including rice husk ash. The latter led to formation of a fully amorphous sodium aluminosilicate gel (geopolymer), while the materials produced from the other silicas contained amorphous phase and crystalline zeolites. Application of the double-resonance NMR methods allowed to identify hydrous alumina gel domains in the rice husk ash-based material as well as significantly differing amounts of residual silica in the three cured materials. Four-coordinated Al existed not only in the aluminosilicate gel framework but also in a water-rich chemical environment with only a small amount of Si in proximity, likely in the alumina gel or possibly present as extra-framework Al in the aluminosilicate gel. The results demonstrate how the employment of different silica starting materials determines the phase assemblage of one-part alkali-activated materials, which in turn influences their engineering properties such as the resistance against chemically/biologically aggressive media.
Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles.
While calcined clays in general have been credited with a great potential to mitigate CO2 emissions related to cement production and consumption, calcined brick clays are currently understudied in this regard. In the present work, two brick clays, a low-grade kaolinitic clay, and a mixed clay composed of 50% brick clay and 50% low-grade kaolinitic clay were studied regarding transformations on calcination, and strength and durability performance as well as pore structure of mortars made with the blended cements. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the low-grade kaolinitic clay. However, the mixed clay performed very similar to the low-grade kaolinitic clay, which points to a viable option for optimal use of brick clays in cementitious systems. The carbonation resistance of the blended cement mortars was generally worse than that of the plain Portland cement mortar, as expected, but the former exhibited a significantly improved chloride penetration resistance. The latter improvement was due to pore structure refinement in the blended cement mortars, compared to the Portland cement mortar.
Portland cement is one of the principal sources of anthropomorphic CO2 emissions. It is estimated that cement production contributes up to 10% of greenhouse gas emissions and annual cement production over 4 billion tons. This has led to the development of a range of alkali activated materials (AAM), the most common precursor materials being class F fly ash and blast furnace slag. At present Class C Fly Ash is not widely utilized as an AAM due to the chemical composition and activation requirements. However, initial research on high Calcium German Class C Fly Ash suggests that the material may have potential for application as an AAM. This paper reports the development of ambient cured alkali activated mortar optimised by varying the alkali modulus and w/b ratio. The evolution of the mechanical and microstructural properties is reported over the initial 28 day period. Compressive strength in excess of 10 MPa at 7 days and 15 MPa at 28 days was achieved at ambient temperature. Similar strengths were observed for both 10% and 15% dosage but as dosage increases the optimal Alkali Modulus reduces.
Two brick clays (rich in 2:1 clay minerals) and a low-grade kaolinitic clay were studied regarding their transformations during calcination and their performance in blended cement mortars. The mortars with calcined clays exhibited decreased workability (slump flow), but this effect could be mitigated by employment of a conventional superplasticizer; however, compressive strength of the hardened mortar was lowered in some cases. While the kaolinitic clay generally yielded the highest strength, the performance of a brick clay could be increased by grinding to higher fineness and by mixing it with the kaolinitic clay.
The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose.
Two hybrid alkaline cements (HAC) based on Portland clinker, ground granulated blast furnace slag (GGBFS), fly ash and sodium sulfate, as well as an alkali-activated GGBFS/fly ash blend and a Portland cement paste were exposed to a saturated saline solution for 70 days. The combined chemical attack of chloride, magnesium and sulfate ions and the associated changes of the phase assemblage of the materials were studied by X-ray diffraction, thermal analysis and spatially resolved X-ray fluorescence spectroscopy. The experimental results revealed dissolution of ettringite, C-N-A-S-H and calcite, and the formation of gypsum, Kuzel's salt and Friedel's salt; thermodynamic modeling indicated the formation of M-S-H. The resistance of the HAC against attack by the saline solution increased with Portland clinker fraction. The capacity of portlandite to maintain pH at values above 10 is found to be a major factor controlling the resistance of HAC against corrosion in the saline solution.
One-part geopolymers were synthesized from two different silica materials (a silica-rich residue from chlorosilane production and a commercial microsilica) and sodium aluminate at three different SiO2/Al2O3 ratios and a nominal water/solids ratio of 0.5. The degree of reaction of the silica in the cured geopolymers (i.e. the fraction of silica dissolved to form aluminosilicates and minor products) was determined using two different methods: chemical attack with HCl to dissolve the reaction products and evaluation of peak areas of 29Si MAS NMR spectra. It was found that the degree of reaction of the silica decreases with increasing the silica content of the starting mix, and that it is almost constant after 1 day of curing and almost independent from the kind of starting silica. From the results of the NMR-based method, the mean SiO2/Al2O3 ratio of the reaction products (aluminosilicates and minor products) can be estimated to be ca. 2.0, nearly independent of the starting composition of the geopolymers. The dissolution method is biased, but of sufficient precision to be useful for following changes of the degree of reaction. Major crystalline phases in the cured geopolymers are zeolite A and/or hydrosodalite. Depending on the starting composition, the relative amounts of these zeolites vary; additionally, sodalite (only for the residue from chlorosilane production with >1 wt% Cl-), faujasite, and zeolite EMT can appear in the geopolymers. The 29Si and 27Al MAS NMR results indicate mainly Si(4Al) and Al(4Si) sites, in line with the presence of zeolite A, hydrosodalite, sodalite, and geopolymeric gel of comparatively low SiO2/Al2O3 ratio.
The 87Sr/86Sr isotope ratio can, in principle, be used for provenancing of cement. However, while commercial cements consist of multiple components, no detailed investigation into their individual 87Sr/86Sr isotope ratios or their influence on the integral 87Sr/86Sr isotope ratio of the resulting cement was conducted previously. Therefore, the present study aimed at determining and comparing the conventional 87Sr/86Sr isotope ratios of a diverse set of Portland cements and their corresponding Portland clinkers, the major component of these cements. Two approaches to remove the additives from the cements, i.e. to measure the conventional 87Sr/86Sr isotopic fingerprint of the clinker only, were tested, namely, treatment with a potassium hydroxide/sucrose solution and sieving on a 11-µm sieve. Dissolution in concentrated hydrochloric acid/nitric acid and in diluted nitric acid was employed to determine the 87Sr/86Sr isotope ratios of the cements and the individual clinkers. The aim was to find the most appropriate sample preparation procedure for cement provenancing, and the selection was realised by comparing the 87Sr/86Sr isotope ratios of differently treated cements with those of the corresponding clinkers. None of the methods to separate the clinkers from the cements proved to be satisfactory. However, it was found that the 87Sr/86Sr isotope ratios of clinker and cement generally corresponded, meaning that the latter can be used as a proxy for the clinker 87Sr/86Sr isotope ratio. Finally, the concentrated hydrochloric acid/nitric acid dissolution method was found to be the most suitable sample preparation method for the cements; it is thus recommended for 87Sr/86Sr isotope analyses for cement provenancing.
Geopolymer-zeolite composites were synthesized using a silica-rich industrial byproduct from chlorosilane production and sodium aluminate. Pastes were cured at 80 °C and 80% RH, and subsequently dried in two different climates: at 23 °C and 50% RH, and under vacuum. 1H MAS, 23Na MAS and 29Si MAS NMR and XRD measurements were performed after the drying procedures as well as after subsequent aging. Zeolite Na-A was found beside traces of faujasite-type zeolite and zeolite EMT as major crystalline phases in the cured composites; the fraction of geopolymeric gel in the reaction products was determined to be ~18% on a molar basis. Various water species could be distinguished using 1H MAS and 1H-29Si CP MAS NMR, applying rotorsynchronized echo experiments. The largest fraction of the pore water resides in the α-cages of the zeolite Na-A and in the geopolymeric gel; in addition, water exists in the β-cages of the zeolites and adsorbed at sodium ions. The water species in α-cages and in the pores of the geopolymeric gel exhibit slightly different chemical shifts of 4.7 ppm and 4.9 ppm, respectively, in the 1H MAS NMR spectra. Changes of the water content in the geopolymer pores of differently dried samples were observed and led to slightly varied chemical shifts in the 29Si MAS NMR spectra too. Measurements after more than 500 days revealed no significant aging effects of the composites, which confirm their chemical stability.
Due to environmental concerns regarding the use of Portland cement as the principal binder material in concrete and mortar it is imperative to identify alternative materials that could reduce the carbon footprint of the construction industry. One alternative to address these issues is the use of alkali activated materials, in particular, when based on waste streams that currently have no or only limited industrial application. This paper reports a preliminary study into the synthesis of geopolymer mortar utilizing Brown Coal Fly Ash. The ash had a CaO content of ~39%, indicating that synthesis at ambient or low temperature may be feasible. The paper reports initial trials on the effect of curing temperature, ambient to 120 °C, on the mechanical properties of the mortars produced. The results showed that ambient cured mortar achieved a compressive strength of 6.5 MPa at 3 days. A curing temperature of 60 °C gave the optimum results with a compressive strength of almost 20 MPa and a flexural strength of 3.5 MPa obtained.
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
In this work, one-part geopolymers were synthesized by mixing solid silica and sodium aluminate with water. Pastes were cured at elevated temperatures (60–90 °C) and relative humidity (r.H.) of 80–98 %. After curing the pastes at 80 °C and 80% r.H for one day, the reaction virtually ceased. Depending on the silica source either geopolymer- zeolite composites or zeolite-free geopolymeric gel forms. The compressive strength of the geopolymer-zeolite composites was lower as the compressive strength of a pure geopolymer, mainly due to a significantly denser and glassy microstructure with less interfaces of the latter one. The major part of the thermal dehydration occurred between 60 °C and 200 °C. Up to 700–800 °C only minor changes of the phase assemblage have been observed for the composites. Depending on the paste composition either ceramic or amorphous phases form during exposure to 1000 °C. Compared to other AAM, very low ambient drying/wetting shrinkage/expansion was observed for the mortars The mortars furthermore provide very high resistance against sulfuric acid (pH 1). Huge parts of the corroded layer are not dissolved from the specimen and can still provide protection for a potential substrate. In terms of sulfuric acid resistance, above a critical CaO content, the formation of gypsum is introduced. This causes expansion, cracking and the decrease of the sulfuric acid resistance.
Monitoring of repositories for radioactive waste requires techniques which can be applied long-term under harsh conditions. In this work, the reliability and suitability of materials and a capacitive sensor for measuring relative humidity are investigated, which are to be embedded in the special concrete components for the closure structures of underground repository. Preliminary tests with accelerated aging of the materials used, validation of the sensors under difficult conditions, investigations of the surfaces after aging by pH 14 solution, defined exposure of the sensors in a climatic chamber and the microscope images are discussed. The results will be used for further development and optimization of the RFID based sensor systems which can be applied to monitor the condition of different building structures without cabling.
Concretes produced from salt aggregate and hybrid alkaline cements, an alkali-activated slag/fly ash blend, or a Portland cement were exposed to a magnesium chloride-rich saline solution ([Mg2+] = 3.6 m, [Cl−] = 8.3 m), representing a solution formed after contact of surface water with evaporite rock (rock salt) in a nuclear waste repository. The hydration and deterioration of the concretes were studied with X-ray diffraction, thermogravimetric analysis, pH mapping and permeability measurements. The results show that calcium silicate hydrate (C-S-H) or sodium-substituted calcium aluminium silicate hydrate (C-N-A-S-H) and Friedel's salt were the major reaction products in the concretes prior to exposure to the saline solution. During exposure to the saline solution, increasing amounts of C-S-H/C-N-A-S-H dissolved, and gypsum and a secondary AFm phase formed. The durability of the concretes improved with increasing amounts of Portland clinker in the cements, due to the associated differences in permeability and chemical resistance. Nevertheless, a massive increase of permeability occurred for all concretes, likely caused by crack formation due to the formation of gypsum from anhydrite in the salt aggregate. Thus, the behavior of the concretes differed from, and was more complex than, the behavior of plain cement pastes.
The passive fire protection of steel structures and other load-bearing components will continue to gain importance in future years. In the present contribution, novel intumescent aluminosilicate (geopolymer-bound) composites are proposed as fire-protective coatings on steel. Steel plates coated with these materials were exposed to the standard temperature-time curve as defined in ISO 834 – 1:1999. The coatings partially foamed during curing and expanded further during thermal exposure, demonstrating their intumescent characteristic.Thermogravimetryandoscillatory rheometry determined that the intumescent behavior is attributed to a transition to a viscous state (loss factor > 1) in the temperature range of major water release, differing from conventional geopolymers. XRD and SEM images showed that the coatings had characteristics of ceramic or glass-ceramic foams after fire resistance testing, suggesting superior performance under challenging conditions. The thickness of the coatings influenced their foaming and intumescent behavior and thus the time for the coated steel plates to reach 500 °C. A number of additives were also studied with the best performance obtained from samples containing sodium tetraborate.Acoating of just 6mmwas able to delay the time it takes for a steel substrate to reach 500 °C to more than 30 minutes.
One-part geopolymers, synthesized from three different silica sources and sodium aluminate, were investigated regarding their microstructure and the evolution of their compressive strength on curing at slightly elevated temperatures. The effect of thermal treatment was studied up to 1000 °C and for the investigation of the chemical durability specific samples were treated with sulfuric acid (H2SO4, pH = 1).
Depending on the silica feedstock, different degrees of reaction were observed. One of the silicas had a significantly higher reactivity. For two of the silicas, significant amounts of zeolites occurred as reaction products besides geopolymeric gel, whereas the more reactive silica source lead to the formation of a rather fully condensed geopolymeric network.
The composites indicated promising behavior on heating in so far as no distinct shrinkage step occurred in the temperature range of dehydration. Up to 400 °C the residual strength of those mixes increased. Above 800 °C the samples underwent new phase formation. After exposure to sulfuric acid (pH 1; 70 d) specimens showed a residual compressive strength of about 77 % of the reference, indicating high acid resistance.
The project "SealWasteSafe" of the Bundesanstalt für Materialforschung und -prüfung (BAM, Berlin) deals with sealing structures applied for underground disposal of nuclear waste from two perspectives: (1) material improvement for application in sealing constructions and (2) feasibility study regarding multi-sensor approaches to ensure quality assurance and long-term monitoring.
One specimen of 150 l made of alkali-activated material, which was found innovative and suitable for sealing constructions based on preliminary laboratory studies, and, for comparison purpose, another one made of salt concrete, are manufactured with an integrated multi-sensory setup for quality assurance and long-term-monitoring. The specimens were left in their cast form and additionally thermally insulated to simulate the situation in the repository. The multi-sensory concept comprises RFID technology embedded in the specimens suppling material temperature and moisture measurements, integrated fibre optic sensing allowing strain measurement and acoustic emission testing for monitoring possible crack formation. Overall, the suitability and the functionality of the sensors embedded into and attached to strongly alkaline (pH > 13 for the AAM) and salt corrosive (NaCl) environment was proven for the first 672 h.
First temperature measurement based on RFID succeeded after 626 h for the alkali-activated material and after 192 h for the conventional salt concrete. Strain measurement based on distributed fibre optic sensing turned out the alkali-activated material with > 1 mm m-1 undergoing approximately twice the compression strain as the salt concrete with strains < 0.5 mm m-1. In contrast, the acoustic emission first and single hits representing crack formation in numbers, was found for alkali-activated material half of that detected at the salt concrete.
Multi-sensory monitoring and ultrasound for quality assurance at underground sealing structures
(2023)
Within the safety concepts of underground disposal sites of nuclear waste, engineered barriers play an important role. As these sealing structures have high demands concerning integrity, we aim at advancing the available construction materials, monitoring, and inspection techniques within the project SealWasteSafe. A specifically developed alkali-activated material is compared to classical salt concrete. A comprehensive multi-sensory monitoring scheme is used at 150-340 l specimens to monitor setting and hardening of both materials. All sensors are demonstrated to resist the highly alkaline environments. Besides cabled and wireless temperature and humidity of the materials, strain variations using fibre optic sensors and acoustic emissions are recorded over periods of at least 28 days, partly for more than eight months. After hardening of the specimens, further nondestructive evaluations using ultrasonic echo and thermographic measurements are conducted.
Preliminary results proof the suitability of the tested sensors and clearly highlight differences between the tested materials. Particularly, the newly developed alkali-activated material shows lower acoustic emission activity indicating less cracking activity. Additionally, unique ultrasonic methods will enable better images of potential internal objects and cracks at in-situ sealing structures. A largescale ultrasonic system is optimised to reliably detect objects at a depth exceeding 9 m while still obtaining a good resolution. Modelling studies show the potential of further increasing the distance between individual transducer arrays. Additionally, a new ultrasonic borehole probe using phased arrays allowing for beam focussing is constructed and tested. Laboratory measurements at a halfcylindrical concrete specimen coincide well with the previous modelling. In total, the presented safe materials, detailed monitoring approaches and ultrasonic quality assurance methods will help to obtain safe sealing structures within salt as a host rock. The concepts can partly be transferred to sealing structures in alternative host rocks and will also be valuable for non-nuclear waste repositories.