Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (15) (entfernen)
Schlagworte
- Alkali-activated materials (4)
- Geopolymers (4)
- Monitoring (3)
- SealWasteSafe (3)
- Brown Coal Fly Ash (2)
- Lignite Coal (2)
- One-part geopolymers (2)
- One-part mix (2)
- AAM (1)
- Abwasserinfrastruktur (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (8)
- 7.4 Baustofftechnologie (8)
- 8 Zerstörungsfreie Prüfung (3)
- 6 Materialchemie (2)
- 6.3 Strukturanalytik (2)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (2)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (2)
- 8.0 Abteilungsleitung und andere (1)
- 8.6 Faseroptische Sensorik (1)
Due to environmental concerns regarding the use of Portland cement as the principal binder material in concrete and mortar it is imperative to identify alternative materials that could reduce the carbon footprint of the construction industry. One alternative to address these issues is the use of alkali activated materials, in particular, when based on waste streams that currently have no or only limited industrial application. This paper reports a preliminary study into the synthesis of geopolymer mortar utilizing Brown Coal Fly Ash. The ash had a CaO content of ~39%, indicating that synthesis at ambient or low temperature may be feasible. The paper reports initial trials on the effect of curing temperature, ambient to 120 °C, on the mechanical properties of the mortars produced. The results showed that ambient cured mortar achieved a compressive strength of 6.5 MPa at 3 days. A curing temperature of 60 °C gave the optimum results with a compressive strength of almost 20 MPa and a flexural strength of 3.5 MPa obtained.
Die Hauptfunktion von Verschlussbauwerken für End- und Zwischenlager von radioaktiven Abfällen besteht in der Erhaltung der geologischen Barriere. Vor allem soll ein potenzieller Stofftransport durch eine möglichst geringe Permeabilität des Bauwerks verhindert bzw. auf vernachlässigbare Werte herabgesetzt werden. Die in-situ-Permeabilität des Verschlussbauwerks steht dabei in direktem Zusammenhang mit dessen Poren- und Makrostruktur, welche bei Bauwerken auf Basis von Beton insbesondere durch Schwind-verformungen und durch thermisch induzierte Rissbildung infolge der Reaktionswärmeentwicklung des Bindemittels gestört werden kann. Die Betone müssen daher neben einer hohen chemischen Langzeitstabilität auch eine geringe bzw. langsame Wärmeentwicklung während der Erhärtungsreaktionen aufweisen. Als hybride Zemente werden Mischungen aus Portlandzement, Betonzusatzstoffen und einem alkalischen Aktivator bezeichnet. Dabei können u. a. Alkalisulfate, Alkalicarbonate, Alkalisilicate und Alkalihydroxide als Aktivatoren zum Einsatz kommen. Aufgrund ihrer hohen chemischen Stabilität im salinaren Milieu sind Betone aus solchen Zementen potenziell besonders gut als Verfüllmaterial für End- und Zwischenlager im Steinsalz geeignet. In der vorliegenden Studie wurden daher hybride Zemente hinsichtlich ihrer Wärmeentwicklung in einem isothermen Kalorimeter sowie hinsichtlich Phasenbestand und Festigkeiten untersucht. Hybride Zementleime wurden auf Basis von Portlandklinker, Hüttensandmehl, Flugasche und Natriumsulfat hergestellt und die Zusammensetzungen systematisch variiert, um den Einfluss der Komponenten auf Wärmeentwicklung, Phasenbestand und mechanische Eigenschaften der Leime zu untersuchen; zusätzlich wurden zu Vergleichszwecken ein Zementleim auf Basis der Betonrezeptur M2 sowie eine alkalisch aktivierte Flugasche untersucht.
The production and processing of ordinary Portland cement are responsible for nearly 5% of the world C02 emissions. Due to the world’s increasing requirement for building materials, this air pollution is growing up in the next decades. Alternative cement such as geopolymers can reduce these emissions effectively, Conventional geopolymer binders, produced ffom fly ash or metakaolin as aluminosilicate source and water-glass or alkali hydroxide Solutions as activator, are often used and studied. It is known that under appropriate conditions the starting materials form a three-dimensional aluminosilicate structure and create a gel-like matrix, In our case, a silica source from wastewater treatment of chlorosilane production and solid sodium aluminate as starting materials are initiated to harden by water. This procedure is known as “just add water” or “one-part” geopolymer formulation. These composites have significant advantages for use on construction site, but their Chemical structure is not extensively analyzed. In this work, a well known one-part geopolymer is investigated by 'H and 27A1 magic-angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy. Furthermore, it is shown that overlapping NMR lines can resolved with echo experiments and
Geopolymers are promising alkali activated materials with a wide range of possible applications like heat-resistant coatings and adhesives or concretes with lower C02 emissions than conventional Portland cement-based systems. Conventional ("two-part") geopolymers are synthesized by an activation of aluminosilicate feedstocks like metakaolin or blast furnace slags with highly alkaline solutions like sodium hydroxide solutions and/or water glass solutions.
A more recent approach are so called one-part geopolymers, where the alkaline activator is provided in solid form, so that only water has to be added to initiate the geopolymerisation reaction. The handling of alkaline solutions is avoided, which possesses several advantages compared to conventional geopolymers, in particular regarding safety and health issues, and, thus, it improves economic and social acceptance of these binders. However, the new formulations are less exhaustively studied and the knowledge about conventional geopolymers cannot simply be transferred to this new class of binders.
Two brick clays (rich in 2:1 clay minerals) and a low-grade kaolinitic clay were studied regarding their transformations during calcination and their performance in blended cement mortars. The mortars with calcined clays exhibited decreased workability (slump flow), but this effect could be mitigated by employment of a conventional superplasticizer; however, compressive strength of the hardened mortar was lowered in some cases. While the kaolinitic clay generally yielded the highest strength, the performance of a brick clay could be increased by grinding to higher fineness and by mixing it with the kaolinitic clay.
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
Mixing and curing of geopolymers and related alkali-activated materials without storage and handling of highly alkaline solutions possesses advantages regarding safety and economic viability. One possible approach is to produce these materials from solid silica feedstocks and solid sodium aluminate, and subsequent mixing with water. We present a comparison between geopolymers and aluminosilicate gel-zeolite composites synthesized by this route from different silica feedstocks (by-product silica from chlorosilane production, microsilica, rice husk ash) and with different SiO2/Al2O3 ratios, using results from XRD, NMR, SEM, thermal analysis, mechanical and acid resistance testing. The use of rice husk ash favors formation of a fully amorphous geopolymer with high strength. Utilization of the other silica feedstocks leads to formation of aluminosilicate gel-zeolite composites, the amount and kind of zeolites depending on the feedstock and the SiO2/Al2O3 ratio. These composites show beneficial dehydration behavior, viz. no distinct dehydration step of thermal strain, with the phase assemblage after heating to 1000°C controlled by the starting composition. Mortars produced from both, the geopolymers as well as the composites, exhibit high resistance to sulfuric acid attack, making them promising materials for the construction and the repair of industrial and sewer structures.
One-part geopolymers, synthesized from three different silica sources and sodium aluminate, were investigated regarding their microstructure and the evolution of their compressive strength on curing at slightly elevated temperatures. The effect of thermal treatment was studied up to 1000 °C and for the investigation of the chemical durability specific samples were treated with sulfuric acid (H2SO4, pH = 1).
Depending on the silica feedstock, different degrees of reaction were observed. One of the silicas had a significantly higher reactivity. For two of the silicas, significant amounts of zeolites occurred as reaction products besides geopolymeric gel, whereas the more reactive silica source lead to the formation of a rather fully condensed geopolymeric network.
The composites indicated promising behavior on heating in so far as no distinct shrinkage step occurred in the temperature range of dehydration. Up to 400 °C the residual strength of those mixes increased. Above 800 °C the samples underwent new phase formation. After exposure to sulfuric acid (pH 1; 70 d) specimens showed a residual compressive strength of about 77 % of the reference, indicating high acid resistance.